Powder metallurgical processing of Ti6Al4V alloy

被引：1

作者：

Liu Na ^{[1
]}

Li Zhou ^{[1
]}

Yuan Hua ^{[1
]}

Xu Wenyong ^{[1
]}

Zhang Yong ^{[1
]}

Zhang Guoqing ^{[1
]}

机构：

[1] Beijing Inst Aeronaut Mat, Natl Key Lab Sci & Technol Adv High Temp Struct M, Beijing 100095, Peoples R China

来源：

HIGH PERFORMANCE STRUCTURES AND MATERIALS ENGINEERING, PTS 1 AND 2 | 2011年 / 217-218卷

关键词：

argon gas atomization; pre-alloyed Ti6Al4V powder; powder metallurgical; hot isostatic pressing; COMPONENTS; SIZE;

D O I：

10.4028/www.scientific.net/AMR.217-218.1336

中图分类号：

TH [机械、仪表工业];

学科分类号：

0802 ;

摘要：

Ti6Al4V powders were produced by Argon gas atomization, the powder fraction < 250 mu m was hot isostatically pressed (HIP) at 920 degrees C and 140MPa. The properties of pre-alloyed powders and the compact were investigated in this paper. Powder particles are almost perfectly spherical. The microstructure of powder surface is approximate hexagonal cellular structure, the inner structure exhibits cellular alpha phase and needle-like martensite alpha' phase, these are resulting from the rapid solidification. After HIP, Ti6Al4V alloy has a Widmanstaten microstructure consisting of continuous grain boundary alpha (GB alpha) phase and beta transformation structure, the grain size of GB alpha phase is in the range of 5 similar to 15 mu m. The tensile test at room temperature shows that strength of samples is 880MPa, the fracture surface exhibits obvious brittle cleavage fracture features including cleavage facets with river pattern and a few elongate dimples of different sizes and big voids at localized area.

引用

页码：1336 / 1342

页数：7

共 50 条

[21] Performance characterization of powder mixed wire electrical discharge machining technique for processing of Ti6Al4V alloy
Chakraborty, Sadananda
Mitra, Souren
Bose, Dipankar
PROCEEDINGS OF THE INSTITUTION OF MECHANICAL ENGINEERS PART E-JOURNAL OF PROCESS MECHANICAL ENGINEERING, 2022, 236 (04) : 1283 - 1295
[22] Application of thermohydrogen processing to Ti6Al4V alloy blade isothermal forging
Huang Shuhui
Zong Yingying
Shan Debin
MATERIALS SCIENCE AND ENGINEERING A-STRUCTURAL MATERIALS PROPERTIES MICROSTRUCTURE AND PROCESSING, 2013, 561 : 17 - 25
[23] Laser surface processing of Ti6Al4V alloy precoated with hard particles
Yilbas, Bekir Sami
Optics and Laser Technology, 2022, 153
[24] Laser surface processing of Ti6Al4V alloy precoated with hard particles
Yilbas, Bekir Sami
OPTICS AND LASER TECHNOLOGY, 2022, 153
[25] Effect of Laser Processing Parameters on Surface Texture of Ti6Al4V Alloy
Xi, Xiaoying
Pan, Yongzhi
Wang, Pengcheng
Fu, Xiuli
2019 INTERNATIONAL CONFERENCE ON ADVANCED ELECTRONIC MATERIALS, COMPUTERS AND MATERIALS ENGINEERING (AEMCME 2019), 2019, 563
[26] Direct Metal Laser Sintering of the Ti6Al4V Alloy from a Powder Blend
Ramosena, Lekhetho Ambition
Dzogbewu, Thywill Cephas
du Preez, Willie
MATERIALS, 2022, 15 (22)
[27] SURFACE ROUGHNESS OF Ti6Al4V ALLOY PRODUCED BY LASER POWDER BED FUSION
Liovic, David
Franulovic, Marina
Ferlic, Luka
Gubeljak, Nenad
FACTA UNIVERSITATIS-SERIES MECHANICAL ENGINEERING, 2024, 22 (01) : 63 - 76
[28] Drilling of titanium alloy (Ti6Al4V) - a review
Yuan, Chua Guang
Pramanik, A.
Basak, A. K.
Prakash, C.
Shankar, S.
MACHINING SCIENCE AND TECHNOLOGY, 2021, 25 (04) : 637 - 702
[29] Anodizing of Ti6Al4V alloy for aeronautical applications
Gomez-Mendez, M.
Duran-Pabon, C.
Naranjo, D. I.
Arenas, M. A.
Garcia-Vergara, S. J.
III COLOMBIAN CONGRESS OF ELECTROCHEMISTRY, 2018, 1119
[30] ELECTRON BEAM WELDING OF Ti6Al4V ALLOY
Foret, Rudolf
Havlik, Petr
METAL 2016: 25TH ANNIVERSARY INTERNATIONAL CONFERENCE ON METALLURGY AND MATERIALS, 2016, : 1266 - 1271

← 1 2 3 4 5 →