Magnetic anisotropy of permalloy films grown on an Mo(001) stepped surface

The Mo(001) stepped surface was self-assembled on Al2O3(1-102) substrate by molecular beam epitaxy. Ni80Fe20 films were subsequently deposited on the fresh Mo(001) stepped surface at growth temperature (T-g) between 30 and 400 degreesC. Interestingly, in the low T-g regime (< 100 degreesC) the Ni80Fe20 films were grown as (001) single crystal while high T-g (> 300 degreesC) results in the growth of Ni80Fe20 (110) quadcrystal. For low T-g samples, the easy axis of the Ni80Fe20 film is directed parallel to the underlying Mo step edge direction and the M-H loop along the hard axis reveals a two-step magnetic moment rotation process. In contrast, the high T-g samples display isotropic-like magnetic behavior with a much enhanced coercivity due likely to the surface roughness effect. We conclude that the growth temperature of Ni80Fe20 film on the Mo stepped surface plays an important role on the crystal structure and magnetic anisotropy of Ni80Fe20 film. (C) 2001 American Institute of Physics.