New ferroelectric BaTi2O5

被引：108
|
作者：
Akishige, Y [1 ]
Fukano, K [1 ]
Shigematsu, H [1 ]
机构：
[1] Shimane Univ, Fac Educ, Matsue, Shimane 6908504, Japan
来源：
JAPANESE JOURNAL OF APPLIED PHYSICS PART 2-LETTERS & EXPRESS LETTERS | 2003年 / 42卷 / 8A期
关键词：
BaTi2O5; high Curie temperature; high dielectric constant; ferroelectrics; D-E loop; space group;
D O I：
10.1143/JJAP.42.L946
中图分类号：
O59 [应用物理学];
学科分类号：
摘要：
A needle-shaped BaTi2O5 crystal was grown from a Ti-rich solution. The chemical composition of the crystal was analyzed by an electron probe micro-analyzer (EPMA). X-ray Weissenberg photographs were taken at room temperature (RT): the crystal is monoclinic with a = 16.91 Angstrom, b = 3.94 Angstrom, c = 9.49 Angstrom, beta = 103.0degrees and Z = 6. A broad and large dielectric anomaly reaching 30,000 was observed at 430degreesC for the dielectric constant along the b-axis. Also, spontaneous polarization was estimated to be approximately 7 muC/cm(2) from the D-E loops at RT. Thus the crystal is a new ferroelectric substance with a high Curie temperature of 430degreesC and the space group C-2 at RT.
引用
收藏
页码：L946 / L948
页数：3
相关论文
共 50 条
  • [21] Frequency-dependent electrical properties of ferroelectric BaTi2O5 single crystal
    Maso, Nahum
    Yue, XinYan
    Goto, Takashi
    West, Anthony R.
    JOURNAL OF APPLIED PHYSICS, 2011, 109 (02)
  • [22] Synthesis of ferroelectric BaTi2O5 nanoparticles via modifying peroxopolytitanic acid solution
    Yamada, Katsumi
    Miyazaki, Hidetoshi
    Tsukada, Shinya
    CERAMICS INTERNATIONAL, 2020, 46 (14) : 23232 - 23235
  • [23] Preparation of polycrystalline BaTi2O5 by pressureless sintering
    Li, Guo-jun
    Tu, Rong
    Goto, Takashi
    MATERIALS RESEARCH BULLETIN, 2009, 44 (02) : 468 - 471
  • [24] Order-disorder nature of ferroelectric BaTi2O5 -: art. no. 112903
    Hushur, A
    Shigematsu, H
    Akishige, Y
    Kojima, S
    APPLIED PHYSICS LETTERS, 2005, 86 (11) : 1 - 3
  • [25] Sol-gel synthesis of BaTi2O5
    Xu, YB
    Huang, GH
    Long, H
    MATERIALS LETTERS, 2003, 57 (22-23) : 3570 - 3573
  • [26] Successive crystallization of ferroelectric-based BaTi2O5 bulk glass studied by Raman scattering
    Taniguchi, Hiroki
    Yu, Jianding
    Arai, Yasutomo
    Fu, Desheng
    Yagi, Toshirou
    Itoh, Mitsuru
    MATERIALS SCIENCE AND ENGINEERING B-ADVANCED FUNCTIONAL SOLID-STATE MATERIALS, 2008, 148 (1-3): : 48 - 52
  • [27] Dielectric and ferroelectric properties of BaTi2O5 thin films prepared by sol-gel method
    Guo, Dongyun
    Gong, Yiping
    Wang, Chuanbin
    Shen, Qiang
    Zhang, Lianmeng
    MATERIALS LETTERS, 2013, 95 : 55 - 58
  • [28] Phase change in calcination process for BaTi2O5 and proposal of a new temperature profile
    Tashiro, Shinjiro
    Ishii, Keisuke
    ADVANCED POWDER TECHNOLOGY, 2014, 25 (02) : 761 - 766
  • [29] Anomalous permittivity during crystallization of BaTi2O5 glass
    Yu, Jinding
    Arai, Yasutomo
    FERROELECTRICS, 2006, 333 : 221 - 226
  • [30] Sol–gel synthesis and characterization of BaTi2O5 powders
    S. Tangjuank
    T. Tunkasiri
    Applied Physics A, 2005, 81 : 1105 - 1107
12345