Transformation of the Surface Cracks of in Continuously Cast Slabs Made of Low-Alloy Pipe Steels during Hot Rolling

被引：2

作者：

Chukin, M., V ^{[1
]}

Salganik, V. M. ^{[1
]}

Moller, A. B. ^{[1
]}

Chikishev, D. N. ^{[1
]}

机构：

[1] Nosov Magnitogorsk State Tech Univ, Magnitogorsk 455000, Russia

来源：

RUSSIAN METALLURGY | 2021年 / 2021卷 / 10期

关键词：

hot rolling; thick-sheet steel; low-alloy pipe steels; continuously cast slab; mathematical model; finite element method; surface crack; surface crack transformation;

D O I：

10.1134/S0036029521100116

中图分类号：

TF [冶金工业];

学科分类号：

0806 ;

摘要：

A finite-element mathematical model is developed to describe the transformation of the surface cracks of continuously cast slabs made of low-alloy pipe steels into sheet defects during hot rolling. The transformation of axial, edge, rib, and side cracks of a slab is investigated. It is found that, depending on the deformation conditions, surface cracks on rolling a slab into a thick sheet can close in the first passages under compressive stresses, come to the surface, form folds, twist toward the edge, or completely rolled out.

引用

页码：1275 / 1283

页数：9

共 50 条

[1] Transformation of the Surface Cracks of in Continuously Cast Slabs Made of Low-Alloy Pipe Steels during Hot Rolling
M. V. Chukin
V. M. Salganik
A. B. Moller
D. N. Chikishev
Russian Metallurgy (Metally), 2021, 2021 : 1275 - 1283
[2] OVERVIEW - SURFACE CRACKING MECHANISM OF CONTINUOUSLY CAST LOW-CARBON LOW-ALLOY STEEL SLABS
MAEHARA, Y
YASUMOTO, K
TOMONO, H
NAGAMICHI, T
OHMORI, Y
MATERIALS SCIENCE AND TECHNOLOGY, 1990, 6 (09) : 793 - 806
[3] TRANSFORMATION OF SURFACE-DEFECTS ON CONTINUOUSLY CAST BILLETS DURING HOT-ROLLING
LIBERMAN, AL
KAN, YE
MIRONOVA, NA
LUKER, MG
LAPSHIN, OV
STEEL IN THE USSR, 1984, 14 (09): : 428 - 431
[4] AUTOMATIC DETECTION OF SURFACE-DEFECTS ON CONTINUOUSLY CAST HOT SLABS .3. QUICK DETECTION OF LONGITUDINAL FACIAL CRACKS ON CONTINUOUSLY CAST HOT SLABS
KOMORI, S
MIYANO, H
HORIUCHI, Y
YOSHINO, M
YAMADA, T
UESUGI, M
TRANSACTIONS OF THE IRON AND STEEL INSTITUTE OF JAPAN, 1982, 22 (09) : B260 - B260
[5] EFFECT OF CARBON ON HOT DUCTILITY OF AS-CAST LOW-ALLOY STEELS
MAEHARA, Y
YASUMOTO, K
SUGITANI, Y
GUNJI, K
TETSU TO HAGANE-JOURNAL OF THE IRON AND STEEL INSTITUTE OF JAPAN, 1985, 71 (11): : 1534 - 1541
[6] EFFECT OF CARBON ON HOT DUCTILITY OF AS-CAST LOW-ALLOY STEELS
MAEHARA, Y
YASUMOTO, K
SUGITANI, Y
GUNJI, K
TRANSACTIONS OF THE IRON AND STEEL INSTITUTE OF JAPAN, 1985, 25 (10) : 1045 - 1052
[7] Surface cracking mechanism of continuously cast low carbon low alloy steel slabs
1990, (06)
[8] EFFECT OF THERMOMECHANICAL HISTORY ON SURFACE CRACKING OF AS CAST LOW-ALLOY STEEL SLABS
YASUMOTO, K
TETSU TO HAGANE-JOURNAL OF THE IRON AND STEEL INSTITUTE OF JAPAN, 1986, 72 (04): : S165 - S165
[9] STUDY OF STRUCTURAL BEHAVIOR OF LOW-ALLOY STEELS DURING CONTROLLED ROLLING
ROTHWELL, AB
MEMOIRES SCIENTIFIQUES DE LA REVUE DE METALLURGIE, 1972, 69 (06): : 413 - &
[10] EFFECT OF SURFACE-ROUGHNESS ON HOT DUCTILITY OF LOW-ALLOY STEELS
MAEHARA, Y
TETSU TO HAGANE-JOURNAL OF THE IRON AND STEEL INSTITUTE OF JAPAN, 1985, 71 : 1017 - 1017

← 1 2 3 4 5 →