Preparation and characterization of a new phosphor Lu2O3: Eu3+

被引：0
|
作者：
Chen, QW [1 ]
Shi, Y [1 ]
Shi, JL [1 ]
机构：
[1] Chinese Acad Sci, Shanghai Inst Ceram, Shanghai 200050, Peoples R China
来源：
HIGH-PERFORMANCE CERAMICS III, PTS 1 AND 2 | 2005年 / 280-283卷
关键词：
Lu2O3 : Eu3+; phosphor; combustion synthesis; photoluminescence;
D O I：
10.4028/www.scientific.net/KEM.280-283.525
中图分类号：
TQ174 [陶瓷工业]; TB3 [工程材料学];
学科分类号：
0805 ; 080502 ;
摘要：
Europium-doped Lu2O3 nanocrystalline powders were prepared via a novel solution combustion route, with glycine as the fuel. The crystalline size and specific surface area of the combustion derived powders are strongly dependent on the glycine-to-nitrate ratio, which can control the combustion flame temperature. XRD, SEM, TEM and BET were used to characterize the phosphors and the photoluminescence was also investigated. Lu2O3:Eu3+ exhibits narrow-band red emission extending from 580-700nm with a sharp peak at 611nm, corresponding to D-5(0) F-7(2) transition of the Eu3+ ion.
引用
收藏
页码：525 / 528
页数：4
相关论文
共 50 条
  • [21] Theoretical analysis on quenching mechanisms for Lu2O3: Eu3+ nanospheres
    Bingye Zhang
    Lu Han
    Ye Qi
    Jinsu Zhang
    Baojiu Chen
    Journal of Materials Science: Materials in Electronics, 2017, 28 : 18015 - 18021
  • [22] Luminescence properties of a Lu2O3:Eu3+ nano-phosphor and radiation hardness measurements with a proton beam
    Myeongjin Oh
    H. J. Kim
    Sunghwan Kim
    ChongKyu Cheon
    Journal of the Korean Physical Society, 2012, 61 : 273 - 277
  • [23] Luminescence properties of Eu3+:Y2O3 and Eu3+:Lu2O3 nanoparticles, ceramics and thin films
    Zhang, K
    Hunter, D
    Mohanty, S
    Dadson, JB
    Barnakov, Y
    Pradhan, AK
    Organic and Nanocomposite Optical Materials, 2005, 846 : 231 - 235
  • [24] Electrospinning synthesis and luminescent properties of Lu2O3:Eu3+ nanofibers
    张浩
    陈金灯
    郭海
    JournalofRareEarths, 2010, 28(S1) (S1) : 232 - 235
  • [25] Sol-Gel Template Synthesis and Characterization of Lu2O3:Eu3+ Nanowire Arrays
    Hu, Yahua
    Gu, Mu
    Liu, Xiaolin
    Zhang, Juannan
    Huang, Shiming
    Liu, Bo
    MICROMACHINES, 2018, 9 (11):
  • [26] The synthesis and luminescence properties of Lu2O3:Eu3+ rods and its comparative analysis with Lu2O2S:Eu3+ rods
    Wang, Ze
    Qian, Benfu
    Wang, Hongyang
    Wang, Di
    Zou, Haifeng
    Song, Yanhua
    Zhou, Xiuqing
    Sheng, Ye
    OPTICAL MATERIALS, 2020, 109
  • [27] Luminescence properties of a Lu2O3:Eu3+ nano-phosphor and radiation hardness measurements with a proton beam
    Oh, Myeongjin
    Kim, H. J.
    Kim, Sunghwan
    Cheon, ChongKyu
    JOURNAL OF THE KOREAN PHYSICAL SOCIETY, 2012, 61 (02) : 273 - 277
  • [28] Preparation and luminescence properties of Lu2O3:Eu3+ nanofibers by sol-gel/electrospinning process
    Li, Xue
    Yu, Min
    Hou, Zhiyao
    Wang, Wenxin
    Li, Guogang
    Cheng, Ziyong
    Chai, Ruitao
    Lin, Jun
    JOURNAL OF COLLOID AND INTERFACE SCIENCE, 2010, 349 (01) : 166 - 172
  • [29] Photoluminescence and structural characteristics of LU2O3:Eu3+ nanocrystallites in silica matrix
    Sokolnicki, Jerzy
    JOURNAL OF SOLID STATE CHEMISTRY, 2007, 180 (08) : 2400 - 2408
  • [30] Processing and scintillation properties of Eu3+ doped Lu2O3 transparent ceramics
    Shi, Y.
    Chen, Q. W.
    Shi, J. L.
    OPTICAL MATERIALS, 2009, 31 (05) : 729 - 733
12345