Electrochemical Corrosion Behavior of AA7003

被引：0
|
作者：
Hua, T. S. [1 ]
Zhang, X. Y. [1 ]
Zheng, C. B. [2 ]
Song, R. G. [1 ]
机构：
[1] Changzhou Univ, Sch Mat Sci & Engn, Changzhou, Peoples R China
[2] Jiangsu Univ Sci & Technol, Sch Mat Sci & Engn, Zhenjiang, Peoples R China
来源：
MATERIALS PERFORMANCE | 2018年 / 57卷 / 12期
基金：
中国国家自然科学基金;
关键词：
MECHANICAL-PROPERTIES; CRACKING; EMBRITTLEMENT;
D O I：
暂无
中图分类号：
TB3 [工程材料学];
学科分类号：
0805 ; 080502 ;
摘要：
The electrochemical corrosion behavior of 7003 aluminum alloy (AA7003) under peak aging (PA), double peak aging (DPA), and regression re-aging (RRA) in sodium chloride (NaCl) solution at different temperatures have been studied by using potentiodynamic polarization and electrochemical impedance spectroscopy tests in combination with scanning electron microscopy. The results showed that the electrochemical corrosion rate of AA7003 in 3.5 wt% NaCl solution increases with increasing temperature, and the effect of aging treatments on the electrochemical corrosion rate in descending order is as follows: PA>DPA>RRA.
引用
收藏
页码：40 / 44
页数：5
相关论文
共 50 条
  • [1] Effects of Aging Treatment on Intergranular Corrosion and Stress Corrosion Cracking Behavior of AA7003
    Xiaoyan Zhang
    Renguo Song
    Bin Sun
    Journal of Wuhan University of Technology-Mater. Sci. Ed., 2018, 33 : 1198 - 1204
  • [2] Exfoliation corrosion of artificially aged AA7003 extrusions
    Krishnan, C.
    Kish, J. R.
    CANADIAN METALLURGICAL QUARTERLY, 2014, 53 (04) : 455 - 459
  • [3] Effects of Aging Treatment on Intergranular Corrosion and Stress Corrosion Cracking Behavior of AA7003
    张晓燕
    宋仁国
    SUN Bin
    JournalofWuhanUniversityofTechnology(MaterialsScience), 2018, 33 (05) : 1198 - 1204
  • [4] Effects of Aging Treatment on Intergranular Corrosion and Stress Corrosion Cracking Behavior of AA7003
    Zhang Xiaoyan
    Song Renguo
    Sun Bin
    JOURNAL OF WUHAN UNIVERSITY OF TECHNOLOGY-MATERIALS SCIENCE EDITION, 2018, 33 (05): : 1198 - 1204
  • [5] Localized Corrosion and Stress Corrosion Cracking Behavior of AA7003 in a 3.5 wt% NaCl Aqueous Solution
    Xing Qi
    Bin Sun
    Xiaoming Chen
    Renguo Song
    Journal of Wuhan University of Technology-Mater. Sci. Ed., 2020, 35 : 986 - 995
  • [6] Localized Corrosion and Stress Corrosion Cracking Behavior of AA7003 in a 3.5 wt% NaCl Aqueous Solution
    祁星
    SUN Bin
    CHEN Xiaoming
    宋仁国
    Journal of Wuhan University of Technology(Materials Science), 2020, 35 (05) : 986 - 995
  • [7] Localized Corrosion and Stress Corrosion Cracking Behavior of AA7003 in a 3.5 wt% NaCl Aqueous Solution
    Qi, Xing
    Sun, Bin
    Chen, Xiaoming
    Song, Renguo
    JOURNAL OF WUHAN UNIVERSITY OF TECHNOLOGY-MATERIALS SCIENCE EDITION, 2020, 35 (05): : 986 - 995
  • [8] Hot Deformation Behavior of Alloy AA7003 with Different Zn/Mg Ratios
    Zheng, Xu
    Tang, Jianguo
    Wan, Li
    Zhao, Yan
    Jiao, Chuanrong
    Zhang, Yong
    METALS, 2022, 12 (09)
  • [9] Effects of cathodic polarization on SCC behavior of AA7003 under various aging treatments
    Qi Xing
    Sun Bin
    Zhang Xiao-yan
    Qi Wen-juan
    Wang Chao
    Song Ren-guo
    JOURNAL OF CENTRAL SOUTH UNIVERSITY, 2018, 25 (10) : 2299 - 2308
  • [10] Effect of recrystallization and texture on mechanical properties of extruded AA7003 alloyEinfluss von Rekristallisation und Textur auf die mechanischen Eigenschaften der Strangpresslegierung AA7003
    Du, X.
    You, J.
    Qu, Y.
    Wang, S.
    Zhou, N.
    MATERIALWISSENSCHAFT UND WERKSTOFFTECHNIK, 2019, 50 (07) : 829 - 836
12345