Characteristics of Development of Fatigue Cracks in Steel under Low-Level Operation Loading

被引：0
|
作者：
Lebedinskii, S. G. [1 ]
Moskvitin, G. V. [1 ]
Pugachev, M. S. [1 ]
Polyakov, A. N. [1 ]
机构：
[1] Russian Acad Sci, Blagonravov Inst Mech Engn, Moscow 101990, Russia
来源：
JOURNAL OF MACHINERY MANUFACTURE AND RELIABILITY | 2020年 / 49卷 / 02期
基金：
俄罗斯基础研究基金会;
关键词：
operational loading; low-alloyed steel; fatigue cracks; crack growth under low-level loading; railway structures;
D O I：
10.3103/S1052618820020107
中图分类号：
TH [机械、仪表工业];
学科分类号：
0802 ;
摘要：
An assessment method for characteristics of low-rate development of fatigue cracks under operational loading is proposed. The method is based on the decrease in the irregular loading level by conservation of its conformity during crack growth. The control factor of the loading decrease is the intrinsic increase in the compliance of a sample during crack growth by its fixed opening. The experimental dependences of the crack growth rate on the number of operation load blocks with a decrease in the loading level are obtained.
引用
收藏
页码：144 / 149
页数：6
相关论文
共 50 条
  • [41] FATIGUE CRACK-GROWTH IN HIGH AND LOW STRENGTH STEEL UNDER TORSIONAL LOADING
    TSCHEGG, EK
    THEORETICAL AND APPLIED FRACTURE MECHANICS, 1985, 3 (02) : 157 - 178
  • [42] Extremely low cycle fatigue fracture prediction of steel connections under cyclic loading
    Wang, W. (weiwang@tongji.edu.cn), 1600, Science Press (42):
  • [43] Reliability Analysis of Steel Bridges under Propagating Fatigue Cracks
    Ali, H.
    Soliman, M.
    MAINTENANCE, SAFETY, RISK, MANAGEMENT AND LIFE-CYCLE PERFORMANCE OF BRIDGES, 2018, : 614 - 619
  • [44] DAMAGE DEVELOPMENT OF A LOW-CARBON STEEL UNDER BIAXIAL LOADING
    BERARD, JY
    ANTOLOVICH, SD
    REVUE DE METALLURGIE-CAHIERS D INFORMATIONS TECHNIQUES, 1991, 88 (06): : 557 - 563
  • [45] THERE IS NO LOW-LEVEL FERTILITY AND DEVELOPMENT TRAP
    SIMON, JL
    POPULATION STUDIES-A JOURNAL OF DEMOGRAPHY, 1980, 34 (03): : 476 - 486
  • [46] Mathematical modeling of fatigue fracture of plates with cracks under block loading
    Andreikiv O.E.
    Kit M.B.
    Khyl' S.V.
    Journal of Mathematical Sciences, 2013, 190 (6) : 752 - 763
  • [47] Fatigue propagation threshold of short cracks under constant amplitude loading
    Chapetti, MD
    INTERNATIONAL JOURNAL OF FATIGUE, 2003, 25 (12) : 1319 - 1326
  • [48] Fatigue crack growth behavior of corner cracks under LBH loading
    Oh, CS
    Park, P
    Huh, YH
    Ko, SG
    Hwang, DY
    An, HM
    ADVANCES IN FRACTURE AND STRENGTH, PTS 1- 4, 2005, 297-300 : 128 - 133
  • [49] DEVELOPMENT OF SUBMICROSCOPIC CRACKS IN POLYMERS UNDER CYCLIC LOADING
    KNOPOV, VM
    SLUTSKER, AI
    SOVIET PHYSICS SOLID STATE,USSR, 1970, 12 (04): : 918 - &
  • [50] THE GROWTH OF SHORT FATIGUE CRACKS UNDER COMPRESSIVE AND OR TENSILE CYCLIC LOADING
    MCEVILY, AJ
    YANG, Z
    METALLURGICAL TRANSACTIONS A-PHYSICAL METALLURGY AND MATERIALS SCIENCE, 1991, 22 (05): : 1079 - 1082
12345