Research on mechanical and erosion behavior of stepped polymeric functionally graded materials reinforced with aluminum

被引：10

作者：

Boggarapu, Vasavi ^{[1
]}

Ruthik, L. ^{[1
]}

Adapa, Sunil ^{[1
]}

Kanakam, Rakesh ^{[1
]}

Ojha, Shakuntla ^{[2
]}

Gujjala, Raghavendra ^{[1
]}

机构：

[1] Natl Inst Technol, Dept Mech Engn, Warangal 506004, Andhra Pradesh, India

[2] Kakatiya Inst Technol & Sci, Dept Mech Engn, Warangal, Andhra Pradesh, India

来源：

POLYMER COMPOSITES | 2022年 / 43卷 / 02期

关键词：

epoxy; erosion wear; functionally graded materials; mechanical strength; thermal curing; SLURRY EROSION; PARTICLE-SIZE; WEAR BEHAVIOR; COMPOSITES; RESISTANCE; GRADIENT;

D O I：

10.1002/pc.26433

中图分类号：

TB33 [复合材料];

学科分类号：

摘要：

The aim of this research is to evaluate the mechanical and erosion characteristics of stepped polymeric functionally graded materials (PFGMs) reinforced with aluminum particles. By varying the filler content, gradation is achieved along the sample's thickness direction. Three distinct methodologies were adopted in the fabrication of PFGMs; no curing time between the layers (M1), providing curing time between the layers at room temperature (M2) and thermal curing between the layers at 60 degrees C (M3). The results showed that tensile strength and compressive strength of sample M3 increased by 30.3%, 20.8% and 10.3%, 5% as compared to M1 and M2 respectively. The flexural strength of M3 was enhanced by 9% when load direction was from top to bottom (T-B) than from bottom to top (B-T). Moreover, the erosion resistance of M3 was higher among all the test samples.

引用

页码：1048 / 1059

页数：12

共 50 条

[31] Flexural Behavior of Functionally Graded Plates with Piezoelectric Materials
Chanda, Aniket
Sahoo, Rosalin
ARABIAN JOURNAL FOR SCIENCE AND ENGINEERING, 2020, 45 (11) : 9227 - 9248
[32] Flexural Behavior of Functionally Graded Plates with Piezoelectric Materials
Aniket Chanda
Rosalin Sahoo
Arabian Journal for Science and Engineering, 2020, 45 : 9227 - 9248
[33] Behavior of functionally graded concrete beams reinforced with steel slag
Selmi, Abdellatif
Hlel, Moncef Ben
INTERNATIONAL JOURNAL OF COMPUTATIONAL MATERIALS SCIENCE AND ENGINEERING, 2024, 13 (02)
[34] Research Progress in Manufacturing Technology of Functionally Graded Materials
Song C.-C.
Yan X.-R.
Zhang Z.-A.
Di T.-D.
Ma G.-Y.
Niu F.-Y.
Wu D.-J.
Surface Technology, 2022, 51 (12): : 20 - 38
[35] Thermo-Mechanical Behavior of Spatially Tailored Functionally Graded Materials in a High Temperature Environment
Deierling, P.
Zhupanska, O. I.
Pasiliao, C. L.
PROCEEDINGS OF THE AMERICAN SOCIETY FOR COMPOSITES: THIRTIETH TECHNICAL CONFERENCE, 2015, : 1462 - 1472
[36] Erosion Behavior of Fiber Reinforced Materials.
Armbrust, S.
Kunststoffe, 1973, 63 (12): : 907 - 910
[37] Preparation and Mechanical Properties of Zirconia / Nickel Functionally Graded Materials
El-Wazery, M. S.
EL-Desouky, A. R.
Hamed, O. A.
Mansour, N. A.
Hassan, Ahmed. A.
ARAB JOURNAL OF NUCLEAR SCIENCES AND APPLICATIONS, 2012, 45 (02): : 435 - 446
[38] Mechanical characterization of functionally graded materials with a yield strength gradient
Nayebi, A
Mauvoisin, G
Bartier, O
El Abdi, R
SURFACE ENGINEERING 2001 - FUNDAMENTALS AND APPLICATIONS, 2001, 697 : 21 - 26
[39] DEVELOPMENT OF SPECIFIC PROPERTIES OF FUNCTIONALLY GRADED MATERIALS IN MECHANICAL SYSTEMS
Nistor, Liviu
Lazar, Vasile
METALURGIA INTERNATIONAL, 2010, 15 (09): : 65 - 69
[40] Mechanical modeling of Thin Films Bonded to Functionally Graded Materials
Guler, Mehmet Ali
Gulver, Yusuf Fuat
Dag, Serkan
MULTISCALE, MULTIFUNCTIONAL AND FUNCTIONALLY GRADED MATERIALS, 2010, 631-632 : 333 - +

← 1 2 3 4 5 →