Roughness of the surface layers of plasma oxidation-treated ductile cast iron

被引：3

作者：

Jeong, BY ^{[1
]}

Hwang, MS ^{[1
]}

Lee, C ^{[1
]}

Kim, MH ^{[1
]}

机构：

[1] Inha Univ, Dept Met Engn, Inchon 402751, South Korea

来源：

SURFACE & COATINGS TECHNOLOGY | 2001年 / 135卷 / 2-3期

关键词：

plasma oxidation; ductile cast iron; plasma etching; optical emission spectroscopy (OES); spheroidal graphite;

D O I：

10.1016/S0257-8972(00)00984-1

中图分类号：

TB3 [工程材料学];

学科分类号：

0805 ; 080502 ;

摘要：

The roughness of the surface layers of oxygen plasma-treated ductile cast iron was investigated. The non-intrusive technique of optical emission spectroscopy was used to identify the oxygen plasma species. The etching behaviors at various substrate temperatures in the oxygen plasma treatment were investigated using atomic force microscopy. The etching depth increased first with increasing substrate temperature, and reached maximum depth at 500 degreesC, and then decreased with increasing the substrate temperature further. (C) 2001 Elsevier Science B.V. All rights reserved.

引用

页码：279 / 285

页数：7

共 50 条

[1] Surface Hardening of Ductile Cast Iron by Electrolytic Plasma Technology
Ayday, A.
Durman, M.
ACTA PHYSICA POLONICA A, 2013, 123 (02) : 291 - 293
[2] Fabrication of high chromium white iron surface layers on ductile cast iron substrate by laser surface alloying
Silesian University of Technology, Faculty of Mechanical Engineering, Konarskiego 18A, Gliwice, Poland
Stroj Vest, 12 (705-714):
[3] Fabrication of High Chromium White Iron Surface Layers on Ductile Cast Iron Substrate by Laser Surface Alloying
Janicki, Damian
STROJNISKI VESTNIK-JOURNAL OF MECHANICAL ENGINEERING, 2017, 63 (12): : 705 - 714
[4] Fabrication of tic-reinforced surface layers on ductile cast iron substrate by laser surface alloying
Janicki D.
Solid State Phenomena, 2020, 308 : 76 - 99
[5] Application of EDS microanalysis in the identification of inhomogeneities in surface protective layers on ductile cast iron parts
Boron, L.
Tchorz, A.
PROCEEDINGS OF THE 11TH EUROPEAN WORKSHOP OF THE EUROPEAN-MICROBEAM-ANALYSIS-SOCIETY (EMAS) ON MODERN DEVELOPMENTS AND APPLICATIONS IN MICROBEAM ANALYSIS, 2010, 7
[6] MATERIAL REMOVAL RATE AND SURFACE ROUGHNESS ON GRINDING OF DUCTILE CAST IRON USING MINIMUM QUANTITY LUBRICATION
Rahman, M. M.
Kadirgama, K.
INTERNATIONAL JOURNAL OF AUTOMOTIVE AND MECHANICAL ENGINEERING, 2015, 11 : 2471 - 2483
[7] THE MORPHOLOGY OF DUCTILE CAST IRON SURFACE DAMAGED BY CAVITATION
Dojcinovic, Marina
Eric, Olivera
Rajnovic, Dragan
Sidjanin, Leposava
Balos, Sebastijan
METALLURGICAL & MATERIALS ENGINEERING-ASSOCIATION OF METALLURGICAL ENGINEERS OF SERBIA, 2012, 18 (03): : 165 - 176
[8] Oxidation of Ductile Cast Iron at 900 degree C.
Pelhan, C.
Giessereipraxis, 1975, (01): : 1 - 9
[9] Evaluating Surface Roughness of Ductile Cast Iron Machined by EDM Using Solid and Hollow Cylindrical Copper Electrodes
Mehra, Rahul
Singh, Harvinder
Chaubey, Sujeet Kumar
PERIODICA POLYTECHNICA-MECHANICAL ENGINEERING, 2025, 69 (01): : 46 - 54
[10] Comparison of Mechanical Properties of Ductile Cast Iron and Magnesium-Treated Malleable Cast Iron.
Lepand, H.
Komp, U.
Jahnkow, H.
1978, (05): : 51 - 64

← 1 2 3 4 5 →