The effects of copper (Cu) or zinc (Zn) on fluidity of A357 alloy

被引：5
|
作者：
Mao, Guoling [1 ]
Liu, Dongyang [1 ]
Gao, Wenli [1 ]
Liu, Shanguang [2 ]
Zhong, Liwei [2 ]
机构：
[1] Hunan Univ, Coll Mat Sci & Engn, Changsha 410082, Peoples R China
[2] Beijing Inst Aeronaut Mat, Beijing 100097, Peoples R China
来源：
MATERIALS LETTERS | 2021年 / 304卷
关键词：
A357; alloy; Fluidity; Cu; Zn; Metals and alloys; Thermal analysis; AL; SC;
D O I：
10.1016/j.matlet.2021.130733
中图分类号：
T [工业技术];
学科分类号：
08 ;
摘要：
Excellent fluidity is an essential condition for Al-Si-Mg alloy (like A357) to make large thin-walled and complex structure castings, but there is no research about the effects of Cu or Zn on the fluidity of Al-Si-Mg alloys. Under sand casting conditions, the effects of Cu or Zn on the fluidity of A357 were investigated through spiral fluidity resin sand molds, DSC, polarizing microscope and SEM. The results showed that with increase of Cu or Zn content, the solidification temperature range (T) of A357 alloy increased, and the fluidity decreased. With Cu or Zn addition, the grain size of A357 alloy increased, but the coarse grain is not the main reason for the fluidity to deteriorate.
引用
收藏
页数：3
相关论文
共 50 条
  • [1] The fluidity of A357 alloy with scandium (Sc) and zirconium (Zr) addition
    Mao, Guoling
    Wu, Zhigang
    Liu, Shanguang
    Zhong, Liwei
    Gao, Wenli
    JOURNAL OF MATERIALS RESEARCH AND TECHNOLOGY-JMR&T, 2020, 9 (06): : 13570 - 13574
  • [2] Effects of Solidification Parameters on SDAS of A357 Alloy
    He Juan
    Zeng Jian-Min
    Yan Along
    ENGINEERING MATERIALS III, 2008, 51 : 85 - +
  • [3] Thixoextrusion of A357 aluminium alloy
    A.FORN
    G.VANEETVELD
    J.C.PIERRET
    S.MENARGUES
    M.T.BAILE
    M.CAMPILLO
    A.RASSILI
    Transactions of Nonferrous Metals Society of China, 2010, 20(S3) (S3) : 1005 - 1009
  • [4] Thixoextrusion of A357 aluminium alloy
    Forn, A.
    Vaneetveld, G.
    Pierret, J. C.
    Menargues, S.
    Baile, M. T.
    Campillo, M.
    Rassili, A.
    TRANSACTIONS OF NONFERROUS METALS SOCIETY OF CHINA, 2010, 20 : S1005 - S1009
  • [5] Effects of Melt Treatment on Dendrite Coherency of A357 Alloy
    Chen, Zhongwei
    Chen, Pei
    Fan, Li
    MANUFACTURING PROCESS TECHNOLOGY, PTS 1-5, 2011, 189-193 : 3886 - 3890
  • [6] An Investigation on the Overheating of A357 Aluminum Alloy
    Pan, Jiehua
    Zou, Yongzhi
    Lin, Yi
    Zeng, Jianmin
    MANUFACTURING SCIENCE AND ENGINEERING, PTS 1-5, 2010, 97-101 : 1049 - +
  • [7] Effects of Secondary Dendrite Arm Spacing on Microporosity of A357 Alloy
    Zou, Yongzhi
    Xu, Zhengbing
    Zeng, Jianmin
    MANUFACTURING SCIENCE AND ENGINEERING, PTS 1-5, 2010, 97-101 : 781 - 784
  • [8] A357 Alloy by LPBF for Industry Applications
    Lorusso, Massimo
    Trevisan, Francesco
    Calignano, Flaviana
    Lombardi, Mariangela
    Manfredi, Diego
    MATERIALS, 2020, 13 (07)
  • [9] Modification effects of lanthanum-rich mischmetal on A357 alloy
    Li, HJ
    Liu, CM
    Li, GS
    Xue, HS
    JOURNAL OF RARE EARTHS, 2001, 19 (01) : 49 - 52
  • [10] Effects of sample thickness on microstructures and mechanical properties of A357 alloy
    Xiong, B. W.
    Yu, H.
    Yan, Q. S.
    Zhao, J. Q.
    Chen, S. N.
    Yang, Z.
    INTERNATIONAL JOURNAL OF CAST METALS RESEARCH, 2012, 25 (06) : 374 - 378
12345