Microstructure of high Jc NdBa2Cu3Ox/Nd4Ba2Cu2O10 composite superconductor

被引：0
|
作者：
Matsuoka, S
Sumida, M
Umeda, T
Shiohara, Y
机构：
[1] ISTEC, Superconduct Res Lab, Koto Ku, Tokyo 135, Japan
[2] Univ Tokyo, Grad Sch Engn, Bunkyo Ku, Tokyo 113, Japan
来源：
APPLIED SUPERCONDUCTIVITY | 1997年 / 5卷 / 1-6期
关键词：
D O I：
10.1016/S0964-1807(98)00017-9
中图分类号：
T [工业技术];
学科分类号：
08 ;
摘要：
Single crystalline NdBa2Cu3Ox (Nd123) superconductors with dispersed Nd4Ba2Cu2O10 (Nd422) particles were produced by the floating zone partial melting and solidification (FZPMS) method. The initial composition of the precursor material was Nd1.8Ba2.4Cu3.4Ox with or without 0.1 wt% Pt addition. FZPMS was carried out in a low oxygen partial pressure atmosphere. Microstructure of quenched samples were investigated by optical microscopy, scanning electron microscopy (SEM) and electron probe microanalysis (EPMA). Furthermore, superconductive properties were measured by superconducting quantum interference device (SQUID:). The results of SQUID measurements indicate that the critical temperature (T-c) of the samples with Pt addition so produced with the oxygen heat treatment (623 K for 300 h) was 94 K and the critical current density (J(c)) was 2.3 x 10(4) A/cm(2) at 77 K, 0.2 T. (C) 1998 Published by Elsevier Science Ltd. All rights reserved.
引用
收藏
页码：139 / 146
页数：8
相关论文
共 50 条
  • [31] FORMATION PROCESSES OF POLYCRYSTALLINE LABA2CU3OX, NDBA2CU3OX, SMBA2CU3OX, EUBA2CU3OX, GDBA2CU3OX, DYBA2CU3OX, HOBA2CU3OX, ERBA2CU3OX, TMBA2CU3OX, YBBA2CU3OX AND LUBA2CU3OX
    ITOH, T
    UZAWA, M
    UCHIKAWA, H
    JOURNAL OF CRYSTAL GROWTH, 1988, 91 (03) : 397 - 401
  • [32] Enhancement of Jc by refinement of Nd4Ba2Cu2O10 particles in OCMG processed Nd-Ba-Cu-O system with Pt and CeO2 addition (vol B65, 48, 1999)
    Chauhan, HS
    Murakami, M
    MATERIALS SCIENCE AND ENGINEERING B-SOLID STATE MATERIALS FOR ADVANCED TECHNOLOGY, 2000, 72 (01): : 59 - 59
  • [33] SCANNING PROBE MICROSCOPY OF NDBA2CU3OX THIN-FILM SURFACES
    BADAYE, M
    TING, W
    FUKUSHIMA, K
    KOSHIZUKA, N
    MORISHITA, T
    TANAKA, S
    APPLIED PHYSICS LETTERS, 1995, 67 (15) : 2155 - 2157
  • [34] Preparation of NdBa2Cu3Ox thin films and their superconducting properties in magnetic fields
    Ichino, Y
    Matsumoto, K
    Takahashi, Y
    Kim, S
    Ikuta, H
    Hirabayashi, I
    Mizutani, U
    ADVANCES IN SUPERCONDUCTIVITY XII, 2000, : 879 - 881
  • [35] DEPRESSION OF T-C CAUSED BY ND+3 PAIR-BREAKING IN NDBA2CU3OX
    BLACKSTEAD, HA
    DOW, JD
    PACKARD, WE
    PULLING, DB
    PHYSICA C, 1994, 235 : 1363 - 1364
  • [36] Observation of an inelastic scattering mode by scanning tunneling spectroscopy on NdBa2Cu3Ox
    Das, Pintu
    Koblischka, Michael R.
    Hartmann, Uwe
    PROCEEDINGS OF THE INTERNATIONAL CONFERENCE ON NANOSCIENCE AND TECHNOLOGY, 2007, 61 : 234 - 238
  • [37] High temperature phase relationships in (Y,Nd)-123 superconducting oxides:: the Y2BaCuO5-Nd4Ba2Cu2O10-Ba3Cu5Ox system
    Kambara, M
    Babu, NH
    Shi, Y
    Cardwell, DA
    SUPERCONDUCTOR SCIENCE & TECHNOLOGY, 2002, 15 (05): : 708 - 711
  • [38] INTERPRETATION OF THE MAGNETIC SPECIFIC-HEAT OF OXYGEN-DEFICIENT AND DOPED NDBA2CU3OX AND DYBA2CU3OX COMPOUNDS
    ALLENSPACH, P
    MAPLE, MB
    FURRER, A
    JOURNAL OF ALLOYS AND COMPOUNDS, 1994, 207 : 213 - 220
  • [39] VALENCE BANDS, OXYGEN IN PLANES AND CHAINS, AND SURFACE CHANGES FOR SINGLE-CRYSTALS OF PR2CUO4, ND2CUO4, EU2CUO4, GD2CUO4 AND PRBA2CU3OX, NDBA2CU3OX, EUBA2CU3OX, GDBA2CU3OX
    WEAVER, JH
    MEYER, HM
    WAGENER, TJ
    HILL, DM
    GAO, Y
    PETERSON, D
    FISK, Z
    ARKO, AJ
    PHYSICAL REVIEW B, 1988, 38 (07): : 4668 - 4676
  • [40] The effects of chemical doping and hydrostatic pressure on Tc of Y1-yCayBa2Cu3Ox and NdBa2Cu3Ox single crystals
    Schlachter, SI
    Weiss, KP
    Fietz, WH
    Grube, K
    Leibrock, H
    Wolf, T
    Obst, B
    Schweiss, P
    Kläser, M
    Wühl, H
    JOURNAL OF LOW TEMPERATURE PHYSICS, 1999, 117 (3-4) : 921 - 925
12345