Impact of corrosion on low-cycle fatigue degradation of reinforcing bars with the effect of inelastic buckling

被引：72
|
作者：
Kashani, Mohammad M. [1 ]
Alagheband, Peyman [2 ]
Khan, Rafid [1 ]
Davis, Sean [3 ]
机构：
[1] Univ Bristol, Dept Civil Engn, Bristol BS8 1TR, Avon, England
[2] Univ Surrey, Univ Bristol, Dept Civil Engn, Guildford GU2 5XH, Surrey, England
[3] Univ Bristol, Sch Chem, Bristol BS8 1TR, Avon, England
来源：
INTERNATIONAL JOURNAL OF FATIGUE | 2015年 / 77卷
基金：
英国工程与自然科学研究理事会;
关键词：
Low-cycle fatigue; Corrosion; Buckling; Cyclic behaviour; Reinforcing steel; STEEL BARS; BEHAVIOR; COLUMNS; PATTERN;
D O I：
10.1016/j.ijfatigue.2015.03.013
中图分类号：
TH [机械、仪表工业];
学科分类号：
0802 ;
摘要：
The combined effect of inelastic buckling and chloride induced corrosion damage on low-cycle high amplitude fatigue life of embedded reinforcing bars in concrete is investigated experimentally. A total of forty-eight low-cycle fatigue tests on corroded reinforcing bars varied in percentage mass loss, strain amplitudes and buckling lengths are conducted. The failure modes and crack propagation are investigated by fractography of fracture surfaces using scanning electron microscope. The results show that the inelastic buckling, percentage mass loss and nonuniform corrosion pattern are the main parameters affecting the low-cycle fatigue life of reinforcing bars. It was found that the fatigue life of corroded reinforcing bars combined with inelastic buckling has a significant path dependency. The results show that in some cases the number of cycles to failure of corroded bars under constant amplitude fatigue test is increased. (C) 2015 Elsevier Ltd. All rights reserved.
引用
收藏
页码：174 / 185
页数：12
相关论文
共 50 条
  • [31] Effects of Corrosion and Ribs on Low Cycle Fatigue Behavior of Reinforcing Steel Bars S400
    Apostolopoulos, Ch. Alk.
    Pasialis, V. P.
    JOURNAL OF MATERIALS ENGINEERING AND PERFORMANCE, 2010, 19 (03) : 385 - 394
  • [32] Low-Cycle Fatigue Tests of a Type of Buckling Restrained Braces
    Usami, Tsutomu
    Wang, Chunlin
    Funayama, Jyunki
    PROCEEDINGS OF THE TWELFTH EAST ASIA-PACIFIC CONFERENCE ON STRUCTURAL ENGINEERING AND CONSTRUCTION (EASEC12), 2011, 14 : 956 - 964
  • [33] Concrete Cover Influence on Inelastic Buckling of Longitudinal Reinforcing Bars
    Korentz, Jacek
    Kucharczyk, Anna
    WORLD MULTIDISCIPLINARY CIVIL ENGINEERING-ARCHITECTURE-URBAN PLANNING SYMPOSIUM - WMCAUS, 2017, 245
  • [34] FATIGUE CURVE FOR LOW-CYCLE LOADING IN CORROSION MEDIA
    PETRIK, VM
    PROTECTION OF METALS, 1978, 14 (03): : 249 - 250
  • [35] Modelling inelastic buckling of reinforcing bars under earthquake loading
    Fragiadakis, Michalis
    Pinho, Rui
    Antoniou, Stelios
    COMPUTATIONAL STRUCTURAL DYNAMICS AND EARTHQUAKE ENGINEERING, 2009, 2 : 347 - +
  • [36] Effect of corrosion on mass loss, and high and low cycle fatigue of reinforcing steel
    Ch. Alk Apostolopoulos
    D. Michalopoulos
    Journal of Materials Engineering and Performance, 2006, 15 : 742 - 749
  • [37] Effect of corrosion on mass loss, and high and low cycle fatigue of reinforcing steel
    Apostolopoulos, Ch. Alk.
    Michalopoulos, D.
    JOURNAL OF MATERIALS ENGINEERING AND PERFORMANCE, 2006, 15 (06) : 742 - 749
  • [38] Evaluation of the Low-Cycle Fatigue Life in ASTM A706 and A615 Grade 60 Steel Reinforcing Bars
    Hawileh, R.
    Rahman, A.
    Tabatabai, H.
    JOURNAL OF MATERIALS IN CIVIL ENGINEERING, 2010, 22 (01) : 65 - 76
  • [39] Compressive stress?strain behaviour of stainless steel reinforcing bars with the effect of inelastic buckling
    Limbert, J.
    Afshan, S.
    Kashani, M. M.
    Robinson, A. F.
    ENGINEERING STRUCTURES, 2021, 237
  • [40] Nonlinear stress-strain behavior of corrosion-damaged reinforcing bars including inelastic buckling
    Lin, Mingqiang
    Dai, Fengjuan
    Li, Jiatao
    PROCEEDINGS OF THE 2017 7TH INTERNATIONAL CONFERENCE ON ADVANCED DESIGN AND MANUFACTURING ENGINEERING (ICADME 2017), 2017, 136 : 288 - 291
12345