Screen printed Tl-1223 superconducting thick films

被引：5

作者：

Heiml, O ^{[1
]}

König, WT ^{[1
]}

Gritzner, G ^{[1
]}

机构：

[1] Johannes Kepler Univ, Inst Chem Technol Organ Stoffe, A-4040 Linz, Austria

来源：

PHYSICA C | 2000年 / 341卷

关键词：

D O I：

10.1016/S0921-4534(00)01281-8

中图分类号：

O59 [应用物理学];

学科分类号：

摘要：

Highly oriented bismuth- and lead-codoped Tl-1223 superconducting, 5 - 10 mum thick films of the composition (Tl0.6Bi0.16Pb0.24)(Ba0.1ST0.9)(2)Ca2Cu3Oy were prepared on polycrystalline ZrO2 substrates by screen printing. The influence of the mesh opening and the heat treatment on the properties of the superconducting film was investigated. Sintering was performed by a two step process with an intermediate uni-axial compaction step to enhance both texturing and density. T-c(0)-values of 118 K with narrow transition widths around 1 K were observed. X-ray diffraction proved the high phase purity of the material. The degree of texturing was calculated from the intensities of the respective XRD peaks. Transport critical current densities in the range of 10 kA cm(-2) at 77 K were obtained.

引用

页码：2397 / 2398

页数：2

共 50 条

[21] Irreversibility line of Tl-1223/Ag sheathed superconducting composite tape
Tang, H
Wang, YZ
Yang, ZQ
Zhang, C
Hua, L
deBoer, FR
Qiao, GW
Zhou, SH
Peng, HT
PHYSICA C, 1997, 282 : 2111 - 2112
[22] Irreversibility line of Tl-1223/Ag sheathed superconducting composite tape
Tang, H.
Wang, Y.Z.
Yang, Z.Q.
Zhang, C.
Hua, L.
de Boer, F.R.
Qiao, G.W.
Zhou, S.H.
Peng, H.T.
Physica C: Superconductivity and its Applications, 1997, 282-287 (pt 4): : 2111 - 2112
[23] Transmission electron microscopy of Tl-1223 films on lanthanum aluminate
Przybylski, K
Heiml, O
Gritzner, G
PHYSICA C-SUPERCONDUCTIVITY AND ITS APPLICATIONS, 2005, 423 (1-2): : 63 - 68
[24] A new process to prepare thick bufferless Tl-1223/Ag high temperature superconducting coated conductors using electrodeposition
Jeong, D. Y.
Kim, Y. H.
Shirage, P. M.
Kim, S. Y.
Horiuchi, S.
Lee, J. H.
SUPERCONDUCTOR SCIENCE & TECHNOLOGY, 2007, 20 (12): : 1239 - 1252
[25] Magnetoconductivity of polycrystalline Hg,Tl-1223
Axnäs, J
Bryntse, I
Safonova, I
Rapp, Ö
PHYSICA B, 2000, 284 : 1009 - 1010
[26] THE PROCESSING, PROPERTIES, AND PROSPECTS OF TL-1223
TKACZYK, JE
JOM-JOURNAL OF THE MINERALS METALS & MATERIALS SOCIETY, 1994, 46 (12): : 26 - 27
[27] Future Circular Collider beam screen: progress on Tl-1223 HTS coating
Leveratto, A.
Saba, A.
Holleis, S.
Himmerlich, M.
Henrist, B.
Fernandez-Pena, S.
Moros, A.
Bernardi, J.
Eisterer, M.
Bernini, C.
Vaglio, R.
Putti, M.
Ferdeghini, C.
Calatroni, S.
Bellingeri, E.
SUPERCONDUCTOR SCIENCE & TECHNOLOGY, 2020, 33 (05):
[28] Fabrication of biaxially textured Ni substrates and LaNiO3 buffer layers for Tl-1223 thick films
Gladstone, TA
Moore, JC
Wilkinson, AJ
Grovenor, CRM
IEEE TRANSACTIONS ON APPLIED SUPERCONDUCTIVITY, 1999, 9 (02) : 2252 - 2255
[29] The influence of zinc on Tl-1223 superconductors
Kühberger, M
Gritzner, G
PHYSICA C-SUPERCONDUCTIVITY AND ITS APPLICATIONS, 2003, 390 (03): : 263 - 269
[30] Effect of pressure on the electrical resistivity of a 116 K Tl-1223 superconducting ceramic
Triscone, G
Gladyshevskii, RE
Han, SH
Herrmann, J
Maple, MB
PHYSICA C, 1996, 272 (1-2): : 21 - 25

← 1 2 3 4 5 →