Transformation of the Surface Cracks of in Continuously Cast Slabs Made of Low-Alloy Pipe Steels during Hot Rolling

被引：2
|
作者：
Chukin, M., V [1 ]
Salganik, V. M. [1 ]
Moller, A. B. [1 ]
Chikishev, D. N. [1 ]
机构：
[1] Nosov Magnitogorsk State Tech Univ, Magnitogorsk 455000, Russia
来源：
RUSSIAN METALLURGY | 2021年 / 2021卷 / 10期
关键词：
hot rolling; thick-sheet steel; low-alloy pipe steels; continuously cast slab; mathematical model; finite element method; surface crack; surface crack transformation;
D O I：
10.1134/S0036029521100116
中图分类号：
TF [冶金工业];
学科分类号：
0806 ;
摘要：
A finite-element mathematical model is developed to describe the transformation of the surface cracks of continuously cast slabs made of low-alloy pipe steels into sheet defects during hot rolling. The transformation of axial, edge, rib, and side cracks of a slab is investigated. It is found that, depending on the deformation conditions, surface cracks on rolling a slab into a thick sheet can close in the first passages under compressive stresses, come to the surface, form folds, twist toward the edge, or completely rolled out.
引用
收藏
页码：1275 / 1283
页数：9
相关论文
共 50 条
  • [21] HOT CRACKING OF LOW-ALLOY STEELS IN SIMULATED CONTINUOUS-CASTING DIRECT ROLLING PROCESS
    MAEHARA, Y
    NAKAI, K
    YASUMOTO, K
    MISHIMA, T
    TRANSACTIONS OF THE IRON AND STEEL INSTITUTE OF JAPAN, 1988, 28 (12) : 1021 - 1027
  • [22] HOT CRACKING OF LOW-ALLOY STEELS IN SIMULATED CONTINUOUS CASTING-DIRECT ROLLING PROCESS
    MAEHARA, Y
    NAKAI, K
    YASUMOTO, K
    MISHIMA, T
    TETSU TO HAGANE-JOURNAL OF THE IRON AND STEEL INSTITUTE OF JAPAN, 1987, 73 (07): : 876 - 883
  • [23] EFFECT OF BORON ACCOMPANIED BY CHROMIUM, VANADIUM AND TITANIUM ON THE TRANSFORMATION TEMPERATURES OF LOW-ALLOY CAST STEELS
    Bialobrzeska, B.
    Dziurka, R.
    ARCHIVES OF METALLURGY AND MATERIALS, 2023, 68 (01) : 257 - 267
  • [24] Hot Cracking Susceptibility of Welded Joints of Low-Alloy CrNiMoV Steels and the Conditions for Preventing the Occurrence of Hot Cracks.
    Pilous, Vaclav
    Zvaranie Bratislava, 1981, 30 (07): : 193 - 197
  • [25] EFFECT OF THERMOMECHANICAL HISTORY ON SURFACE CRACKING OF AS-CAST LOW-CARBON LOW-ALLOY STEEL SLABS
    YASUMOTO, K
    MAEHARA, Y
    NAGAMICHI, T
    TOMONO, H
    ISIJ INTERNATIONAL, 1989, 29 (11) : 933 - 939
  • [26] EFFECT OF THERMOMECHANICAL HISTORY ON SURFACE CRACKING OF AS-CAST LOW-CARBON LOW-ALLOY STEEL SLABS
    YASUMOTO, K
    MAEHARA, Y
    NAGAMICHI, T
    TOMONO, H
    TETSU TO HAGANE-JOURNAL OF THE IRON AND STEEL INSTITUTE OF JAPAN, 1987, 73 (10): : 1381 - 1388
  • [27] Solubility Study of Carbonitrides in Low-Alloy Pipe Steels with Mo and Nb at Heating for Rolling Based on Thermodynamic Calculations
    Gorbachev, I. I.
    Popov, V. V.
    Khabibulin, D. M.
    Urtsev, N. V.
    PHYSICS OF METALS AND METALLOGRAPHY, 2024, 125 (11): : 1219 - 1223
  • [28] Formation of surface heat crack in low carbon steels during hot rolling
    Lee, JL
    Pan, YT
    Hwang, YS
    37TH MECHANICAL WORKING AND STEEL PROCESSING CONFERENCE PROCEEDINGS, 1996, 33 : 11 - 21
  • [29] Investigation of the temperature distribution in seamless low-alloy steel pipes during the hot rolling process
    Langbauer, Raphael
    Nunner, Georg
    Zmek, Thomas
    Klarner, Jurgen
    Prieler, Rene
    Hochenauer, Christoph
    ADVANCES IN INDUSTRIAL AND MANUFACTURING ENGINEERING, 2021, 2
  • [30] Microstructure Evolution and Mechanical Property of Low-Alloy Steel Used for Armor Layer of Flexible Pipe During Thermomechanical Process and Hot Rolling Process
    Liu, Zhenguang
    Chen, Shoudong
    Gao, Xiuhua
    Su, Guanqiao
    Du, Linxiu
    Li, Jianping
    Wang, Xiaonan
    Zhou, Xiaowei
    JOURNAL OF MATERIALS ENGINEERING AND PERFORMANCE, 2019, 28 (01) : 107 - 116
12345