Atomistic modeling of the tensile behavior of monoclinic ZrO2 bicrystal

被引:2
|
作者
Wang, C. [1 ]
Feng, R. [1 ]
Diestler, D. J. [2 ]
Zeng, X. C. [3 ]
机构
[1] Univ Nebraska, Dept Engn Mech, Lincoln, NE 68588 USA
[2] Univ Nebraska, Dept Agron & Hort, Lincoln, NE 68583 USA
[3] Univ Nebraska, Dept Chem, Lincoln, NE 68588 USA
基金
美国国家科学基金会;
关键词
MOLECULAR-DYNAMICS SIMULATION; GRAIN-BOUNDARY; STABILIZED ZIRCONIA; DEFORMATION; STRENGTH;
D O I
10.1063/1.3452340
中图分类号
O59 [应用物理学];
学科分类号
摘要
Molecular dynamics was used to simulate the tensile behavior of monoclinic ZrO2 bicrystals constructed by fusing two symmetrically tilted single crystals at several temperatures ranging from 300 to 1200 K and then annealing them to 300 K. The average amorphous grain boundary (GB) is about 11 angstrom thick (approximately twice the average unit-cell dimension). Axial elongation of the typical bicrystal at constant (boundary) velocity leads to failure at a global strain of about 4%, at which the maximum stress (i.e., the tensile strength) is approximately 6 GPa. The failure process is ductile, driven by growth and coalescence of voids in the GB, in contrast with that of the monoclinic single crystal, which undergoes essentially brittle fracture at a tensile stress of around 10 GPa. The tensile strength of the bicrystal is approximately inversely proportional to the thickness of the GB. Decreasing the fusion temperature increases the thickness of the GB and lowers the tensile strength accordingly. The dependence of tensile strength on the loading rate is insignificant for the range of tilt angles and loading conditions examined. The influence of the GB on the small-strain effective elastic response of the bicrystal is also insignificant. (C) 2010 American Institute of Physics. [doi:10.1063/1.3452340]
引用
收藏
页数:9
相关论文
共 50 条
  • [21] SLIP CASTING OF MONOCLINIC ZRO2 FIBER PZT COMPOSITES
    TAKAHASHI, M
    BABA, K
    NISHIZATO, O
    TAKAMURA, A
    KATSUBE, M
    NIPPON SERAMIKKUSU KYOKAI GAKUJUTSU RONBUNSHI-JOURNAL OF THE CERAMIC SOCIETY OF JAPAN, 1993, 101 (12): : 1404 - 1408
  • [22] VAPOR-PHASE GROWTH OF MONOCLINIC ZRO2 WHISKERS
    EGASHIRA, M
    KATSUKI, H
    TAKATSUKI, S
    IWANAGA, H
    YOGYO-KYOKAI-SHI, 1987, 95 (01): : 138 - 143
  • [23] Synthesis of Monoclinic and Cubic ZrO2 Nanoparticles from Zircon
    Manivasakan, Palanisamy
    Rajendran, Venkatachalam
    Rauta, Prema Ranjan
    Sahu, Bhakta Bandhu
    Panda, Bharati Krushna
    JOURNAL OF THE AMERICAN CERAMIC SOCIETY, 2011, 94 (05) : 1410 - 1420
  • [24] Formation mechanism of monoclinic ZrO2 at the contact of YSZ with CuO
    A. A. Bokov
    A. V. Nikonov
    Inorganic Materials, 2015, 51 : 553 - 558
  • [25] The (011) Twin Structure Periodical in Monoclinic ZrO2 Nanofiber
    Yang, Qing
    Tatsuoka, Hirokazu
    Tanaka, Miyoko
    E-JOURNAL OF SURFACE SCIENCE AND NANOTECHNOLOGY, 2014, 12 : 418 - 419
  • [26] Pure monoclinic ZrO2 prepared by hydrothermal method for isosynthesis
    Zhang, Rongjun
    Liu, Huimin
    He, Dehua
    CATALYSIS COMMUNICATIONS, 2012, 26 : 244 - 247
  • [27] Formation mechanism of monoclinic ZrO2 at the contact of YSZ with CuO
    Bokov, A. A.
    Nikonov, A. V.
    INORGANIC MATERIALS, 2015, 51 (06) : 553 - 558
  • [28] DIFFUSE REFLECTANCE CHARACTERISTICS OF MONOCLINIC ZRO2 AS A FUNCTION OF PURITY
    SARVER, JF
    AMERICAN CERAMIC SOCIETY BULLETIN, 1967, 46 (09): : 837 - &
  • [29] Thermoluminescence of monoclinic ZrO2: Kinetic analysis and dosimetric features
    Lokesha, H. S.
    Chithambo, M. L.
    Chikwembani, S.
    JOURNAL OF LUMINESCENCE, 2020, 218 (218)
  • [30] DIFFUSE REFLECTANCE CHARACTERISTICS OF MONOCLINIC ZRO2 AS A FUNCTION OF PURITY
    SARVER, JF
    AMERICAN CERAMIC SOCIETY BULLETIN, 1966, 45 (04): : 383 - &