Effect of tensile dwell on high-temperature low-cycle fatigue and fracture behaviour of cast superalloy MAR-M247

被引：41
|
作者：
Sulak, Ivo [1 ]
Obrtlik, Karel [1 ]
机构：
[1] Acad Sci Czech Republ, Inst Phys Mat, Zizkova 22, Brno 61662, Czech Republic
来源：
ENGINEERING FRACTURE MECHANICS | 2017年 / 185卷
关键词：
Nickel-based superalloy; High-temperature low-cycle fatigue; Tensile dwell; Fatigue life; Damage mechanisms; DAMAGE MECHANISMS; CREEP-FATIGUE; DEGREES-C; ALLOY; 713LC; LIFE;
D O I：
10.1016/j.engfracmech.2017.04.002
中图分类号：
O3 [力学];
学科分类号：
08 ; 0801 ;
摘要：
Hot isostatically-pressed, nickel-based superalloy MAR-M247 was tested under fatigue and creep-fatigue conditions. Continuous cycling and cycling with 10 min tensile dwells in each cycle were applied in symmetrical strain control cycle with constant total strain amplitude at 900 degrees C in air. Cyclic hardening/softening curves, cyclic stress-strain curves and fatigue life curves were obtained. The introduction of tensile dwells resulted in lower fatigue life in total strain representation. Surface relief, specimen sections and fracture surface observations revealed crack initiation sites, crack density and crack paths, and help to clarify the effect of dwells on fatigue behaviour. (C) 2017 Elsevier Ltd. All rights reserved.
引用
收藏
页码：92 / 100
页数：9
相关论文
共 50 条
  • [31] Rapid extrapolation of high-temperature low-cycle fatigue curves for a nickel superalloy
    Viespoli L.M.
    Berto F.
    Material Design and Processing Communications, 2019, 1 (06):
  • [32] High-temperature low-cycle fatigue and fatigue-creep behaviour of Inconel 718 superalloy: Damage and deformation mechanisms
    Bartosak, Michal
    Horvath, Jakub
    Galikova, Marketa
    Slany, Michal
    Sulak, Ivo
    INTERNATIONAL JOURNAL OF FATIGUE, 2024, 186
  • [33] High Cycle Fatigue Damage Mechanisms of MAR-M 247 Superalloy at High Temperatures
    Smid, M.
    Hornik, V.
    Hutar, P.
    Hrbacek, K.
    Kunz, L.
    TRANSACTIONS OF THE INDIAN INSTITUTE OF METALS, 2016, 69 (02) : 393 - 397
  • [34] High Cycle Fatigue Damage Mechanisms of MAR-M 247 Superalloy at High Temperatures
    M. Šmíd
    V. Horník
    P. Hutař
    K. Hrbáček
    L. Kunz
    Transactions of the Indian Institute of Metals, 2016, 69 : 393 - 397
  • [35] High-temperature low-cycle fatigue behaviour of a cast Al-12Si-CuNiMg alloy
    Zhang, Qing
    Zuo, Zhengxing
    Liu, Jinxiang
    FATIGUE & FRACTURE OF ENGINEERING MATERIALS & STRUCTURES, 2013, 36 (07) : 623 - 630
  • [36] Numerical simulation and high cycle fatigue behaviour study on shot peening of MAR-M247 nickel-based alloy
    Jiang, Yunqing
    Liu, Meng
    Zou, Tongfei
    Wang, Quanyi
    Wu, Hao
    Pei, Yubing
    Zhang, Hong
    Liu, Yongjie
    Wang, Qingyuan
    INTERNATIONAL JOURNAL OF FATIGUE, 2024, 182
  • [37] HIGH-TEMPERATURE LOW-CYCLE FATIGUE OF AS-CAST MARM002
    BADDELEY, DT
    HANCOCK, P
    CIM BULLETIN, 1986, 79 (890): : 89 - 89
  • [38] HIGH-TEMPERATURE LOW-CYCLE FATIGUE BEHAVIOR OF A NIMONIC PE-16 SUPERALLOY CORRELATION WITH DEFORMATION AND FRACTURE
    VALSAN, M
    PARAMESWARAN, P
    RAO, KBS
    VIJAYALAKSHMI, M
    MANNAN, SL
    SHASTRY, DH
    METALLURGICAL TRANSACTIONS A-PHYSICAL METALLURGY AND MATERIALS SCIENCE, 1992, 23 (06): : 1751 - 1761
  • [39] Effect of tensile dwell on low cycle fatigue of cast superalloy Inconel 792-5A at 800°C
    Smid, Miroslav
    Obrtlik, Karel
    Petrenec, Martin
    Polak, Jaroslav
    ADVANCES IN FRACTURE AND DAMAGE MECHANICS X, 2012, 488-489 : 735 - 738
  • [40] Room-temperature low-cycle fatigue behaviour of cast and additively manufactured IN939 superalloy
    Babinsky, T.
    Sulak, I.
    Galikova, M.
    Kubena, I.
    Poloprudsky, J.
    Nahlik, L.
    MATERIALS SCIENCE AND ENGINEERING A-STRUCTURAL MATERIALS PROPERTIES MICROSTRUCTURE AND PROCESSING, 2025, 924
12345