Study of (Nd, Sm)422 solid solution and its effect on the melt process of Nd123 bulk superconductors

被引：4
|
作者：
Yoshioka, J
Iida, K
Murakami, M
机构：
[1] ISTEC, Superconduct Res Lab, Morioka Lab, Morioka, Iwate 0200852, Japan
[2] ISTEC, Superconduct Res Lab, Tamachi Lab, Minato Ku, Morioka, Iwate 0200852, Japan
来源：
PHYSICA C | 2001年 / 354卷 / 1-4期
关键词：
Nd123; Nd422; Nd-Sm solid solution; transition temperature; critical current density;
D O I：
10.1016/S0921-4534(01)00140-X
中图分类号：
O59 [应用物理学];
学科分类号：
摘要：
We have studied the range of Nd-Sm solid solution in the (Nd1-x, Sm-x)(4-2y)Ba2+2yCu2-yOz, system in the Nd123 matrix. X-ray diffraction studies for the sintered (Nd1-x, Sm-x)(4-2y)Ba2+2yCu2-yOz powders in air showed that the samples were a single phase 422 in the range of x = 0-0.3, showing that Sm substituted on Nd site in Nd422. It was also found that Sm is soluble up to x = 0.3 in (Nd1-x, Sm-x)(3.6)Ba2.4Cu1.8Oz. We then fabricated Nd123/Nd422 bulk superconductors by melt processing, in which Nd123 powder is mixed with 20 mol% (Nd-0.8 Sm-0.2)(3.6)Ba2.4Cu1.8Oz and 1 wt.% CeO2. The sample exhibited high T-c of 97 K and sharp superconducting transition when melt-processed under controlled oxygen partial pressure (P-O2) of 0.01 atm. (C) 2001 Elsevier Science B.V. All. rights reserved.
引用
收藏
页码：401 / 405
页数：5
相关论文
共 36 条
  • [1] Effect of Nd422 addition on J(c) in Nd123 melt-textured bulk superconductor
    Ikeda, S
    Oka, T
    Yamada, Y
    Yoshikawa, M
    Yanagi, Y
    Itoh, Y
    Mizutani, U
    JAPANESE JOURNAL OF APPLIED PHYSICS PART 2-LETTERS, 1997, 36 (3B): : L345 - L348
  • [2] AC magnetization characteristics of Nd123 bulk superconductors
    Waki, K
    Higuchi, T
    Yoo, SI
    Watahiki, M
    Hayashi, N
    Sakai, N
    Chikumoto, N
    Murakami, M
    CRYOGENICS, 1997, 37 (10) : 643 - 647
  • [3] TEM observations of melt-textured Nd123 superconductors
    Hu, A.M.
    Liu, W.
    Xiong, J.W.
    Qin, Y.L.
    Pang, C.
    Zhao, Z.X.
    Physica C: Superconductivity and its Applications, 1998, 297 (1-2): : 52 - 58
  • [4] TEM observations of melt-textured Nd123 superconductors
    Hu, AM
    Liu, W
    Xiong, JW
    Qin, YL
    Pang, C
    Zhao, ZX
    PHYSICA C, 1998, 297 (1-2): : 52 - 58
  • [5] Fabrication of melt-textured Nd123 superconductors with Nd2BaO4 addition
    Hu, A
    Obradors, X
    Gomis, V
    Puig, T
    Carrillo, A
    Cardellach, E
    Mendoza, E
    Zhao, ZX
    Xiong, JW
    APPLIED SUPERCONDUCTIVITY, 1998, 6 (2-5) : 129 - 137
  • [6] Sm-Ba-Cu-O bulk superconductors melt processed in air, using Nd123/MgO thin film cold seeding
    Fujimoto, H
    Ozaku, H
    Ohtabara, E
    PHYSICA C-SUPERCONDUCTIVITY AND ITS APPLICATIONS, 2003, 386 : 198 - 201
  • [7] A NEW-TYPE OF PINNING CENTER IN MELT GROWN ND123 AND SM123
    MURAKAMI, M
    YOO, SI
    HIGUCHI, T
    SAKAI, N
    WATABIKI, M
    KOSHIZUKA, N
    TANAKA, S
    PHYSICA C-SUPERCONDUCTIVITY AND ITS APPLICATIONS, 1994, 235 : 2781 - 2782
  • [8] OCMG process for filamentary Nd123 superconductor produced by solution spinning
    Nagoya Inst of Technology, Nagoya, Japan
    Appl Supercond, 2-5 (157-162):
  • [9] OCMG process for filamentary Nd123 superconductor produced by solution spinning
    Goto, T
    Takahama, M
    Kimura, T
    APPLIED SUPERCONDUCTIVITY, 1998, 6 (2-5) : 157 - 162
  • [10] Microstructure and superconducting properties of bulk superconductors prepared from Sm123-RE211 (RE = Y, Gd and Sm) and Sm123-Nd422 precursors
    Nariki, S
    Seo, SJ
    Sakai, N
    Murakami, M
    ADVANCES IN SUPERCONDUCTIVITY XII, 2000, : 485 - 487
1234