Effect of surface modification on the stability of oxide scales formed on TiAl intermetallic alloys at high temperature

被引：5
|
作者：
Pilone, D. [1 ]
Brotzu, A. [1 ]
Felli, F. [1 ]
机构：
[1] Sapienza Univ Roma, Dept ICMA, Via Eudossiana 18, I-00184 Rome, Italy
来源：
21ST EUROPEAN CONFERENCE ON FRACTURE, (ECF21) | 2016年 / 2卷
关键词：
TiAl intermetallics; oxidation; surface modification; OXIDATION BEHAVIOR; ALUMINUM-ALLOY; CORROSION-RESISTANCE; CONVERSION COATINGS; PHOSPHORIC-ACID; TI-6AL-4V; ELEMENTS;
D O I：
10.1016/j.prostr.2016.06.287
中图分类号：
TH [机械、仪表工业];
学科分类号：
0802 ;
摘要：
TiAl intermetallic alloys have many interesting potential applications in the automotive and aerospace industry due to their low density and good mechanical properties at high temperature. Unfortunately they have a low oxidation resistance at temperature higher than 700 degrees C and the improvement of their oxidation behavior is still an open issue. In this work the surface of a TiA1CrNb alloy has been modified by means of either anodic coating or cerium conversion coating. Afterwards the stability of the oxide scale formed at 900 degrees C has been studied by analyzing crack formation and propagation, which is the phenomenon that can produce scale spallation during the alloy cooling. Copyright (C) 2016 The Authors. Published by Elsevier B.V.
引用
收藏
页码：2291 / 2298
页数：8
相关论文
共 50 条
  • [31] Surface analyses of high-temperature oxidated TiAl-based alloys
    Qu, HL
    Zhou, L
    Wei, HR
    RARE METAL MATERIALS AND ENGINEERING, 2000, 29 (02) : 90 - 93
  • [32] Effect of platinum on the growth rate of the oxide scale formed on cast nickel aluminide intermetallic alloys
    Cadoret, Y
    Monceau, D
    Bacos, M
    Josso, P
    Maurice, V
    Marcus, P
    OXIDATION OF METALS, 2005, 64 (3-4): : 185 - 205
  • [33] Effect of Platinum on the Growth Rate of the Oxide Scale Formed on Cast Nickel Aluminide Intermetallic Alloys
    Y. Cadoret
    D. Monceau
    M. -P. Bacos
    P. Josso
    V. Maurice
    P. Marcus
    Oxidation of Metals, 2005, 64 : 185 - 205
  • [34] High Temperature Oxidation Behaviors of Powder Metallurgical γ-TiAl Based Alloys: Effects of Surface Defects on Morphology of the Oxide Scale
    Su, Ziteng
    Song, Xiaolei
    Duan, Zhenxin
    Chen, Hua
    Huang, Haoxuan
    Liu, Yang
    Han, Ying
    METALS, 2022, 12 (10)
  • [35] On the effect of oxide scale stability on the internal nitridation process in high-temperature alloys
    Orosz, R
    Krupp, U
    Christ, HJ
    ZEITSCHRIFT FUR METALLKUNDE, 2005, 96 (07): : 775 - 780
  • [36] Structure and formation mechanism of oxide scales of TiAl/TiB2 composites at high temperature
    Gao, WL
    Zhang, H
    Zhang, EL
    Zeng, SY
    Chen, ZH
    RARE METAL MATERIALS AND ENGINEERING, 2006, 35 (02) : 209 - 212
  • [37] Effect of nitridation on the oxidation behavior of TiAl-based intermetallic alloys
    Zhao, B
    Wu, JS
    Sun, J
    Tu, BJ
    Wang, F
    INTERMETALLICS, 2001, 9 (08) : 697 - 703
  • [38] Oxidizing modification of surface composition of high- temperature alloys
    Getsov, L.B.
    Rybnikov, A.I.
    Krukovskij, P.G.
    Zashchita Metallov, 1995, 31 (04): : 376 - 381
  • [39] Internal friction of γ-TiAl alloys at high temperature
    Weller, M
    Chatterjee, A
    Haneczok, G
    Clemens, H
    JOURNAL OF ALLOYS AND COMPOUNDS, 2000, 310 : 134 - 138
  • [40] Recent Progress in high temperature TiAl Alloys
    Chen, G. L.
    Zhao, L. L.
    Lin, J. P.
    Xu, X. J.
    TMS2011 SUPPLEMENTAL PROCEEDINGS, VOL 2: MATERIALS FABRICATION, PROPERTIES, CHARACTERIZATION, AND MODELING, 2011, : 547 - 555
12345