Fabrication of YBCO films on SrTiO3 and textured Ag substrates by TFA-MOD method

被引：2

作者：

Liu, M. ^{[1
]}

Suo, H. L. ^{[1
]}

Zhao, Y. ^{[1
]}

Zhang, Y. X. ^{[1
]}

He, D. ^{[1
]}

Ma, L. ^{[1
]}

Zhou, M. L. ^{[1
]}

机构：

[1] Beijing Univ Technol, Coll Mat Sci & Engn, Beijing 100022, Peoples R China

来源：

IEEE TRANSACTIONS ON APPLIED SUPERCONDUCTIVITY | 2007年 / 17卷 / 02期

关键词：

coated conductor; textured Ag substrate; TFA-MOD; YBCO;

D O I：

10.1109/TASC.2007.898339

中图分类号：

TM [电工技术]; TN [电子技术、通信技术];

学科分类号：

0808 ; 0809 ;

摘要：

In this paper, we presented the result of YBCO films deposited epitaxially on both SrTiO3 single crystal and textured Ag substrates by a TFA-MOD method. The growing conditions and forming mechanisms of the YBCO films on these two kinds of substrates was investigated systematically. It was found that the precursor film coated on Ag substrate took less time to completely decompose to an amorphous precursor film during the first stage of the calcination than that on SrTiO3 substrate. Moreover, the higher temperature was needed to obtain pure YBCO phase on Ag substrate during the second annealing stage. A possible growing mechanism for this difference was described. A transport j, value of 1.5 x 10(4) A/cm(2) (at 77 K) was obtained for the YBCO film deposited on Ag substrate, while the film on SrTiO3 substrate exhibited an a T-c onset of 92 K and a high jc value of 2.3 MA/cm(2) at 77 K in self-field was measured.

引用

页码：3601 / 3604

页数：4

共 50 条

[31] Fabrication of YBCO film by TFA-MOD process at low-pressure atmosphere
Teranishi, R
Honjo, T
Tokunaga, Y
Fuji, H
Matsuda, J
Izumi, T
Yajima, A
Shiohara, Y
PHYSICA C-SUPERCONDUCTIVITY AND ITS APPLICATIONS, 2004, 412 : 920 - 925
[32] Enhanced Flux Pinning in YBCO plus YSZ Composite Films Grown by TFA-MOD Method
Ye, Shuai
Suo, Hongli
Liu, Min
Tang, Xiao
Wang, Rong
Wu, Ziping
Zhou, Meiling
IEEE TRANSACTIONS ON APPLIED SUPERCONDUCTIVITY, 2010, 20 (03) : 1573 - 1576
[33] Effects of precursor solution concentration on the properties and morphology of YBCO films deposited by TFA-MOD method
Cui, XM
Tao, BW
Li, YR
Liu, XZ
Chen, JJ
Xiong, J
RARE METALS, 2005, 24 (03) : 272 - 276
[34] JC properties and microstructures of YBCO films fabricated by low temperature calcination in TFA-MOD method
Teranishi, R.
Yoshida, J.
Mori, N.
Yamada, K.
Mukaida, M.
Kiss, T.
Inoue, M.
Matsuda, J.
Nakaoka, K.
Izumi, T.
Shiohara, Y.
PHYSICA C-SUPERCONDUCTIVITY AND ITS APPLICATIONS, 2009, 469 (15-20): : 1332 - 1335
[35] Optimization of oxygenation process in YBCO tapes fabricated by TFA-MOD method
Chikumoto, N
Machi, T
Tokunaga, Y
Izumi, T
Tajima, S
PHYSICA C-SUPERCONDUCTIVITY AND ITS APPLICATIONS, 2005, 426 : 1118 - 1121
[36] Precursor evolution and growth mechanism of BTO/YBCO films by TFA-MOD process
Wang Hong-Yan
Ding Fa-Zhu
Gu Hong-Wei
Zhang Teng
Peng Xing-Yu
CHINESE PHYSICS B, 2014, 23 (10)
[37] The Influence of Gas Flow Rate on the Growth of YBCO Films Prepared by TFA-MOD
Chen, Huan
Feng, Feng
Qu, Timing
Han, Zhenghe
IEEE TRANSACTIONS ON APPLIED SUPERCONDUCTIVITY, 2009, 19 (03) : 3123 - 3126
[38] Use of polymeric compounds to produce thick YBCO films by TFA-MOD process
Morlens, S.
Roma, N.
Ricart, S.
Moreto, J. M.
Puig, T.
Pomar, A.
Obradors, X.
7TH EUROPEAN CONFERENCE ON APPLIED SUPERCONDUCTIVITY (EUCAS'05), 2006, 43 : 182 - 186
[39] Optimization of the TFA-MOD Process for Introduction of BaZrO3 Pinning Centers in YBCO Films
Ghalsasi, Sameer
Majkic, Goran
Salama, Kamel
IEEE TRANSACTIONS ON APPLIED SUPERCONDUCTIVITY, 2011, 21 (03) : 3070 - 3074
[40] High speed production of YBCO precursor films by advanced TFA-MOD process
Ichikawa, H.
Nakaoka, K.
Miura, M.
Sutoh, Y.
Nakanishi, T.
Nakai, A.
Yoshizumi, M.
Izumi, T.
Shiohara, Y.
PHYSICA C-SUPERCONDUCTIVITY AND ITS APPLICATIONS, 2009, 469 (15-20): : 1329 - 1331

← 1 2 3 4 5 →