Zirconium phase transformations observed by "in-situ" XRD analysis

被引：4
|
作者：
Riha, Jan [1 ]
Sutta, Pavol [1 ]
Vincze, Andrej [2 ]
Medlin, Rostislav [1 ]
机构：
[1] Univ W Bohemia, New Technol Res Ctr, Plzen 30614, Czech Republic
[2] Ctr Int Laser, Bratislava 84104, Slovakia
来源：
VACUUM | 2012年 / 86卷 / 06期
关键词：
Zirconium; In-situ XRD analysis; Phase transformation;
D O I：
10.1016/j.vacuum.2011.07.009
中图分类号：
T [工业技术];
学科分类号：
08 ;
摘要：
The high temperature phase transformations of zirconium were investigated by "in-situ" X-ray diffraction analysis. The experiments were carried out in a high temperature chamber Anton Paar HTK 1200N mounted on powder diffractometer Panalytical X'Pert Pro. The chamber was evacuated by a turbo-molecular pump creating a pressure about 3 x 10(-4) Pa at the temperature 1200 degrees C before the measurement. The experimental samples were uniformly heated without thermal gradients up to 1000 degrees C or 1200 degrees C and then exposed for 180 min. At high temperature four or six diffraction patterns of each sample were recorded for the illustration of the phase changes in the material structure. Chemical composition of some samples after the exposure was determined by secondary ion mass spectrometry and compared with composition of the material in its initial state. (C) 2011 Elsevier Ltd. All rights reserved.
引用
收藏
页码：785 / 788
页数：4
相关论文
共 50 条
  • [41] Application of in-situ diffraction experiments to understand nonequilibrium phase transformations in structural alloys
    Babu, S. S.
    Elmer, J. W.
    Specht, E. D.
    Vitek, J. M.
    David, S. A.
    SOLID-SOLID PHASE TRANSFORMATIONS IN INORGANIC MATERIAL 2005, VOL 2, 2005, : 475 - 492
  • [42] In-situ phase mapping and direct observations of phase transformations during arc welding of 1045 steel
    Elmer, J. W.
    Palmer, T. A.
    METALLURGICAL AND MATERIALS TRANSACTIONS A-PHYSICAL METALLURGY AND MATERIALS SCIENCE, 2006, 37A (07): : 2171 - 2182
  • [43] In-situ study of phase transformations during homogenization of 6060 and 6063 Al alloys
    Bayat, N.
    Carlberg, T.
    Cieslar, M.
    JOURNAL OF PHYSICS AND CHEMISTRY OF SOLIDS, 2019, 130 : 165 - 171
  • [44] Quantitative analysis of C-S-H in hydrating alite pastes by in-situ XRD
    Bergold, S. T.
    Goetz-Neunhoeffer, F.
    Neubauer, J.
    CEMENT AND CONCRETE RESEARCH, 2013, 53 : 119 - 126
  • [45] In-situ neutron diffraction studies of phase transformations in Si-MnTRIP steel
    Muránsky, O
    Lukas, P
    Sittner, P
    Zrník, J
    Jencus, P
    Novy, Z
    RESIDUAL STRESSES VII, PROCEEDINGS, 2005, 490-491 : 275 - 280
  • [46] Application of in-situ electrical resistance measurements to the study of phase transformations in ferrous alloys
    Kirbis, Peter
    Anzel, Ivan
    Bruncko, Mihael
    PHYSICS OF METALS AND METALLOGRAPHY, 2016, 117 (11): : 1092 - 1100
  • [47] In-situ phase mapping and direct observations of phase transformations during arc welding of 1045 steel
    J. W. Elmer
    T. A. Palmer
    Metallurgical and Materials Transactions A, 2006, 37 : 2171 - 2182
  • [48] Stress-induced phase transformations studied by in-situ transmission electron microscopy
    No, M. L.
    Ibarra, A.
    Caillard, D.
    San Juan, J.
    15TH INTERNATIONAL CONFERENCE ON THE STRENGTH OF MATERIALS (ICSMA-15), 2010, 240
  • [49] In-situ study of phase transformations during homogenization of 6005 and 6082 Al alloys
    Bayat, N.
    Carlberg, T.
    Cieslar, M.
    JOURNAL OF ALLOYS AND COMPOUNDS, 2017, 725 : 504 - 509
  • [50] TG/DTG-DSC and high temperature in-situ XRD analysis of natural thaumasite
    Kostova, B.
    Petkova, V
    Kostov-Kytin, Vl
    Tzvetanova, Y.
    Avdeev, G.
    THERMOCHIMICA ACTA, 2021, 697
12345