Localized corrosion behavior of scratches on nickel-base Alloy 690TT

被引：46
|
作者：
Meng, Fanjiang [1 ]
Han, En-Hou [1 ]
Wang, Jianqiu [1 ]
Zhang, Zhiming [1 ]
Me, Wei [1 ]
机构：
[1] Chinese Acad Sci, State Key Lab Corros & Protect, Inst Met Res, Shenyang 110016, Peoples R China
来源：
ELECTROCHIMICA ACTA | 2011年 / 56卷 / 04期
关键词：
Scratch; Localized corrosion; SECM; Crack initiation; Alloy; 690; SCANNING ELECTROCHEMICAL MICROSCOPY; OXIDATION; CRACKING; WATER;
D O I：
10.1016/j.electacta.2010.08.028
中图分类号：
O646 [电化学、电解、磁化学];
学科分类号：
081704 ;
摘要：
Localized corrosion of scratched Alloy 690TT was studied using scanning electrochemical microscopy (SECM) in 10 wt.% NaOH solution and atomic force microscopy (AFM) after short-time oxidation tests in high temperature high pressure water at 250 degrees C. The results show that the scratches detected by SECM displayed more extensive electrochemical activity. The scratch groove and the whole deformed region caused by scratching as anode corresponded to the peak of tip current. The oxides formed in 250 degrees C high purity pressurized water nucleated preferentially at the scratch groove and grew faster than non-scratched surface. The nano-grained scratch groove has more electrochemical reactivity than mechanical twins at scratch banks. The intense localized corrosion could contribute to crack initiation at the bottom of scratch groove. (C) 2010 Elsevier Ltd. All rights reserved.
引用
收藏
页码：1781 / 1785
页数：5
相关论文
共 50 条
  • [41] Electrochemical Corrosion Performance of Mechanically Polished Alloy 690TT at High-Temperature Water (200°C)
    Arjmand, Farzin
    Zhang, Lefu
    CORROSION, 2015, 71 (12) : 1481 - 1489
  • [42] Effect of electropolishing on general corrosion of Alloy 690TT tubes in simulated primary coolant of pressurized water reactors
    Shim, Hee-Sang
    Seo, Myung Ji
    Hur, Do Haeng
    APPLIED SURFACE SCIENCE, 2019, 467 : 467 - 476
  • [43] Corrosion Behavior of Arc Sprayed Nickel-Base Coatings
    Dingyong He
    Na Dong
    Jianmin Jiang
    Journal of Thermal Spray Technology, 2007, 16 : 850 - 856
  • [44] Corrosion Behavior of arc sprayed nickel-base coatings
    He, Dingyong
    Dong, Na
    Jiang, Jianmin
    JOURNAL OF THERMAL SPRAY TECHNOLOGY, 2007, 16 (5-6) : 850 - 856
  • [45] Oxide properties of deformed Alloy 690TT in caustic solution at high temperature
    Wang, X. Y.
    Li, Z. H.
    Bai, Y. K.
    Sun, C.
    Wang, K.
    Liu, T. G.
    Lu, Y. H.
    Shoji, T.
    CORROSION SCIENCE, 2020, 174 (174)
  • [46] Effect of the frequency on fretting corrosion behavior between Alloy 690TT tube and 405 stainless steel plate in high temperature pressurized water
    Zhang, Yusheng
    Ming, Hongliang
    Tang, Lichen
    Wang, Jianqiu
    Qian, Hao
    Han, En-Hou
    TRIBOLOGY INTERNATIONAL, 2021, 164
  • [47] EFFECT OF PHOSPHORUS AND SILICON ON INTERGRANULAR CORROSION OF A NICKEL-BASE ALLOY
    VERMILYEA, DA
    TEDMON, CS
    BROECKER, DE
    CORROSION, 1975, 31 (06) : 222 - 223
  • [48] NICKEL-BASE ALLOY WITH UNUSUAL CREEP-BEHAVIOR
    STROBEL, GR
    METALS ENGINEERING QUARTERLY, 1974, 14 (02): : 12 - 16
  • [49] Stress corrosion behavior of scratched Alloy 690TT steam generator tube in chlorine-containing high-temperature pressurized water
    Wu, Bin
    Meng, Fanjiang
    Zhang, Zhiming
    Li, Rongbo
    Ming, Hongliang
    Wang, Jianqiu
    Han, En-Hou
    MATERIALS AND CORROSION-WERKSTOFFE UND KORROSION, 2022, 73 (10): : 1563 - 1574
  • [50] CYCLIC CREEP-BEHAVIOR OF A NICKEL-BASE ALLOY
    WANG, X
    NI, QH
    ZHOU, H
    KONG, QP
    MATERIALS SCIENCE AND ENGINEERING A-STRUCTURAL MATERIALS PROPERTIES MICROSTRUCTURE AND PROCESSING, 1990, 123 (02): : 207 - 211
12345