Fatigue crack growth behaviors in Al-Si-Mg sand cast alloys

被引：5

作者：

Han, SW ^{[1
]}

Kim, SW ^{[1
]}

机构：

[1] Chonbuk Natl Univ, Div Adv Mat Engn, Res Inst Adv Mat Dev, Cheonju 561756, South Korea

来源：

METALS AND MATERIALS INTERNATIONAL | 2004年 / 10卷 / 01期

关键词：

Al-Si-Mg cast alloys; porosity; deflection of fatigue crack; age hardening;

D O I：

10.1007/BF03027358

中图分类号：

T [工业技术];

学科分类号：

08 ;

摘要：

The fatigue crack growth behavior of Al-Si-Mg sand cast alloys has been investigated with reference to the effects of solidification structure and aging condition. Fatigue crack growth tests have been carried out under constant load amplitude and a stress ratio of R=0.1 using CT specimens. The amount of pores in the matrix was limited by performing HIP treatment. The pores tended to promote deflection of fatigue cracks, which decreased the fatigue crack growth rate at low DeltaK regions and increased the number of cycles until final fatigue fracture. Refining and spheroidizing of eutectic Si particles increased the fatigue crack growth rates over a wide range of DeltaK up to larger DeltaK values. The difference of aging conditions significantly affected the da/dN-DeltaK(eff) relationship.

引用

页码：13 / 18

页数：6

共 50 条

[41] Dependence of phase selection on cooling rates in as-cast Al-Si-Mg alloys
何志
张瑞杰
刘永勤
介万奇
Transactions of Nonferrous Metals Society of China, 2006, (S3) : 1592 - 1594
[42] Effects of Mg Content on the Fatigue Strength and Fracture Behavior of Al-Si-Mg Casting Alloys
Wu, Ming-Ze
Zhang, Ji-Wang
Zhang, Yan-Bin
Wang, Hua-Qiang
JOURNAL OF MATERIALS ENGINEERING AND PERFORMANCE, 2018, 27 (11) : 5992 - 6003
[43] Effect of grain refiner on the tensile and impact properties of Al-Si-Mg cast alloys
Samuel, E.
Golbahar, B.
Samuel, A. M.
Doty, H. W.
Valtierra, S.
Samuel, F. H.
MATERIALS & DESIGN, 2014, 56 : 468 - 479
[44] On the effect of hydrogen and Fe on reproducibility of tensile properties in cast Al-Si-Mg alloys
Eisaabadi B, G.
Davami, P.
Varahram, N.
Kim, S. K.
MATERIALS SCIENCE AND ENGINEERING A-STRUCTURAL MATERIALS PROPERTIES MICROSTRUCTURE AND PROCESSING, 2013, 565 : 278 - 284
[45] Effects of Mg Content on the Fatigue Strength and Fracture Behavior of Al-Si-Mg Casting Alloys
Ming-Ze Wu
Ji-Wang Zhang
Yan-Bin Zhang
Hua-Qiang Wang
Journal of Materials Engineering and Performance, 2018, 27 : 5992 - 6003
[46] Effects of fluidised bed quenching on heat treating characteristics of cast Al-Si-Mg and Al-Si-Mg-Cu alloys
Chaudhury, S. K.
Apelian, D.
INTERNATIONAL JOURNAL OF CAST METALS RESEARCH, 2006, 19 (06) : 361 - 369
[47] Damage mechanisms of cast Al-Si-Mg alloys under superimposed thermal-mechanical fatigue and high-cycle fatigue loading
Beck, Tilmann
Loehe, Detlef
Luft, Jochen
Henne, Ingo
MATERIALS SCIENCE AND ENGINEERING A-STRUCTURAL MATERIALS PROPERTIES MICROSTRUCTURE AND PROCESSING, 2007, 468 : 184 - 192
[48] Crack initiation and small fatigue crack growth behaviour of squeeze-cast Al-Si aluminium alloys
Shiozawa, K
Tohda, Y
Sun, SM
FATIGUE & FRACTURE OF ENGINEERING MATERIALS & STRUCTURES, 1997, 20 (02) : 237 - 247
[49] Crack initiation and small fatigue crack growth behaviour of squeeze-cast Al-Si aluminum alloys
Toyama Univ, Toyama, Japan
Fatigue Fract Eng Mater Struct, 2 (237-247):
[50] Microstructure observation in T5 treated Al-Si-Mg system cast alloys
TSUCHIYA T.
MAKITA Y.
LEE S.
SAIKAWA S.
IKENO S.
MATSUDA K.
MATSUDA, Kenji (matsuda@sus.u-toyama.ac.jp), 1600, Japan Institute of Light Metals (71): : 166 - 170

← 1 2 3 4 5 →