Structure and Magnetic Properties of S-doped Mn3O4/S Composited Nanoparticles and Mn3O4 Nanoparticles

Composited nanoparticles, consisting of Mn3O4, S-doped Mn3O4 and 5, were synthesized by co-precipitation reaction and Mn3O4 nanoparticles were then obtained after removing the pure S from the composited nanoparticles. The Mn3O4-type phase with larger lattice constant a was formed by doping sulfur. At fixed temperatures below Curie temperature (T-C), the magnetization of the S-doped Mn3O4/S composited nanoparticles was smaller than that of the Mn3O4 nanoparticles. The blocking temperature was 36.3 and 34.8 K for S-doped Mn3O4/S composite and Mn3O4 nanoparticles, respectively. The anisotropy field of S-doped Mn3O4/S composite was determined to be about 55.3 kOe.