Structural and adhesion properties of poly(ethyl 2-cyanoacrylate) post-cured at different temperatures and times

被引：4
|
作者：
Estan-Cerezo, Gabriel [1 ,2 ,3 ]
Alonso, Diego A. [2 ,3 ]
Miguel Martin-Martinez, Jose [1 ]
机构：
[1] Univ Alicante, Adhes & Adhes Lab, E-03080 Alicante, Spain
[2] Univ Alicante, Organ Chem Dept, Alicante, Spain
[3] Univ Alicante, Inst Organ Synth, Alicante, Spain
来源：
JOURNAL OF ADHESION SCIENCE AND TECHNOLOGY | 2019年 / 33卷 / 04期
关键词：
Poly(ethylcyanoacrylate); thermal post-cure; adhesion; unzipping mechanism; DSC; TGA; CYANOACRYLATE; POLYMERIZATION; DEGRADATION; ETHYL;
D O I：
10.1080/01694243.2018.1509502
中图分类号：
TQ [化学工业];
学科分类号：
0817 ;
摘要：
The structure and properties of poly(ethyl 2-cyanoacrylate)s (pECNs) cured at 25 degrees C during 24hours, and post-cured at different temperatures (45-90 degrees C) and times (2-6hours) were studied. Irrespective of the post-cure conditions, pECN was not fully polymerized and two different structures of different molecular weights and topographies were obtained. The post-cure decreased the shear strength values in joints made with aluminum and ethyl cyanoacrylate due to the decrease in the percentage of higher molecular weight polymeric chains and the formation of new short polymeric chains by unzipping de-polymerization mechanism, both contributed to decrease the mechanical properties. On the other hand, the post-cure changed the morphology of pECN because of nano-spheres were produced by curing at 25 degrees C which were not present after post-cure at 90 degrees C.
引用
收藏
页码：329 / 345
页数：17
相关论文
共 50 条
  • [1] Mechanical and viscoelastic properties of SiO2/epoxy nanocomposites post-cured at different temperatures
    Singh, Sushil Kumar
    Kumar, Abhishek
    Jain, Anuj
    PLASTICS RUBBER AND COMPOSITES, 2021, 50 (03) : 116 - 126
  • [2] Influence of initiators on the growth of poly(ethyl 2-cyanoacrylate) nanofibers
    Mankidy, Pratik J.
    Rajagopalan, Ramakrishnan
    Foley, Henry C.
    POLYMER, 2008, 49 (09) : 2235 - 2242
  • [3] Phase separation and morphology of PDLC based on poly(ethyl 2-cyanoacrylate)
    Borgini, T
    Carpaneto, L
    Costa, G
    Stagnaro, P
    Valenti, B
    MOLECULAR CRYSTALS AND LIQUID CRYSTALS SCIENCE AND TECHNOLOGY SECTION A-MOLECULAR CRYSTALS AND LIQUID CRYSTALS, 1999, 336 : 199 - 210
  • [4] Phase separation and morphology of PDLC based on poly(ethyl 2-cyanoacrylate)
    Dipartimente Chim. Chim. Industriale, Via Dodecaneso 31, 16146 Genova, Italy
    不详
    Mol Cryst Liq Cryst Sci Technol Sect A Mol Crys Liq Cryst, (199-210):
  • [5] ADHESIVE PROPERTIES OF ETHYL 2-CYANOACRYLATE CONTAINING SMALL AMOUNTS OF ACETIC ACID AS ADHESION PROMOTER.
    Kotzev, D.L.
    Denchev, Z.Z.
    Kabaivanov, V.S.
    International Journal of Adhesion and Adhesives, 1987, 7 (02): : 93 - 96
  • [6] ADHESIVE PROPERTIES OF ETHYL 2-CYANOACRYLATE CONTAINING SMALL AMOUNTS OF ACETIC-ACID AS ADHESION PROMOTER
    KOTZEV, DL
    DENCHEV, ZZ
    KABAIVANOV, VS
    INTERNATIONAL JOURNAL OF ADHESION AND ADHESIVES, 1987, 7 (02) : 93 - 96
  • [7] Poly(vinylidene fluoride) and Poly(ethyl 2-cyanoacrylate) Blends through Controlled Polymerization of Ethyl 2-Cyanoacrylates
    Tiwari, Manish K.
    Bayer, Ilker S.
    Jursich, Gregory M.
    Schutzius, Thomas M.
    Megaridis, Constantine M.
    MACROMOLECULAR MATERIALS AND ENGINEERING, 2009, 294 (11) : 775 - 780
  • [8] POLYMERIZATION OF ETHYL 2-CYANOACRYLATE IN THE PRESENCE OF POLY(BUTADIENE-CO-ACRYLONITRILE)
    DIKOV, VK
    KOTZEV, DL
    KABAIVANOV, VS
    BRITISH POLYMER JOURNAL, 1988, 20 (01): : 9 - 12
  • [9] THE EFFECT OF HEAT ON THE MOLECULAR-WEIGHT OF POLY(ETHYL 2-CYANOACRYLATE) ADHESIVE
    GUTHRIE, J
    OTTERBURN, MS
    ROONEY, JM
    TSANG, CN
    JOURNAL OF APPLIED POLYMER SCIENCE, 1985, 30 (07) : 2863 - 2867
  • [10] Synthesis and modification of poly(ethyl 2-cyanoacrylate) film on silicon wafer.
    Lu, ZX
    McCarthy, TJ
    ABSTRACTS OF PAPERS OF THE AMERICAN CHEMICAL SOCIETY, 2004, 227 : U379 - U379
12345