Formation mechanism of black LiTaO3 single crystals through chemical reduction

被引：23
|
作者：
Yan, Tao [1 ]
Zheng, Feifei [1 ]
Yu, Yonggui [2 ]
Qin, Shubin [1 ]
Liu, Hong [1 ]
Wang, Jiyang [1 ]
Yu, Dehong [3 ]
机构：
[1] Shandong Univ, State Key Lab Crystal Mat, Jinan 250100, Peoples R China
[2] Deqing Huaying Elect Co, Deqing 313200, Peoples R China
[3] Australian Nucl Sci & Technol Org, Bragg Inst, Lucas Heights, NSW 2234, Australia
来源：
JOURNAL OF APPLIED CRYSTALLOGRAPHY | 2011年 / 44卷
关键词：
black lithium tantalate; X-ray photoelectron spectroscopy; X-ray diffraction; LITHIUM-NIOBATE; DEVICE FABRICATION; OXYGEN VACANCIES; DEFECT STRUCTURE; LINBO3; CRYSTALS; DOPED LINBO3; GROWTH; STOICHIOMETRY; PERFORMANCE; TANTALATE;
D O I：
10.1107/S0021889810052520
中图分类号：
O6 [化学];
学科分类号：
0703 ;
摘要：
Lithium tantalate (LiTaO3, LT) wafers of different colors were prepared through chemical reduction of regular congruent LT wafers. Samples with different colors corresponding to different annealing temperatures were characterized by X-ray diffraction, X-ray photoelectron spectroscopy, and measurements of the Curie temperature and density. It was found that chemical reduction does not influence the basic LT structure. The Ta charge state change due to chemical reduction was found to be the main reason for the formation of black LT wafers.
引用
收藏
页码：158 / 162
页数：5
相关论文
共 50 条
  • [31] Ultrasonic microspectroscopy of LiNbO3 and LiTaO3 single crystals for SAW devices
    Kushibiki, J
    Ono, Y
    Takanaga, I
    ELECTRONICS AND COMMUNICATIONS IN JAPAN PART II-ELECTRONICS, 2000, 83 (09): : 8 - 21
  • [32] Formation of a stoichiometric layer and new polar phase upon exposure of LiTaO3 single crystals to lithium vapor
    M. N. Palatnikov
    V. A. Sandler
    O. B. Shcherbina
    I. N. Efremov
    N. V. Sidorov
    V. T. Kalinnikov
    Inorganic Materials, 2011, 47 : 1233 - 1237
  • [33] Formation of a Stoichiometric Layer and New Polar Phase upon Exposure of LiTaO3 Single Crystals to Lithium Vapor
    Palatnikov, M. N.
    Sandler, V. A.
    Shcherbina, O. B.
    Efremov, I. N.
    Sidorov, N. V.
    Kalinnikov, V. T.
    INORGANIC MATERIALS, 2011, 47 (11) : 1233 - 1237
  • [34] CHEMICAL TWINNING AND FERROELECTRIC DOMAINS IN LITAO3
    BURSILL, LA
    LIN, PJ
    PHILOSOPHICAL MAGAZINE A-PHYSICS OF CONDENSED MATTER STRUCTURE DEFECTS AND MECHANICAL PROPERTIES, 1982, 46 (01): : 1 - 24
  • [35] OPTICAL-TRANSMISSION PROPERTIES OF LITAO3 CRYSTALS
    WANG, XS
    GAO, JX
    TANG, NA
    FERROELECTRICS LETTERS SECTION, 1993, 15 (02) : 49 - 53
  • [36] CZOCHRALSKI GROWTH OF LARGE DIAMETER LITAO3 CRYSTALS
    BRANDLE, CD
    MILLER, DC
    JOURNAL OF CRYSTAL GROWTH, 1974, 24 (OCT) : 432 - 436
  • [37] Spectroscopic properties of holmium doped LiTaO3 crystals
    Dominiak-Dzik, G
    Golab, S
    Zawadzka, J
    Ryba-Romanowski, W
    Lukasiewicz, T
    Swirkowicz, M
    JOURNAL OF PHYSICS-CONDENSED MATTER, 1998, 10 (45) : 10291 - 10306
  • [38] THERMAL EXPANSION OF LITAO3 SINGLE CRYSTAL
    IWASAKI, H
    TOYODA, H
    JAPANESE JOURNAL OF APPLIED PHYSICS, 1967, 6 (11) : 1338 - &
  • [39] On the study of zinc doping in congruent LiTaO3 crystals
    Wu, J. C.
    Chen, Z. B.
    Choubey, R. K.
    Lan, C. W.
    MATERIALS CHEMISTRY AND PHYSICS, 2012, 133 (2-3) : 813 - 817
  • [40] LiTaO3 crystals with near-zero birefringence
    Glazer, A. M.
    Zhang, N.
    Bartasyte, A.
    Keeble, D. S.
    Huband, S.
    Thomas, P. A.
    Gregora, I.
    Borodavka, F.
    Margueron, S.
    Hlinka, J.
    JOURNAL OF APPLIED CRYSTALLOGRAPHY, 2012, 45 : 1030 - 1037
12345