Unveiling the influential mechanism of O2 on the corrosion of N80 carbon steel under dynamic supercritical CO2 conditions

被引：7
|
作者：
Li, Y. Y. [1 ]
Jiang, Z. N. [1 ]
Zhang, Q. H. [1 ]
Lei, Y. [1 ]
Wang, X. [1 ]
Zhang, G. A. [1 ]
机构：
[1] Huazhong Univ Sci & Technol, Sch Chem & Chem Engn, Hubei Key Lab Mat Chem & Serv Failure, Key Lab Mat Chem Energy Convers & Storage,Minist, Wuhan 430074, Peoples R China
来源：
CORROSION SCIENCE | 2022年 / 205卷
基金：
中国国家自然科学基金;
关键词：
Supercritical CO2-O-2; Waterchemistrymodel; Steelcorrosion; Electrochemicalmeasurements; Diffusionbarriereffect; LOW-TEMPERATURE OXIDATION; PRESSURE AIR INJECTION; GEOLOGICAL SEQUESTRATION; MUTUAL SOLUBILITIES; CO2-H2O MIXTURES; AQUEOUS NACL; STORAGE CCS; WATER; BEHAVIOR; CAPTURE;
D O I：
10.1016/j.corsci.2022.110436
中图分类号：
T [工业技术];
学科分类号：
08 ;
摘要：
The influential mechanism of O-2 on the corrosion of N80 carbon steel under dynamic supercritical CO2 conditions was explored by mass loss and electrochemical tests, and surface analysis. It is demonstrated that the introduction of O-2 inhibits the corrosion of steel. The developed water chemistry model confirms that the decrease in the corrosive species concentration by introducing O-2 is not responsible for the inhibition to steel corrosion. The corrosion inhibition of O-2 is implemented by promoting the formation of protective FeCO3 film in the initial period owing to the diffusion barrier effect of the formed outer ferric hydroxide/oxide film.
引用
收藏
页数：20
相关论文
共 50 条
  • [31] Understanding the Influence of SO2 and O2 on the Corrosion of Carbon Steel in Water-Saturated Supercritical CO2
    Hua, Yong
    Barker, Richard
    Neville, Anne
    CORROSION, 2015, 71 (05) : 667 - 683
  • [32] Novel Сarbon Dots for Corrosion Inhibition of N80 Carbon Steel in 3% Saturated CO2 Saline Solution
    Xiaodan Wu
    Jianbo Li
    Jie Lv
    Chaoyi Deng
    Lan Yang
    Russian Journal of Applied Chemistry, 2021, 94 : 1111 - 1121
  • [33] Influence of H2S Content on CO2 Corrosion Behaviors of N80 Tubing Steel
    Jingen, D.
    Wei, Y.
    Xiaorong, L.
    Xiaoqin, D.
    PETROLEUM SCIENCE AND TECHNOLOGY, 2011, 29 (13) : 1387 - 1396
  • [34] The Influence of O2 on the Corrosion Behavior of the X80 Steel in CO2 Environment
    Wang, Xiao
    Wang, Xinyue
    Wang, Jun
    Wang, Guowei
    Pan, Yi
    Yan, Shuangchun
    INTERNATIONAL JOURNAL OF ELECTROCHEMICAL SCIENCE, 2020, 15 (01): : 889 - 898
  • [35] Influence of corrosion products on the inhibition effect of pyrimidine derivative for the corrosion of carbon steel under supercritical CO2 conditions
    Hou, B. S.
    Zhang, Q. H.
    Li, Y. Y.
    Zhu, G. Y.
    Zhang, G. A.
    CORROSION SCIENCE, 2020, 166
  • [36] Electrochemical behaviour of N80 steel in CO2 environment at high temperature and pressure conditions
    Ren, Xiedong
    Wang, Hu
    Wei, Qiang
    Lu, Yuan
    Xiao, Bowen
    Xie, Juan
    CORROSION SCIENCE, 2021, 189
  • [37] Corrosion Behavior of Austenitic Stainless Steel in Supercritical CO2 containing O2 and H2O
    Teeter, L.
    Huerta, N.
    Dogan, O.
    Ziomek-Moroz, M.
    Oleksak, R.
    Oryshchyn, D.
    Disenhof, C.
    Baltrus, J.
    Tucker, J.
    CORROSION GENERAL SESSION, 2016, 72 (17): : 137 - 148
  • [38] Inhibiting Steel Corrosion in Aqueous Supercritical CO2 Conditions
    Zhang, Yucheng
    Gao, Kewei
    Schmitt, Guenter
    MATERIALS PERFORMANCE, 2011, 50 (09) : 54 - 59
  • [39] Influence of CO2 partial pressure on the protection property of corrosion scale formed on N80 steel
    Chen, Dong
    Liu, Wei
    Lu, Minxu
    Wu, Yinshun
    Hou, Shiying
    Chen, Yingfeng
    Beijing Keji Daxue Xuebao/Journal of University of Science and Technology Beijing, 2007, 29 (03): : 288 - 292
  • [40] CORROSION MECHANISM OF OCTG CARBON STEEL IN SUPERCRITICAL CO2/OIL/WATER SYSTEM
    Sun Chong
    Sun Jianbo
    Wang Yong
    Wang Shijie
    Liu Jianzin
    ACTA METALLURGICA SINICA, 2014, 50 (07) : 811 - 820
12345