Influence of the configuration of reconstituted specimens on fracture toughness characterisation of pressure vessel steels

被引：0
|
作者：
DeBacker, F
GutierrezSolana, F
机构：
来源：
ECF 11 - MECHANISMS AND MECHANICS OF DAMAGE AND FAILURE, VOLS I-III | 1996年
关键词：
D O I：
暂无
中图分类号：
TH [机械、仪表工业];
学科分类号：
0802 ;
摘要：
Specimen reconstitution techniques offer the possibility to obtain fracture toughness measurements when only small amounts of material are available. In order to obtain extra information from Charpy specimens, an electron-beam weld reconstitution method is established to obtain Compact Tension specimens from the broken halves of Charpy specimens. The validity of the fracture toughness characterisation is analysed by comparing J(R)-resistance curves of specimens with insert and those of normalised specimens without insert.
引用
收藏
页码：1965 / 1970
页数：6
相关论文
共 50 条
  • [41] An updated correlation for crack-arrest fracture toughness for nuclear reactor pressure vessel steels
    Bass, BR
    Williams, PT
    Pugh, CE
    INTERNATIONAL JOURNAL OF PRESSURE VESSELS AND PIPING, 2005, 82 (06) : 489 - 495
  • [42] Evaluation of fracture toughness and its scatter in the DBTT region of different types of pressure vessel steels
    Samal, M. K.
    Chakravartty, J. K.
    Seidenfuss, M.
    Roos, E.
    ENGINEERING FAILURE ANALYSIS, 2011, 18 (01) : 172 - 185
  • [43] A New Engineering Method for Prediction of Fracture Toughness Temperature Dependence for Pressure-Vessel Steels
    B. Z. Margolin
    A. G. Gulenko
    V. A. Nikolaev
    L. N. Ryadkov
    Strength of Materials, 2003, 35 (5) : 440 - 457
  • [44] Fracture toughness of tool steels using chevron notched specimens
    Villellas, A
    Rios, R
    Martinez, A
    Campos, G
    ECF 11 - MECHANISMS AND MECHANICS OF DAMAGE AND FAILURE, VOLS I-III, 1996, : 577 - 582
  • [45] INFLUENCE OF MANGANESE ON FRACTURE TOUGHNESS OF NICKEL STEELS
    BROOK, R
    SILVA, PSPD
    INTERNATIONAL JOURNAL OF FRACTURE, 1976, 12 (01) : 27 - 32
  • [46] FRACTURE OF REACTOR PRESSURE VESSEL STEELS.
    Radon, J.C.
    Clover, A.P.
    Johnson, F.A.
    Materialpruefung/Materials Testing, 1975, 17 (09): : 319 - 321
  • [47] NUMERICAL PREDICTION OF FRACTURE TOUGHNESS OF A REACTOR PRESSURE VESSEL STEEL BASED ON EXPERIMENTS USING SMALL SPECIMENS
    Metzler, Timo
    Gaganidze, Ermile
    Aktaa, Jarir
    PROCEEDINGS OF ASME 2023 PRESSURE VESSELS & PIPING CONFERENCE, PVP2023, VOL 1, 2023,
  • [48] A LOCAL APPROACH TO ASSESS EFFECTS OF SPECIMEN GEOMETRY ON CLEAVAGE FRACTURE TOUGHNESS IN REACTOR PRESSURE VESSEL STEELS
    Sarzosa, Diego F. B.
    Savioli, Rafael
    Ruggieri, Claudio
    Jivkov, Andrey
    Beswick, Jack
    PROCEEDINGS OF THE ASME PRESSURE VESSELS AND PIPING CONFERENCE, 2018, VOL 6B, 2019,
  • [49] Determination of the key microstructural parameter for the cleavage fracture toughness of reactor pressure vessel steels in the transition region
    Kim, MC
    Lee, BS
    Yang, WJ
    Hong, JH
    ADVANCES IN FRACTURE AND STRENGTH, PTS 1- 4, 2005, 297-300 : 1672 - 1677
  • [50] Radiation embrittlement modelling for reactor pressure vessel steels: I. Brittle fracture toughness prediction
    Margolin, BZ
    Shvetsova, VA
    Gulenko, AG
    INTERNATIONAL JOURNAL OF PRESSURE VESSELS AND PIPING, 1999, 76 (10) : 715 - 729
12345