Rapid solidification behavior of Fe-Cr-Mn-Mo-Si-C alloys

被引：3
|
作者：
Ranganathan, Sathees [1 ]
Makaya, Advenit [1 ]
Fredriksson, Hasse [1 ]
Savage, Steven [1 ]
机构：
[1] Royal Inst Technol, SE-10044 Stockholm, Sweden
来源：
METALLURGICAL AND MATERIALS TRANSACTIONS B-PROCESS METALLURGY AND MATERIALS PROCESSING SCIENCE | 2007年 / 38卷 / 06期
关键词：
D O I：
10.1007/s11663-007-9108-4
中图分类号：
T [工业技术];
学科分类号：
08 ;
摘要：
The rapid solidification behavior of alloys in the Fe-Cr-Mn-Mo-Si-C system was investigated for different compositions and cooling rates. The C content was varied and alloying additions of Mo and B were studied with respect to their effect on the microstructure. The alloys were cast as either melt-spun ribbons or as 1-mm-thick plates after levitation or as rods 2 to 4 mm in diameter by injection into copper molds. A homogeneous single-phase structure was obtained for the alloy of composition 72.8Fe-8Cr-6Mn-5Si-5Mo-3.2C (wt pct), for a sample diameter of 2.85 mm, at a cooling rate of approximate to 1100 K/s. The single-phase structure was identified as a metastable solid solution, exhibiting the characteristics of the e phase. Upon reheating, decomposition of the single-phase structure into fine bainite plates and secondary carbides was observed between 600 degrees C and 700 degrees C. The annealed structure obtained showed high hardness values (> 850 HV).
引用
收藏
页码：917 / 926
页数：10
相关论文
共 50 条
  • [31] Effect of Titanium on the Structure and Properties of Clad Metal from Powder Wires of Fe - C - Si - Mn - Cr - W- V and Fe - C - Si - Mn - Cr - Mo - Ni Systems
    Kibko, N., V
    Usol'tsev, A. A.
    Mikhno, A. R.
    Sychev, A. A.
    METAL SCIENCE AND HEAT TREATMENT, 2022, 64 (5-6) : 281 - 284
  • [32] Plasma nitriding and nitrocarburising of sintered Fe-Cr-Mo and Fe-Cr-Mo-C alloys
    Molinari, A
    Tesi, B
    Bacci, T
    Marcu, T
    SURFACE & COATINGS TECHNOLOGY, 2001, 140 (03): : 251 - 255
  • [33] CORROSION RESISTANCE, ROUGHNESS AND STRUCTURE OF Co64Cr28Mo5(Fe, Si, AI, Be)3 AND Co63Cr29Mo6.5(C, Si, Fe, Mn)1.5 BIOMEDICAL ALLOYS
    Klimecka-Tatar, D.
    Radomska, K.
    Pawlowska, G.
    Journal of the Balkan Tribological Association, 2015, 21 (01): : 204 - 210
  • [34] BORIDES IN MICROCRYSTALLINE FE-CR-MO-B-SI ALLOYS
    LIN, YJ
    HU, J
    JOURNAL OF MATERIALS SCIENCE, 1991, 26 (10) : 2833 - 2840
  • [35] Effect of Manganese on Microstructures and Solidification Modes of Cast Fe-Mn-Si-Cr-Ni Shape Memory Alloys
    Huabei Peng
    Yuhua Wen
    Yangyang Du
    Qinxu Yu
    Qin Yang
    Metallurgical and Materials Transactions B, 2013, 44 : 1137 - 1143
  • [36] Effect of Manganese on Microstructures and Solidification Modes of Cast Fe-Mn-Si-Cr-Ni Shape Memory Alloys
    Peng, Huabei
    Wen, Yuhua
    Du, Yangyang
    Yu, Qinxu
    Yang, Qin
    METALLURGICAL AND MATERIALS TRANSACTIONS B-PROCESS METALLURGY AND MATERIALS PROCESSING SCIENCE, 2013, 44 (05): : 1137 - 1143
  • [37] Containerless solidification studies of the 1/1 phase in Ti-(Mn,Cr,Fe)-Si-O alloys
    Croat, TK
    Kelton, KF
    Holland-Moritz, D
    Rathz, TJ
    Robinson, MB
    QUASICRYSTALS, 1999, 553 : 43 - 48
  • [38] LATTICE-PARAMETERS OF CEMENTITE IN FE-C-CR, FE-C-MN, FE-C-MO, AND FE-C-NI ALLOYS
    KAGAWA, A
    OKAMOTO, T
    TRANSACTIONS OF THE JAPAN INSTITUTE OF METALS, 1979, 20 (11): : 659 - 666
  • [39] EFFECT OF MO AND SI ON PRECIPITATION BEHAVIOR OF LAVES PHASE IN FE-10-PERCENT-CR ALLOYS
    MIYAHARA, K
    HWANG, JH
    SHIMOIDE, Y
    IWAMOTO, T
    HOSOI, Y
    JOURNAL OF THE JAPAN INSTITUTE OF METALS, 1995, 59 (05) : 512 - 518
  • [40] QUASI-CRYSTALLINE GA-PD-M (M = CR, MN OR FE) ALLOYS PREPARED BY RAPID SOLIDIFICATION
    YOKOYAMA, Y
    INOUE, A
    MASUMOTO, T
    MATERIALS TRANSACTIONS JIM, 1992, 33 (10): : 953 - 955
12345