Heterogeneous Fenton-like oxidative degradation of sulfanilamide catalyzed by RuO2-rectorite composite

RuO2-rectorite (RuO2-Rec) was prepared by intercalation, deposition and calcination. Its structure was characterized by XRD, XPS, SEM and EDS. It was used as a catalyst for the sulfanilamide (SA) degradation in the presence of H2O2. Unlike sodium-rectorite and RuO2 which couldn't catalyze the degradation of SA, RuO2-Rec could effectively catalyze the decomposition of H2O2 into hydroxyl radicals to degrade SA. The degradation rate could reach similar to 100% under the optimal conditions of 58 mu mol/L of SA, 1.16 mmol/L of H2O2, 0.133 g/L of RuO2-Rec, pH 3.5 and 25 degrees C in 5 h. The degradation process conformed to pseudo-first-order kinetic correlation. This degradation was affected by pH, the amount of RuO2-Rec and the concentrations of H2O2 and SA. However, under the optimal pH value of 3.5, a high degradation rate could be achieved with the increase in SA concentration from 58 mu mol/L to 290 mu mol/L as long as the optimal ratio of RuO2-Rec, H2O2 and SA kept unchanged. In addition, RuO2-Rec was stable and possessed low ruthenium leaching rate and excellent reusability. Therefore, RuO2-Rec is expected to be an active catalyst for the pollutant removal in the heterogeneous Fenton-like system.