Evaluation of the interfacial adhesion between brittle coating and ductile substrate by cross-sectional indention

被引：0
|
作者：
Su, JY [1 ]
Zhang, K [1 ]
Chen, GN [1 ]
机构：
[1] Chinese Acad Sci, Inst Mech, Beijing 100080, Peoples R China
来源：
14TH CONGRESS OF INTERNATIONAL FEDERATION FOR HEAT TREATMENT AND SURFACE ENGINEERING, VOLS 1 and 2, PROCEEDINGS | 2004年
关键词：
coating; interface adhesion; indentation;
D O I：
暂无
中图分类号：
TH [机械、仪表工业];
学科分类号：
0802 ;
摘要：
The cross-sectional indentation method is extended to evaluate the interfacial adhesion between brittle coating and ductile substrate. The experimental results on electroplated chromium coating/steel substrate show that the interfacial separation occurs due to the edge chipping of brittle coating. The corresponding models are established to elucidate interfacial separation processes. This work further highlights the advantages and potential of this novel indentation method.
引用
收藏
页码：1187 / 1190
页数：4
相关论文
共 50 条
  • [21] EVALUATION OF ADHESION BETWEEN ADHESIVE COATING AND STEEL SUBSTRATE BY ULTRASONIC METHOD
    Ulbrich, D.
    Selech, J.
    Romek, D.
    Wlodarczyk, K.
    Kowalczyk, J.
    Marcinkiewicz, J.
    Staszak, Z.
    ENGINEERING MECHANICS 2018 PROCEEDINGS, VOL 24, 2018, : 881 - 884
  • [22] Thin films interfacial adhesion characterization by Cross-Sectional Nanoindentation: Application to pad structures
    Gallois-Garreignot, S.
    Chave, F.
    Gonchond, J. P.
    Gautheron, B.
    Fiori, V.
    Nelias, D.
    2009 11TH ELECTRONICS PACKAGING TECHNOLOGY CONFERENCE (EPTC 2009), 2009, : 947 - +
  • [23] Interfacial Adhesion of Thick NiTi Coating on Substrate Stainless Steel
    Samal, Sneha
    Kopecek, Jaromir
    Sittner, Petr
    MATERIALS, 2022, 15 (23)
  • [24] Cross-sectional and plan-view observation of cracks introduced in Si at the ductile-brittle transition temperature
    Suprijadi
    Saka, H.
    Materials Research Society Symposium - Proceedings, 1999, 539 : 169 - 174
  • [25] Cross-sectional and plan-view observation of cracks introduced in Si at the ductile-brittle transition temperature
    Suprijadi
    Saka, H
    FRACTURE AND DUCTILE VS. BRITTLE BEHAVIOR-THEORY, MODELLING AND EXPERIMENT, 1999, 539 : 169 - 174
  • [26] Evaluation of interfacial adhesion between Si substrate and organic polymer dielectric film
    Yamazaki, H
    Enoki, M
    JOURNAL OF THE JAPAN INSTITUTE OF METALS, 2004, 68 (07) : 462 - 467
  • [27] Failure assessment of a hard brittle coating on a ductile substrate subjected to cyclic contact loading
    Toyama, Hidehiko
    Niwa, Michihiro
    Xu, Jun
    Yonezu, Akio
    ENGINEERING FAILURE ANALYSIS, 2015, 57 : 118 - 128
  • [28] Digital image correlation approach to cracking and decohesion in a brittle coating/ductile substrate system
    Wu, D. J.
    Mao, W. G.
    Zhou, Y. C.
    Lu, C.
    APPLIED SURFACE SCIENCE, 2011, 257 (14) : 6040 - 6043
  • [29] Fracture properties of thin brittle MTM clay coating on ductile HEC polymer substrate
    da Costa, Marcus Vinicius Tavares
    Li, Lengwan
    Berglund, Lars A.
    MATERIALS & DESIGN, 2023, 230
  • [30] Evaluation of adhesion between coating and substrate by a single pendulum impact scratch test
    Duan, D. L.
    Li, S.
    Zhang, R. L.
    Hu, W. Y.
    Li, S. Z.
    THIN SOLID FILMS, 2006, 515 (04) : 2244 - 2250
12345