Fabrication of YBCO films on SrTiO3 and textured Ag substrates by TFA-MOD method

被引：2

作者：

Liu, M. ^{[1
]}

Suo, H. L. ^{[1
]}

Zhao, Y. ^{[1
]}

Zhang, Y. X. ^{[1
]}

He, D. ^{[1
]}

Ma, L. ^{[1
]}

Zhou, M. L. ^{[1
]}

机构：

[1] Beijing Univ Technol, Coll Mat Sci & Engn, Beijing 100022, Peoples R China

来源：

IEEE TRANSACTIONS ON APPLIED SUPERCONDUCTIVITY | 2007年 / 17卷 / 02期

关键词：

coated conductor; textured Ag substrate; TFA-MOD; YBCO;

D O I：

10.1109/TASC.2007.898339

中图分类号：

TM [电工技术]; TN [电子技术、通信技术];

学科分类号：

0808 ; 0809 ;

摘要：

In this paper, we presented the result of YBCO films deposited epitaxially on both SrTiO3 single crystal and textured Ag substrates by a TFA-MOD method. The growing conditions and forming mechanisms of the YBCO films on these two kinds of substrates was investigated systematically. It was found that the precursor film coated on Ag substrate took less time to completely decompose to an amorphous precursor film during the first stage of the calcination than that on SrTiO3 substrate. Moreover, the higher temperature was needed to obtain pure YBCO phase on Ag substrate during the second annealing stage. A possible growing mechanism for this difference was described. A transport j, value of 1.5 x 10(4) A/cm(2) (at 77 K) was obtained for the YBCO film deposited on Ag substrate, while the film on SrTiO3 substrate exhibited an a T-c onset of 92 K and a high jc value of 2.3 MA/cm(2) at 77 K in self-field was measured.

引用

页码：3601 / 3604

页数：4

共 50 条

[1] Fabrication of YBCO films on Ag substrate by TFA-MOD method
刘敏
董杰
刘丹敏
沈金龙
赵跃
周美玲
TransactionsofNonferrousMetalsSocietyofChina, 2004, (05) : 992 - 995
[2] Fabrication of YBCO films on Ag substrate by TFA-MOD method
Liu, M
Dong, J
Liu, DM
Shen, JL
Zhao, Y
Zhou, ML
TRANSACTIONS OF NONFERROUS METALS SOCIETY OF CHINA, 2004, 14 (05) : 992 - 995
[3] YBCO growth on textured NiW substrates by TFA-MOD method
Nakai, A.
Nakaoka, K.
Sutoh, Y.
Ichikawa, H.
Nakanishi, T.
Miura, M.
Yoshizumi, M.
Izumi, T.
Shiohara, Y.
Mimura, M.
PHYSICA C-SUPERCONDUCTIVITY AND ITS APPLICATIONS, 2008, 468 (15-20): : 1534 - 1536
[4] Microstructure of YBCO thin films prepared by TFA-MOD method
Nagino, I.
Matsumoto, K.
Adachi, H.
Miyata, S.
Yoshizumi, M.
Izumi, T.
Shiohara, Y.
PHYSICA C-SUPERCONDUCTIVITY AND ITS APPLICATIONS, 2010, 470 (20): : 1308 - 1312
[5] Fabrication of YBCO film approached by the '211 process' in the TFA-MOD method
Lim, JH
Jang, SH
Joo, J
Kim, H
Lee, HG
Hong, GW
Kim, CJ
SUPERCONDUCTOR SCIENCE & TECHNOLOGY, 2006, 19 (04): : 306 - 312
[6] Preparation of YBCO films on CeO2 buffered metallic substrates by the TFA-MOD method
Takahashi, Y
Araki, T
Yamagiwa, K
Yamada, Y
Kim, SB
Iijima, Y
Takeda, K
Hirabayashi, I
PHYSICA C-SUPERCONDUCTIVITY AND ITS APPLICATIONS, 2001, 357 : 1003 - 1006
[7] Fabrication of the YBCO films made by TFA-MOD using the 211-process
Lim, Jun Hyung
Jang, Seok Hern
Kim, Kyu Tae
Lee, Seung Yi
Lee, Chang Min
Hwang, Soo Min
Joo, Jinho
Jung, Seung-Boo
Nah, Wan-Soo
IEEE TRANSACTIONS ON APPLIED SUPERCONDUCTIVITY, 2007, 17 (02) : 3302 - 3305
[8] Ethanol-based TFA-MOD method for preparation of YBCO films
Wang, L.
Shi, D. Q.
Zhu, X. B.
Li, Q.
Yamashita, T.
Taylor, R.
Barry, J.
Dou, S. X.
PHYSICA C-SUPERCONDUCTIVITY AND ITS APPLICATIONS, 2010, 470 : S1016 - S1017
[9] Dependence of microstructures on growth rate in YBCO films by TFA-MOD method
Teranishi, R.
Mitani, A.
Yamada, K.
Mori, N.
Mukaida, M.
Miura, M.
Nakaoka, K.
Izumi, T.
Shiohara, Y.
PHYSICA C-SUPERCONDUCTIVITY AND ITS APPLICATIONS, 2009, 469 (15-20): : 1349 - 1352
[10] Growth process of BaZrO3 doped YBCO films by TFA-MOD method
Konya, K.
Masuda, Y.
Teranishi, R.
Kiss, T.
Munetoh, S.
Yamada, K.
Yoshizumi, M.
Izumi, T.
ADVANCES IN SUPERCONDUCTIVITY XXIV, 2012, 27 : 212 - 215

← 1 2 3 4 5 →