Anisotropy of the Cyclic Crack Resistance of Aluminum Alloys After Long-Term Operation

被引：0
|
作者：
Andreiko, I. M. [1 ]
Holovatyuk, Yu. V. [1 ]
Ostash, O. P. [1 ]
Semenets', O. I. [2 ]
Koval'chuk, L. B. [1 ]
机构：
[1] Ukrainian Natl Acad Sci, Karpenko Physicomech Inst, Lvov, Ukraine
[2] ANTONOV State Enterprise, Kiev, Ukraine
来源：
MATERIALS SCIENCE | 2016年 / 52卷 / 01期
关键词：
aluminum alloys; in-service degradation; cyclic crack resistance; anisotropy;
D O I：
10.1007/s11003-016-9929-x
中图分类号：
T [工业技术];
学科分类号：
08 ;
摘要：
We study the characteristics of cyclic crack resistance of specimens of D16ATNV (2024-T3-type) and V95T1 (7075-T6-type) aluminum alloys cut out from different zones of the wing of an AN-12 aircraft after 40 yr of operation along (LT-specimens) and across (TL-specimens) the direction of forge-rolling of skin sheets. It is shown that, as compared with the as-delivered state of these alloys, the D16ATNV and V95T1 aluminum alloys after long-term operation are characterized by the "reverse anisotropy" when the growth rate of fatigue macrocracks in the LT-specimens is higher than in the TL-specimens. Depending on the Al-Cu-Mg alloying system (D16-type alloy) or the Al-Zn-Mg-Cu system (V95-type alloy), this phenomenon can manifest itself in different ways in the tests carried out in air at room and low (- 60A degrees C) temperatures and in corrosive media.
引用
收藏
页码：83 / 88
页数：6
相关论文
共 50 条
  • [41] Long-term failure of isotropic viscoelastic material with a crack under cyclic loading
    Selivanov, M.F.
    Prikladnaya Mekhanika, 1999, 35 (02): : 60 - 64
  • [42] DETERMINATION OF THE BOUNDARIES OF SHORT-TERM AND LONG-TERM FATIGUE IN ALUMINUM-ALLOYS
    EVSEEV, VV
    RUSSIAN METALLURGY, 1989, (03): : 127 - 130
  • [43] Low-temperature cyclic crack resistance of degraded V95-type aluminum alloys
    Andreiko, I. M.
    Holovatyuk, Yu V.
    Koval'chuk, L. B.
    Semenets', O. I.
    Ostash, O. P.
    MATERIALS SCIENCE, 2012, 48 (03) : 259 - 265
  • [44] Low-temperature cyclic crack resistance of degraded V95-type aluminum alloys
    I. M. Andreiko
    Yu. V. Holovatyuk
    L. B. Koval’chuk
    O. I. Semenets’
    O. P. Ostash
    Materials Science, 2012, 48 : 259 - 265
  • [45] Long-term crack resistance of aging viscoelastic composite in static loading
    Gavrilov, GV
    INTERNATIONAL APPLIED MECHANICS, 1999, 35 (02) : 190 - 194
  • [46] Long-term crack resistance of aging viscoelastic composite in static loading
    G. V. Gavrilov
    International Applied Mechanics, 1999, 35 : 190 - 194
  • [47] A device for evaluation of the long-term crack resistance of materials in liquid media
    Pestrikov, VM
    INDUSTRIAL LABORATORY, 1998, 64 (11): : 755 - 756
  • [48] Forecasting crack resistance of short- and long-term loaded coatings
    Glodkowska, W.
    ARCHIVES OF CIVIL AND MECHANICAL ENGINEERING, 2011, 11 (01) : 33 - 44
  • [49] THE LONG-TERM PROGNOSIS AFTER OPERATION FOR LUMBAR SPINAL STENOSIS
    HERNO, A
    AIRAKSINEN, O
    SAARI, T
    SCANDINAVIAN JOURNAL OF REHABILITATION MEDICINE, 1993, 25 (04): : 167 - 171
  • [50] Long-term tricuspid valve function after Norwood operation
    Elmi, Maryam
    Hickey, Edward J.
    Williams, William G.
    Van Arsdell, Glen
    Caldarone, Christopher A.
    McCrindle, Brian W.
    JOURNAL OF THORACIC AND CARDIOVASCULAR SURGERY, 2011, 142 (06): : 1341 - U438
12345