Microstructure and mechanical performance of porous mullite ceramics added with TiO2

被引：25

作者：

Deng, Xiangong ^{[1
,2
]}

Zhang, Wanchun ^{[2
]}

Yin, Jiaqiang ^{[2
]}

Deng, Chaoheng ^{[2
]}

Zhang, Shaowei ^{[3
]}

Zhang, Haijun ^{[3
]}

Ran, Songlin ^{[1
]}

机构：

[1] Anhui Univ Technol, Minist Educ, Key Lab Met Emiss Reduct & Resources Recycling An, Maanshan 243002, Peoples R China

[2] Anhui Univ Technol, Sch Mat Sci & Engn, Key Lab Green Fabricat & Surface Technol Adv Met, Maanshan 243002, Peoples R China

[3] Wuhan Univ Sci & Technol, State Key Lab Refractories & Met, Wuhan 430081, Peoples R China

来源：

CERAMICS INTERNATIONAL | 2020年 / 46卷 / 06期

基金：

中国国家自然科学基金;

关键词：

Porous mullite ceramics; Columnar mullite; TiO2; additive; Mechanical performance; COAL FLY-ASH; HIGH-STRENGTH; FABRICATION; POROSITY; FOAMS;

D O I：

10.1016/j.ceramint.2019.12.078

中图分类号：

TQ174 [陶瓷工业]; TB3 [工程材料学];

学科分类号：

0805 ; 080502 ;

摘要：

Porous mullite samples were manufactured using granular mullite powders as major materials, and TiO2 as the additive agent. Influences of TiO2 contents on rheological characteristics of slurries, and microstructure and bending strength at 25-1400 degrees C of final porous mullite products were investigated. Adding appropriate content of TiO2, a large amount of columnar mullite with mean length of 23.7 mu m and the length-to-diameter ratio of 6.7 was in-situ formed, which could improve the mechanical performance of the resultant porous samples. The bending strength at 25 degrees C of porous products containing 67% porosity fabricated by using 7 wt% TiO2 reached 12.5 MPa, and its bending strength at 1200 degrees C remained as high as 6.1 MPa.

引用

页码：8438 / 8443

页数：6

共 50 条

[21] Synthesis and Performance of Porous TiO2
Zhang, Yingchen
Wu, Hongyan
Zhu, Mingcong
Wang, Enqiang
Li, Dengxin
CHINA POSTDOCTORAL FORUM ON MATERIALS SCIENCE AND ENGINEERING, 2011, 266 : 55 - +
[22] HAp/TiO2 nanocomposites: Influence of TiO2 on microstructure and mechanical properties
Vemulapalli, Ajay Kumar
Penmetsa, Rama Murty Raju
Nallu, Ramanaiah
Siriyala, Rajesh
JOURNAL OF COMPOSITE MATERIALS, 2020, 54 (06) : 765 - 772
[23] Effects of Foaming Agent on Microstructure and Properties of Porous Mullite Ceramics
Li Cuiwei
Yang Fengkun
Han Yao
Wang Chang'an
Chen Kepi
RARE METAL MATERIALS AND ENGINEERING, 2013, 42 : 931 - 934
[24] Fabrication and structure of TiO2 coated open-cell mullite ceramics
Park, Seong-Hwan
Kim, Jae-Won
Jung, Yeon-Gil
Lee, Je-Hyun
Paik, Ungyu
Lee, Hee-Soo
SCIENCE OF ENGINEERING CERAMICS III, 2006, 317-318 : 139 - 142
[25] Effect of cyclic infiltrations on microstructure and mechanical behavior of porous mullite/mullite composites
She, JH
Mechnich, P
Schneider, H
Schmücker, M
Kanka, B
MATERIALS SCIENCE AND ENGINEERING A-STRUCTURAL MATERIALS PROPERTIES MICROSTRUCTURE AND PROCESSING, 2002, 325 (1-2): : 19 - 24
[26] Effect of TiO2 on the mullite formation and mechanical properties of alumina porcelain
Montoya, Noemi
Javier Serrano, Francisco
Mercedes Reventos, Maria
Maria Amigo, Jose
Alarcon, Javier
JOURNAL OF THE EUROPEAN CERAMIC SOCIETY, 2010, 30 (04) : 839 - 846
[27] Phase formation, microstructure development, and mechanical properties of kaolin-based mullite ceramics added with Fe2O3
Liu, Zhenying
Lian, Wei
Liu, Yin
Zhu, Jinbo
Xue, Changguo
Yang, Zhongde
Lin, Xin
INTERNATIONAL JOURNAL OF APPLIED CERAMIC TECHNOLOGY, 2021, 18 (03) : 1074 - 1081
[28] The microstructure, mechanical and dielectric properties of CNTs/mullite ceramics composites
Wang, Jing
Kou, Huamin
Pan, Yubai
Guo, Jingkun
COMPOSITE MATERIALS IV, 2006, 313 : 145 - 150
[29] The microstructure, mechanical and dielectric properties of CNTs/mullite ceramics composites
Wang, Jing
Kou, Huamin
Pan, Yubai
Guo, Jingkun
Key Engineering Materials, 2006, 313 : 145 - 150
[30] Microstructure and mechanical properties of mullite ceramics containing rodlike particles
Meng, JH
Cai, S
Yang, ZF
Yuan, QM
Chen, YR
JOURNAL OF THE EUROPEAN CERAMIC SOCIETY, 1998, 18 (08) : 1107 - 1114

← 1 2 3 4 5 →