LAW OF CRACK GROWTH LIFE FOR P92 STEEL UNDER THE CONDITIONS OF CREEP-FATIGUE MULTIPLICATION AND PROJECTION OF THE THRESHOLD TEMPERATURE OF CREEP CRACK GROWTH BASED ON THIS LAW

被引：0
|
作者：
Yokobori, A. T., Jr. [1 ]
Sugiura, R. [1 ]
Kimoto, S. [1 ]
Yoshino, D. [1 ]
Matsuzaki, T. [1 ]
机构：
[1] Tohoku Univ, Grad Sch Engn, Sendai, Miyagi 980, Japan
来源：
PROCEEDINGS OF THE ASME PRESSURE VESSELS AND PIPING CONFERENCE, VOL 6, PTS A AND B | 2010年
关键词：
D O I：
暂无
中图分类号：
TH [机械、仪表工业];
学科分类号：
0802 ;
摘要：
W-added 9Cr ferritic heat-resistant steels, ASME grade P92, are used under the high temperature creep-fatigue condition. Concerning the maintenance of the operational safety and minimizing operational costs, it is necessary to construct a law of predicting the crack growth life by clarifying the dominant factors of the crack growth life under the condition of creepfatigue multiplication (the effect of stress holding time on the time-dependent fracture). In this study, crack growth tests under the conditions of creep-fatigue multiplication were conducted with various conditions of stress holding time, applied stress and temperatures. As a result, a unified law of predicting the crack growth life under the conditions of creep-fatigue multiplication was derived based on the concept of Q* with the transition function of crack growth life from fatigue to creep.
引用
收藏
页码：1451 / 1460
页数：10
相关论文
共 50 条
  • [41] Creep-Fatigue Crack Growth in Power Plant Steels
    Stuart Holdsworth
    Transactions of the Indian Institute of Metals, 2016, 69 : 353 - 358
  • [42] Modelling the effect of creep-fatigue interaction on crack growth
    Grover, PS
    Saxena, A
    FATIGUE & FRACTURE OF ENGINEERING MATERIALS & STRUCTURES, 1999, 22 (02) : 111 - 122
  • [43] Creep-Fatigue Crack Growth in Power Plant Steels
    Holdsworth, Stuart
    TRANSACTIONS OF THE INDIAN INSTITUTE OF METALS, 2016, 69 (02) : 353 - 358
  • [44] METHODS FOR DETERMINING CREEP DAMAGE AND CREEP-FATIGUE CRACK GROWTH INCUBATION IN AUSTENITIC STAINLESS STEEL
    Webster, George A.
    Dean, David W.
    Spindler, Michael W.
    Smith, N. Godfrey
    PROCEEDINGS OF THE ASME PRESSURE VESSELS AND PIPING CONFERENCE, VOL 6, PTS A AND B, 2010, : 671 - 683
  • [45] A closure model for predicting crack growth under creep-fatigue loading
    Potirniche, Gabriel P.
    INTERNATIONAL JOURNAL OF FATIGUE, 2019, 125 : 58 - 71
  • [46] Early Crack Growth from Notches under Creep-Fatigue Loading
    Garnadt, Florian
    Kontermann, Christian
    Oechsner, Matthias
    23 EUROPEAN CONFERENCE ON FRACTURE, ECF23, 2022, 42 : 1113 - 1120
  • [47] Creep-fatigue crack growth behaviour of P91 steels
    Ab Razak, N.
    Davies, C. M.
    Nikbin, K. M.
    21ST EUROPEAN CONFERENCE ON FRACTURE, (ECF21), 2016, 2 : 855 - 862
  • [48] Models for Small Crack Growth under Creep-Fatigue in Austenitic Steels
    Skelton, R. P.
    CREEP-FATIGUE INTERACTIONS: TEST METHODS AND MODELS, 2011, 1539 : 142 - 177
  • [49] Creep-fatigue crack growth from a stress concentration
    Holdsworth, SR
    MATERIALS AT HIGH TEMPERATURES, 1998, 15 (02) : 111 - 116
  • [50] The Effect of Dwell Time to Creep-Fatigue Crack Growth
    Li, Wen
    Zhang, Guobin
    Yang, Xiaohong
    Jiao, Yan
    PROCEEDINGS OF THE 2016 3RD INTERNATIONAL CONFERENCE ON MATERIALS ENGINEERING, MANUFACTURING TECHNOLOGY AND CONTROL, 2016, 67 : 1036 - 1039
12345