Electrochemical Corrosion Behavior of AA7003

被引：0
|
作者：
Hua, T. S. [1 ]
Zhang, X. Y. [1 ]
Zheng, C. B. [2 ]
Song, R. G. [1 ]
机构：
[1] Changzhou Univ, Sch Mat Sci & Engn, Changzhou, Peoples R China
[2] Jiangsu Univ Sci & Technol, Sch Mat Sci & Engn, Zhenjiang, Peoples R China
来源：
MATERIALS PERFORMANCE | 2018年 / 57卷 / 12期
基金：
中国国家自然科学基金;
关键词：
MECHANICAL-PROPERTIES; CRACKING; EMBRITTLEMENT;
D O I：
暂无
中图分类号：
TB3 [工程材料学];
学科分类号：
0805 ; 080502 ;
摘要：
The electrochemical corrosion behavior of 7003 aluminum alloy (AA7003) under peak aging (PA), double peak aging (DPA), and regression re-aging (RRA) in sodium chloride (NaCl) solution at different temperatures have been studied by using potentiodynamic polarization and electrochemical impedance spectroscopy tests in combination with scanning electron microscopy. The results showed that the electrochemical corrosion rate of AA7003 in 3.5 wt% NaCl solution increases with increasing temperature, and the effect of aging treatments on the electrochemical corrosion rate in descending order is as follows: PA>DPA>RRA.
引用
收藏
页码：40 / 44
页数：5
相关论文
共 50 条
  • [41] Effects of applied potential on the stress corrosion cracking behavior of 7003 aluminum alloy in acid and alkaline chloride solutions
    Zhang, Xiao-yan
    Song, Ren-guo
    Sun, Bin
    Lu, Hai
    Wang, Chao
    INTERNATIONAL JOURNAL OF MINERALS METALLURGY AND MATERIALS, 2016, 23 (07) : 819 - 826
  • [42] Comparison of Electrochemical Noise Method with the Conventional Electrochemical Techniques for Investigation of the Pitting Corrosion on Al Alloys AA6061 and AA5052
    Shahidi, M.
    Tajabadipour, H.
    Hakemi, H. Ganjalikhan
    Gholamhosseinzadeh, M. R.
    INTERNATIONAL JOURNAL OF ELECTROCHEMICAL SCIENCE, 2013, 8 (10): : 11734 - 11751
  • [43] Effects of applied potential on the stress corrosion cracking behavior of 7003 aluminum alloy in acid and alkaline chloride solutions
    Xiao-yan Zhang
    Ren-guo Song
    Bin Sun
    Hai Lu
    Chao Wang
    InternationalJournalofMineralsMetallurgyandMaterials, 2016, 23 (07) : 819 - 826
  • [44] Electrochemical quartz crystal microbalance study of corrosion of phases in AA2024
    Baek, Y
    Frankel, GS
    JOURNAL OF THE ELECTROCHEMICAL SOCIETY, 2003, 150 (01) : B1 - B9
  • [45] ELECTROCHEMICAL TEST FOR PREDICTING MICROBIOLOGICALLY INFLUENCED CORROSION OF ALUMINUM AND AA 7005 ALLOY
    AYLLON, ES
    ROSALES, BM
    CORROSION, 1994, 50 (08) : 571 - 575
  • [46] Crack propagation behavior under low-cycle corrosion fatigue of A7003-T6 aluminum alloy
    Shiozawa, Kazuaki
    Asamoto, Tooru
    Miyao, Kazyu
    Nippon Kikai Gakkai Ronbunshu, A Hen/Transactions of the Japan Society of Mechanical Engineers, Part A, 1988, 54 (505): : 1745 - 1752
  • [47] Mechanical characteristics and corrosion behavior of friction stir AA5251-AA6063 butt welds
    Sudhakar, U.
    Srinivas, J.
    MATERIALS TODAY-PROCEEDINGS, 2019, 15 : 132 - 137
  • [48] Corrosion behavior of AA3003 friction stir welded joints
    Chekalil, I.
    Chadli, R.
    Ghazi, A.
    Miloudi, A.
    Planche, M. P.
    Amrouche, A.
    COLLOIDS AND SURFACES A-PHYSICOCHEMICAL AND ENGINEERING ASPECTS, 2024, 680
  • [49] A study on Corrosion Behavior of AA5083-MWCNT Reinforced Composite
    Nekilesh
    Boobathi, S.
    Jyothi, S.
    Kumar, P. S. Samuel Ratna
    Sudhagar, P. Edwin
    MATERIALS TODAY-PROCEEDINGS, 2020, 22 : 2725 - 2731
  • [50] Effect of Repair Welding on Electrochemical Corrosion and Stress Corrosion Cracking Behavior of TIG Welded AA2219 Aluminum Alloy in 3.5 Wt Pct NaCl Solution
    A. Venugopal
    K. Sreekumar
    V.S. Raja
    Metallurgical and Materials Transactions A, 2010, 41 : 3151 - 3160
12345