Effect of aging temperature and martensite by volume on strain aging behaviour of dual phase steel

被引：18
|
作者：
Guenduez, S. [1 ]
Demir, B. [1 ]
Kacar, R. [1 ]
机构：
[1] Zonguldak Karaelmas Univ, Karabuk Tech Educ Fac, Dept Mat, TR-78200 Karabuk, Turkey
来源：
IRONMAKING & STEELMAKING | 2008年 / 35卷 / 01期
关键词：
dual phase steels; strain aging; martensite; tensile fracture;
D O I：
10.1179/174328107X203949
中图分类号：
TF [冶金工业];
学科分类号：
0806 ;
摘要：
A study has been made of the cold deformation aging susceptibility of dual phase steel with 14 and 22% martensite by volume. It was found that yield strength (YS) and ultimate tensile strength (UTS) increased with increasing testing temperature up to 200 degrees C and then decreased at 250 degrees C which indicated that static strain aging is dominant up to 200 degrees C. This aging is associated with free dislocations in the ferrite as a result of the austenite-martensite transformation, which become preferential sites for solute atom diffusion. At higher temperature (250 degrees C) a softening effect is dominant due to tempering of martensite. It was also observed that at a given aging temperature YS, UTS and Delta Y (increase in stress due to strain aging) increased with by volume of martensite.
引用
收藏
页码：63 / 68
页数：6
相关论文
共 50 条
  • [21] EFFECT OF AUSTENIZATION TEMPERATURE ON AGING PROCESSES IN THE MARTENSITIC AGING OF STEEL
    GRACHEV, SV
    MALTSEVA, LA
    RUSSIAN METALLURGY, 1992, (03): : 78 - 82
  • [22] Effect of Martensite Volume Fraction on Forming Limit Diagrams of Dual-Phase Steel
    Mohammad Zaeimi
    Ali Basti
    Majid Alitavoli
    Journal of Materials Engineering and Performance, 2015, 24 : 1781 - 1789
  • [23] ON THE EFFECT OF THE VOLUME FRACTION OF MARTENSITE ON THE TENSILE-STRENGTH OF DUAL-PHASE STEEL
    JENA, AK
    CHATURVEDI, MC
    MATERIALS SCIENCE AND ENGINEERING, 1988, 100 : 1 - 6
  • [24] Effect of martensite volume fraction on stress triaxiality and deformation behavior of dual phase steel
    Paul, Surajit Kumar
    MATERIALS & DESIGN, 2013, 50 : 782 - 789
  • [25] Effect of Martensite Volume Fraction on Forming Limit Diagrams of Dual-Phase Steel
    Zaeimi, Mohammad
    Basti, Ali
    Alitavoli, Majid
    JOURNAL OF MATERIALS ENGINEERING AND PERFORMANCE, 2015, 24 (05) : 1781 - 1789
  • [26] Effect of Temper-Aging Temperature on the Microstructures and Properties of the Annealed High Aluminum Dual Phase Steel
    Wang Hui
    Deng Zhaojun
    Lin Chengjiang
    Ye Zhongchao
    Zhong Dingzhong
    RARE METAL MATERIALS AND ENGINEERING, 2011, 40 : 184 - 187
  • [27] 2-STAGE STRAIN-AGING RESPONSE IN A DUAL-PHASE STEEL
    GOODMAN, K
    HAWORTH, WL
    HIMMEL, L
    JOURNAL OF METALS, 1980, 32 (12): : 46 - 46
  • [28] Martensite morphology and strain aging behaviours in intercritically treated low carbon steel
    Turkmen, M.
    Gunduz, S.
    IRONMAKING & STEELMAKING, 2011, 38 (05) : 346 - 352
  • [29] Mechanism of martensite aging effect
    Otsuka, K
    Ren, X
    SCRIPTA MATERIALIA, 2004, 50 (02) : 207 - 212
  • [30] On the Low Temperature Strain Aging of Bainite in the TRIP Steel
    Timokhina, Ilana
    Beladi, Hossein
    Xiong, Xiang-Yuan
    Hodgson, Peter D.
    METALLURGICAL AND MATERIALS TRANSACTIONS A-PHYSICAL METALLURGY AND MATERIALS SCIENCE, 2013, 44A (11): : 5177 - 5191
12345