Preparation and ablation resistance of ZrC nanowires-reinforced CVD-ZrC coating on sharp leading edge C/C composites

被引：35
|
作者：
Li, Bo [1 ]
Li, Hejun [1 ]
Yao, Xiyuan [1 ]
Zhu, Xiaofei [1 ]
Liu, Ningkun [1 ]
机构：
[1] Northwestern Polytech Univ, State Key Lab Solidificat Proc, Xian 710072, Shaanxi, Peoples R China
来源：
APPLIED SURFACE SCIENCE | 2022年 / 584卷
基金：
中国国家自然科学基金;
关键词：
ZrC nanowire; Coating; Chemical vapor deposition; Sharp leading edge; Ablation resistance; SIC NANOWIRES; GROWTH-BEHAVIOR; THERMAL-SHOCK; MICROSTRUCTURE; TEMPERATURE; DEPOSITION; OXIDATION;
D O I：
10.1016/j.apsusc.2022.152617
中图分类号：
O64 [物理化学（理论化学）、化学物理学];
学科分类号：
070304 ; 081704 ;
摘要：
To improve the ablation resistance of sharp leading edge (SLE) C/C composites, the ZrC nanowires reinforced ZrC coating (ZrC-ZrCnws) was prepared by two-step CVD method. The preparation of ZrC nanowires and the microstructure, bonding strength, as well as ablation resistance of the ZrC-ZrCnws coating were studied. After the severe ablation, the SLE sample with ZrC-ZrCnws coating presented an excellent ablation resistance with the mass and linear ablation rates of only 0.59 & PLUSMN; 0.06 mg/s and-0.92 & PLUSMN; 0.09 mu m/s, respectively. Such good ablation resistance was attributed to the incorporation of ZrC nanowires, which can inhibit the cracking of coating and form ZrO2 rod-like structures after oxidation, supporting the oxide layer to resist flame scouring.
引用
收藏
页数：10
相关论文
共 50 条
  • [31] Preparation and Ablation Properties of LaB6-Modified C/C-ZrC-SiC Composites
    Xie, Jing
    You, Silun
    Sun, Guodong
    Li, Hui
    Jia, Yan
    Teng, Chengcheng
    Xie, Wangnan
    Xiyou Jinshu Cailiao Yu Gongcheng/Rare Metal Materials and Engineering, 2023, 52 (08): : 2828 - 2834
  • [32] Effect of Monolithic LaB6 on the Ablation Resistance of ZrC/SiC Coating Prepared by Supersonic Plasma Spraying for C/C Composites
    Yujun Jia
    Hejun Li
    Lu Li
    Qiangang Fu
    Kezhi Li
    JournalofMaterialsScience&Technology, 2016, 32 (10) : 996 - 1002
  • [33] Effect of Monolithic LaB6 on the Ablation Resistance of ZrC/SiC Coating Prepared by Supersonic Plasma Spraying for C/C Composites
    Jia, Yujun
    Li, Hejun
    Li, Lu
    Fu, Qiangang
    Li, Kezhi
    JOURNAL OF MATERIALS SCIENCE & TECHNOLOGY, 2016, 32 (10) : 996 - 1002
  • [34] Cyclic Ablation Properties of C/SiC-ZrC Composites
    Ge, Hailang
    Zhang, Lu
    Zhang, Huajun
    Wang, Fang
    Gao, Xiguang
    Song, Yingdong
    AEROSPACE, 2024, 11 (06)
  • [35] Microstructure, thermophysical properties, and ablation resistance of C/HfC-ZrC-SiC composites
    Chen, Yuntian
    Sun, Wei
    Xiong, Xiang
    Chang, Yabin
    Xu, Yonglong
    Peng, Zheng
    Tian, Tian
    Zeng, Yi
    CERAMICS INTERNATIONAL, 2019, 45 (04) : 4685 - 4691
  • [36] Ablation resistance and mechanism of SiC/ZrC-ZrB2double layer coating for C/C composites under plasma flame
    Liu, Han-zhou
    Yang, Xin
    Fang, Cun-qian
    Shi, An-hong
    Chen, Lei
    Huang, Qi-zhong
    JOURNAL OF CENTRAL SOUTH UNIVERSITY, 2020, 27 (09) : 2538 - 2547
  • [37] Comparative research on cyclic ablation behavior of C/C-ZrC-SiC and C/C-ZrC composites at temperatures above 2000 °C
    Zhao, Zhigang
    Li, Kezhi
    Kou, Gang
    Li, Wei
    CORROSION SCIENCE, 2022, 206
  • [38] Ablation behavior and mechanism of C/ZrC, C/ZrC-SiC and C/SiC composites fabricated by polymer infiltration and pyrolysis process
    Yan, Chunlei
    Liu, Rongjun
    Cao, Yingbin
    Zhang, Changrui
    Zhang, Deke
    CORROSION SCIENCE, 2014, 86 : 131 - 141
  • [39] Comparative research on cyclic ablation behavior of C/C-ZrC-SiC and C/ C-ZrC composites at temperatures above 2000?C
    Zhao, Zhigang
    Li, Kezhi
    Kou, Gang
    Li, Wei
    CORROSION SCIENCE, 2022, 206
  • [40] UHTC coating reinforced by HfC nanowires against ablation for C/C composites
    Ren, Jincui
    Zhang, Yulei
    Zhang, Pengfei
    Li, Tao
    Hu, Heng
    SURFACE & COATINGS TECHNOLOGY, 2017, 311 : 191 - 198
12345