Ceramic membrane synthesis based on alkali activated blast furnace slag for separation of water from ethanol

The main purpose of this research is synthesis of zeolite ceramic membranes based on alkali activated blast furnace slag for pervaporation separation of ethanol/water mixture (90 wt%). A new and simple method was applied to fabricate these ceramic membranes. In addition, gross waste of steel industry (blast furnace slag) was firstly used as the main starting material for making the membranes. In this study, for making the zeolite ceramic membranes, some experiments were conducted with water levels of 38, 40, 42 and 44 wt% of the blast furnace slag and NaOH levels of 4, 4.2, 4.4 and 4.6 wt% of the blast furnace slag. At first, for making the membranes, a primary geopolymer gel was prepared. Afterward the membranes were cast at 25 degrees C for 24 h. In order to form the zeolite layer, the membranes after geopolymerization process were kept at 90 degrees C for 24 h. The maximum value of selectivity (2579.48) was obtained for separation of water from ethanol using the synthesized membrane with 42 wt% water and 4 wt% NaOH. (C) 2016 Elsevier Ltd and Techna Group S.r.l. All rights reserved.