Hydrochloric acid leaching of Panzhihua ilmenite for preparation of synthetic rutile

Investigation on hydrochloric acid leaching of the ilmenite from Panzhihua, China was carried out to prepare synthetic rutile. The leaching parameters were optimized to obtain high content of TiO2 in the products. The experimental data suggest that an optimum leaching can be realized with 30% acid, a solid/liquid ratio of 1/4 at 95 degrees C for 4h, and ore ground for -400 mesh size. After the acid leaching, an additional alkaline leaching process using hot NaOH solution was performed, and then the products was in grain form followed by heat treated at 900 C for 2h in order to extract Si and increase the particle size of synthetic rutile. The final product has a high content of TiO2 (about 95%), a low content of chlorine consuming elements (total CaO+MgO =0.07%) and a suitable particle size distribution for chlorination process.