Effect of Zr on nanocrystalline Al-4.5 wt.% Cu alloy and its strengthening mechanisms prepared by mechanical alloying

被引：0

作者：

Dasharath, S. M. ^{[1
]}

Arati, C. ^{[1
]}

机构：

[1] REVA Univ, Sch Mech Engn, Bangalore 560064, Karnataka, India

来源：

MATERIALS TODAY-PROCEEDINGS | 2020年 / 20卷

关键词：

Al-Zr nanostructures; Sintering; Compressive strength; Grain boundary segregation; Solid solution strengthening; Hardness;

D O I：

10.1016/j.matpr.2019.10.086

中图分类号：

T [工业技术];

学科分类号：

08 ;

摘要：

Synthesis and characterization of Al, Al99.5Zr0.5, Al99Zr1 and Al97Zr3 nanostructures developed by high energy ball milling have been carried out in the present study. Mixtures of Aluminium and Zirconium were added to Tungstan carbide vial (Spex Sample Prep) in the desired quantities. The powder mixtures were milled in a Spex 8000 mixer/mill for 500 min to prepare the required nanocrystalline material. Milled powders were compacted in a cylindrical (8 mm dia) tool steel die under an uniaxial applied pressure 99.5 Mpa in a hydraulic pellet press. The compacted milled powders (pellet) were annealed under 2% H-2 (bal. Ar) for 1 h at temperatures from 350 to 500 degrees C and holding at the same temperature for 1 h. The extents of alloying, structural and morphological changes of the nanocrystalline material in the powder form were analyzed and studied using X-ray diffractometer. X-ray diffraction data was analyzed by using X'Pert highscore plus for the calculation of crystallite size and lattice microstrain (%). The Vickers microhardness of all samples was also measured. (C) 2019 Elsevier Ltd. All rights reserved.

引用

页码：140 / 144

页数：5

共 50 条

[21] Characterization of dendrite morphologies in rapidly solidified Al-4.5 wt.%Cu droplets
Bedel, M.
Reinhart, G.
Bogno, A. -A.
Gandin, Ch. -A.
Jacomet, S.
Boller, E.
Nguyen-Thi, H.
Henein, H.
ACTA MATERIALIA, 2015, 89 : 234 - 246
[22] Effects of the simultaneous imposition of electromagnetic and magnetic forces on the solidification structure of pure Al and Al-4.5 wt.%Cu alloy
Li, Xi
Ren, Zhongming
Fautrelle, Yves
JOURNAL OF MATERIALS PROCESSING TECHNOLOGY, 2008, 195 (1-3) : 125 - 134
[23] In situ SiCp/Al-4.5 wt. % Cu composites obtained by direct reaction synthesis
Liang, Yanfeng
Zhou, Jing'en
Dong, Shengquan
Yang, Tong
ADVANCES IN COMPOSITES, PTS 1 AND 2, 2011, 150-151 : 868 - +
[24] Morphological analysis of SSM Al-4.5 wt.% Cu measured by the rheocast quality index
Zoqui, EJ
JOURNAL OF MATERIALS PROCESSING TECHNOLOGY, 2003, 143 : 195 - 201
[25] Prevention of macrosegregation in squeeze casting of an Al-4.5 wt pct Cu alloy
Hong, CP
Shen, HF
Cho, IS
METALLURGICAL AND MATERIALS TRANSACTIONS A-PHYSICAL METALLURGY AND MATERIALS SCIENCE, 1998, 29 (01): : 339 - 349
[26] Prevention of macrosegregation in squeeze casting of an Al-4.5 wt pct Cu alloy
Hong, C.P.
Shen, H.F.
Cho, I.S.
Metallurgical and Materials Transactions A: Physical Metallurgy and Materials Science, 1998, 29 A (01): : 339 - 349
[27] Prevention of macrosegregation in squeeze casting of an Al-4.5 wt pct Cu alloy
C. P. Hong
H. F. Shen
I. S. Cho
Metallurgical and Materials Transactions A, 1998, 29 : 339 - 349
[28] Effects of Solidification, Rotary Swaging and Recrystallization on the Microstructure, Crystallographic Orientation and Electrochemical Behavior of an Al-4.5 wt.% Cu Alloy
Lourenco, J. C.
Souza, L. P.
Silva, G.
Suzuki, P. A.
Robin, A. L. M.
Nunes, C. A.
Tomachuk, C. R.
INTERNATIONAL JOURNAL OF ELECTROCHEMICAL SCIENCE, 2021, 16 (10): : 1 - 22
[29] Hardness and Wear Properties of Al-4.5%Cu/Al3Mg2 Nanocomposite Prepared by Mechanical Alloying
Nemati, Narguess
Emamy, Massoud
Emami, Ali Reza
Mashhoodi, Mashhood
MATERIALS TRANSACTIONS, 2012, 53 (07) : 1310 - 1317
[30] Strengthening of mechanical and tribological properties of Al-4.5% Cu matrix alloy with the addition of bamboo leaf ash
Bannaravuri, Praveen Kumar
Birru, Anil Kumar
RESULTS IN PHYSICS, 2018, 10 : 360 - 373

← 1 2 3 4 5 →