Effect of NiO/YSZ compositions on the co-sintering process of anode-supported fuel cell

被引：62
|
作者：
Bao, WT [1 ]
Chang, QB [1 ]
Meng, GY [1 ]
机构：
[1] Univ Sci & Technol China, Dept Mat Sci & Engn, Hefei 230026, Peoples R China
来源：
JOURNAL OF MEMBRANE SCIENCE | 2005年 / 259卷 / 1-2期
基金：
中国国家自然科学基金;
关键词：
anode support; YSZ dense film; SOFC;
D O I：
10.1016/j.memsci.2005.03.009
中图分类号：
TQ [化学工业];
学科分类号：
0817 ;
摘要：
Effect of NiO/YSZ compositions on the co-sintering process of anode-supported fuel cell was researched. The green YSZ layer was fabricated by modifying electrostatic powder coating, and the relative density is about 52%. After co-firing at 1400 degrees C for 5h, the sample of YSZ film based on the 1000-NY support (pre-calcinated NiO 60wt.%, YSZ 40wt.%) is concave due to the mismatch of shrinkages between the YSZ film and anode support and there exist cracks on the film. Dense YSZ films based on the NY-20P (NiO 48wt.%, YSZ 32wt.% and graphite 20wt.%) support were fabricated after co-firing at 1400 degrees C for 2h. The OCV and the peak power density of a single cell with a 15 mu m thick YSZ film based on the NY-20P support are 1.09 V and 315 mW/cm(2) at 800 degrees C, respectively. (c) 2005 Elsevier B.V. All rights reserved.
引用
收藏
页码：103 / 109
页数：7
相关论文
共 50 条
  • [41] Performance Evaluation of an Anode-supported Honeycomb Solid Oxide Fuel Cell
    Fukushima, Akira
    Nakajima, Hironori
    Kitahara, Tatsumi
    STUDENT POSTERS (GENERAL) - 222ND ECS MEETING/PRIME 2012, 2013, 50 (48): : 71 - 75
  • [42] Anode-supported tubular micro-solid oxide fuel cell
    Sarkar, Partho
    Yamarte, Luis
    Rho, Hongsang
    Johanson, Lorne
    INTERNATIONAL JOURNAL OF APPLIED CERAMIC TECHNOLOGY, 2007, 4 (02) : 103 - 108
  • [43] Reduction of Electrode Polarization in Anode-Supported Solid Oxide Fuel Cell
    Meepho, Malinee
    Wattanasiriwech, Darunee
    Aungkavattana, Pavadee
    Wattanasiriwech, Suthee
    2015 INTERNATIONAL CONFERENCE ON ALTERNATIVE ENERGY IN DEVELOPING COUNTRIES AND EMERGING ECONOMIES, 2015, 79 : 272 - 277
  • [44] The effect of nickel oxide microstructure on the performance of Ni-YSZ anode-supported SOFCs
    Guo, Weimin
    Liu, Jiang
    SOLID STATE IONICS, 2008, 179 (27-32) : 1516 - 1520
  • [45] Durable direct ethanol anode-supported solid oxide fuel cell
    Steil, M. C.
    Nobrega, S. D.
    Georges, S.
    Gelin, P.
    Uhlenbruck, S.
    Fonseca, F. C.
    APPLIED ENERGY, 2017, 199 : 180 - 186
  • [46] Microscale Modeling of an Anode-Supported Planar Solid Oxide Fuel Cell
    Chinda, P.
    Wechsatol, W.
    Chanchaona, S.
    Brault, P.
    FUEL CELLS, 2011, 11 (02) : 184 - 199
  • [47] Effect of anode thickness on impedance response of anode-supported solid oxide fuel cells
    Park, Young Min
    Lee, Hoo Jung
    Bae, Hong Yeol
    Ahn, Jin Su
    Kim, Haekyoung
    INTERNATIONAL JOURNAL OF HYDROGEN ENERGY, 2012, 37 (05) : 4394 - 4400
  • [48] Low-temperature constrained sintering of YSZ electrolyte with Bi2O3 sintering sacrificial layer for anode-supported solid oxide fuel cells
    Lim, Yonghyun
    Lee, Hojae
    Park, Junghum
    Kim, Young-Beom
    CERAMICS INTERNATIONAL, 2022, 48 (07) : 9673 - 9680
  • [49] Effect of Ni diffusion into BaZr0.1Ce0.7Y0.1Yb0.1O3-δ electrolyte during high temperature co-sintering in anode-supported solid oxide fuel cells
    Shimada, Hiroyuki
    Yamaguchi, Toshiaki
    Sumi, Hirofumi
    Yamaguchi, Yuki
    Nomura, Katsuhiro
    Fujishiro, Yoshinobu
    CERAMICS INTERNATIONAL, 2018, 44 (03) : 3134 - 3140
  • [50] In situ fabrication mechanism of a dense Sr and Ca doped lanthanum chromite interconnect on Ni-YSZ anode of a solid oxide fuel cell during co-sintering
    Heidarpour, A.
    Saidi, A.
    Abbasi, M. H.
    Choi, G. M.
    CERAMICS INTERNATIONAL, 2013, 39 (02) : 1821 - 1826
12345