Controlling welding hot cracking based on electromagnetic force

被引：6
|
作者：
Xu, W. [1 ]
Fang, H. Y. [1 ]
Xu, D. [1 ]
Xu, W. L. [1 ]
Liu, X. S. [1 ]
Yang, J. G. [1 ]
机构：
[1] Harbin Inst Technol, State Key Lab Adv Welding Prod Technol, Harbin 150001, Peoples R China
来源：
SCIENCE AND TECHNOLOGY OF WELDING AND JOINING | 2007年 / 12卷 / 07期
关键词：
electromagnetic force; hot cracking; welding;
D O I：
10.1179/174329307X238407
中图分类号：
T [工业技术];
学科分类号：
08 ;
摘要：
Controlling welding hot cracking based on electromagnetic force was carried out. The results show that the welding cracking can be inhibited with this method, which lies on the voltage of capacitor and the frequency of applying force. The sheet bears the downward axial force and the less radial force of flat spiral coil. The radial force points at the centre of the sheet, so it is able to compress the weld metal. Moreover, the axial force also has the ability to compress the weld metal by means of the backing plate under weldment. Controlling welding hot cracking is mainly due to the improving of mechanical condition of weld metal within brittle temperature range.
引用
收藏
页码：659 / 663
页数：5
相关论文
共 50 条
  • [31] Hot cracking during laser welding of steel: Influence of the welding parameters and prevention of cracks
    Schaefer, Marcel
    Kessler, Steffen
    Scheible, Philipp
    Speker, Nicolai
    Harrer, Thomas
    HIGH-POWER LASER MATERIALS PROCESSING: APPLICATIONS, DIAGNOSTICS, AND SYSTEMS VI, 2017, 10097
  • [32] Controlling the Casimir force via the electromagnetic properties of materials
    Yang, Yaping
    Zeng, Ran
    Chen, Hong
    Zhu, Shiyao
    Zubairy, M. Suhail
    PHYSICAL REVIEW A, 2010, 81 (02):
  • [33] Hot cracking susceptibility of fillers 52 and 82 in alloy 690 welding
    Weite Wu
    C. H. Tsai
    Metallurgical and Materials Transactions A, 1999, 30 : 417 - 426
  • [34] Hot cracking susceptibility of fillers 52 and 82 in alloy 690 welding
    Wu, Weite
    Tsai, C.H.
    Metallurgical and Materials Transactions A: Physical Metallurgy and Materials Science, 1999, 30 A (02): : 417 - 426
  • [35] EFFECTS OF WELD WIDTH ON HOT CRACKING IN ELECTRON-BEAM WELDING
    MARKHNENKO, VI
    PIVTORAK, NI
    KOSHELEV, YV
    AUTOMATIC WELDING USSR, 1985, 38 (06): : 36 - 38
  • [36] EVALUATION OF THE RESISTANCE OF STEELS AND ALLOYS TO HOT CRACKING IN THE WELD ZONE IN WELDING
    TARNOVSKII, AI
    SHCHENKOV, AV
    FEKLISTOV, SI
    WELDING PRODUCTION, 1981, 28 (11): : 42 - 43
  • [37] EFFECTS OF MOLYBDENUM AND TUNGSTEN ON RESISTANCE OF WELDS TO HOT CRACKING DURING WELDING
    LEINACHU.EI
    PODGAETS.VV
    PARFESSA, GI
    AUTOMATIC WELDING USSR, 1973, 26 (11): : 10 - 15
  • [38] Reduction of hot cracking susceptibility during laser welding of aluminum by vibrations
    Radel, Tim
    Woizeschke, Peer
    WELDING IN THE WORLD, 2019, 63 (03) : 599 - 606
  • [39] Effect of metallurgical treatment of steels on their susceptibility to hot cracking during welding
    Killing, Robert
    Rawlings, Gerald
    Schweissen und Schneiden/Welding and Cutting, 1989, (07):
  • [40] A QUANTITATIVE DETERMINATION OF CONDITIONS FOR HOT CRACKING DURING WELDING FOR ALUMINUM ALLOYS
    STEENBERGEN, JE
    THORNTON, HR
    WELDING JOURNAL, 1970, 49 (02) : S61 - +
12345