Enhanced diffusion of Cu in aluminium under low-energy ion bombardment

被引：1
|
作者：
Sternberg, Z
Stupnisek, M
机构：
[1] Rudjer Boskovic Inst, Zagreb, Croatia
[2] Fac Mech Engn & Naval Architecture, Zagreb, Croatia
来源：
EUROPHYSICS LETTERS | 2005年 / 71卷 / 05期
关键词：
D O I：
10.1209/epl/i2004-10548-y
中图分类号：
O4 [物理学];
学科分类号：
0702 ;
摘要：
Sputter deposition of copper on aluminium, under intense bombardment of low-energy ions resulted in the formation of two interfacial zones. The mean diffusion coefficient effective in the formation of the first zone, <= 3 x 10(-10) cm(2)/s, is attributed to vacancy supersaturation. The results strongly suggest that by supplying the necessary energy for the formation of vacancies, the activation energy for diffusion can be reduced to the level of the enthalpy of migration, provided lifetimes of freely migrating defects are sufficiently long.
引用
收藏
页码：757 / 762
页数：6
相关论文
共 50 条
  • [21] Roughness evolution of Si(111) by low-energy ion bombardment
    Chan, ACT
    Wang, GC
    SURFACE SCIENCE, 1998, 414 (1-2) : 17 - 25
  • [22] A NEW LOW-ENERGY ION IMPLANTER FOR BOMBARDMENT OF CYLINDRICAL SURFACES
    RENIER, M
    LUCAS, AA
    DONNELLY, SE
    VACUUM, 1985, 35 (12) : 577 - 578
  • [23] OXIDATION OF MOLYBDENUM BY LOW-ENERGY OXYGEN-ION BOMBARDMENT
    Badovinac, Ivana Jelovica
    Piltaver, Ivna Kavre
    Saric, Iva
    Peter, Robert
    Petravic, Mladen
    MATERIALI IN TEHNOLOGIJE, 2017, 51 (04): : 617 - 621
  • [24] InN: Fermi level stabilization by low-energy ion bombardment
    Piper, L. F. J.
    Veal, T. D.
    McConville, C. F.
    Lu, H.
    Schaff, W. J.
    PHYSICA STATUS SOLIDI C - CURRENT TOPICS IN SOLID STATE PHYSICS, VOL 3, NO 6, 2006, 3 (06): : 1841 - 1845
  • [25] Defect formation in graphene during low-energy ion bombardment
    Ahlberg, P.
    Johansson, F. O. L.
    Zhang, Z. -B.
    Jansson, U.
    Zhang, S. -L.
    Lindblad, A.
    Nyberg, T.
    APL MATERIALS, 2016, 4 (04):
  • [26] Stress evolution in Si during low-energy ion bombardment
    Ishii, Yohei
    Madi, Charbel S.
    Aziz, Michael J.
    Chason, Eric
    JOURNAL OF MATERIALS RESEARCH, 2014, 29 (24) : 2942 - 2948
  • [27] DAMAGE CAUSED IN SILICON DIOXIDE BY LOW-ENERGY ION BOMBARDMENT
    MCCAUGHA.DV
    MURPHY, VT
    JOURNAL OF THE ELECTROCHEMICAL SOCIETY, 1971, 118 (08) : C214 - &
  • [28] SURFACE ROUGHENING OF COPPER BY LOW-ENERGY ION-BOMBARDMENT
    NAUNDORF, V
    MACHT, MP
    NUCLEAR INSTRUMENTS & METHODS, 1980, 168 (1-3): : 405 - 409
  • [29] THE DEPTH OF LOW-ENERGY ION-BOMBARDMENT DAMAGE IN TUNGSTEN
    WEBBER, RD
    WALLS, JM
    ULTRAMICROSCOPY, 1980, 5 (02) : 252 - 253
  • [30] VACANCY CREATION DURING LOW-ENERGY ION-BOMBARDMENT
    EDWARDS, D
    KORNELSEN, EV
    RADIATION EFFECTS AND DEFECTS IN SOLIDS, 1975, 26 (03): : 155 - 160
12345