Effect of microstructure on the superconducting properties of Gd-Ba-Cu-O bulk fabricated in air

被引：11
|
作者：
Nariki, S
Hinai, H
Sakai, N
Murakami, M
Otsuka, M
机构：
[1] ISTEC, Superconduct Res Lab, Minato Ku, Tokyo 1050023, Japan
[2] Shibaura Inst Technol, Minato Ku, Tokyo 1088548, Japan
来源：
PHYSICA C | 2001年 / 357卷 / 357-360期
关键词：
melt processing; critical temperature; critical current density; Gd-Ba-Cu-O;
D O I：
10.1016/S0921-4534(01)00373-2
中图分类号：
O59 [应用物理学];
学科分类号：
摘要：
Bulk Gd-Ba-Cu-O superconductors were melt processed in air. The Gd2BaCuO5 (Gd211) particles dispersed in the melt-textured bulk could be refined by employing fine Gd211 starting powders. Since T-c of the bulk samples was lowered with decreasing the size of Gd211 particle, J(c) was not improved. However, we found that a depression of T-c was prevented by Ag addition, leading to higher J(c) values. The J(c) of Gd-Ba-Cu-O/Ag with Gd211 particles about 0.7 mum in size exhibited 60 000 A/cm(2) at 77 K and self-field. (C) 2001 Elsevier Science B.V. All rights reserved.
引用
收藏
页码：817 / 820
页数：4
相关论文
共 50 条
  • [41] Pulsed field magnetization of large-grain Gd-Ba-Cu-O bulk superconductor
    Fukai, H
    Yamada, H
    Sakai, N
    Murakami, M
    PHYSICA C-SUPERCONDUCTIVITY AND ITS APPLICATIONS, 2003, 392 : 585 - 588
  • [42] Measurements of the levitation forces for a bulk Gd-Ba-Cu-O superconductor in high magnetic fields
    Suzuki, T.
    Araki, S.
    Takeuchi, K.
    Murakami, M.
    Nagashima, K.
    Miyazaki, Y.
    Seino, H.
    Sakai, N.
    Hirabayashi, I.
    Sawa, K.
    PHYSICA C-SUPERCONDUCTIVITY AND ITS APPLICATIONS, 2007, 463 (383-386): : 383 - 386
  • [43] Materials preparation and magnetization of Gd-Ba-Cu-O bulk high-temperature superconductors
    Ida, Tetsuya
    Li, Zhi
    Zhou, Difan
    Miki, Motohiro
    Zhang, Yufeng
    Izumi, Mitsuru
    SUPERCONDUCTOR SCIENCE & TECHNOLOGY, 2016, 29 (05):
  • [44] Preparation and properties of OCMG-processed Gd-Ba-Cu-O bulk superconductors with very fine Gd211 particles
    Nariki, S
    Sakai, N
    Murakami, M
    PHYSICA C, 2001, 357 (SUPPL. 2): : 811 - 813
  • [45] Fabrication of high-quality joints between Gd-Ba-Cu-O bulk superconductors
    Tutt, N.
    Congreve, J.
    Shi, Y.
    Namburi, D.
    Dennis, A.
    Druiff, H.
    Durrell, J.
    SUPERCONDUCTOR SCIENCE & TECHNOLOGY, 2023, 36 (08):
  • [46] Processing of high-performance Gd-Ba-Cu-O bulk superconductor with Ag addition
    Nariki, S
    Sakai, N
    Murakami, M
    SUPERCONDUCTOR SCIENCE & TECHNOLOGY, 2002, 15 (05): : 648 - 652
  • [47] Development of Gd-Ba-Cu-O bulk magnets with very high trapped magnetic field
    Nariki, S
    Sakai, N
    Murakami, M
    PHYSICA C-SUPERCONDUCTIVITY AND ITS APPLICATIONS, 2002, 378 : 631 - 635
  • [48] Position dependence of irreversibility line on thin plate Gd-Ba-Cu-O bulk superconductor
    Naito, Tomoyuki
    Furuta, Daiki
    Arayashiki, Takahiro
    Fujishiro, Hiroyuki
    Yanagi, Yousuke
    Itoh, Yoshitaka
    ADVANCES IN SUPERCONDUCTIVITY XXIV, 2012, 27 : 168 - 171
  • [49] Field trapping property of Gd-Ba-Cu-O bulk superconductor 140 mm in diameter
    Sakai, N.
    Kita, M.
    Nariki, S.
    Muralidhar, M.
    Inoue, K.
    Hirabayashi, I.
    Murakami, M.
    PHYSICA C-SUPERCONDUCTIVITY AND ITS APPLICATIONS, 2006, 445 (339-342): : 339 - 342
  • [50] Microstructural and superconducting properties in single-domain Gd-Ba-Cu-O bulk superconductors with in situ formed Fe3O4 ferrimagnetic particles
    Xu, Kun
    Tsuzuki, Keita
    Hara, Shogo
    Zhou, Difan
    Zhang, Yufeng
    Murakami, Masato
    Nishio-Hamane, Daisuke
    Izumi, Mitsuru
    SUPERCONDUCTOR SCIENCE & TECHNOLOGY, 2011, 24 (08):
12345