Synthesis and Characterization of Natural Nano-hydroxyapatite Derived from Turkey Femur-Bone Waste

Hydroxyapatite (HAp) is a bioactive and vital material which has found many applications in the biomedical and clinical fields. This bio-ceramic powder can be synthesized via different bio-waste materials. In this study, the production of natural nanohydroxyapatite was produced through calcination of untreated turkey femur-bone waste powder at 850 degrees C followed by ball milling the powder. The obtained powder was characterized using X-ray diffraction (XRD) and Fourier transform infrared spectroscopy (FTIR) analysis. The morphology, size, and elemental composition of obtained turkey hydroxyapatite (THA) particles were investigated by scanning electron microcopy (SEM), transmission electron microcopy (TEM), and energy dispersive spectroscopy (EDS) analysis, in which the average particle size of ball milled THA was found to be about 85 nm with a Ca/P ratio of 1.63. The powder was then cold pressed and later sintered at 850, 950, 1050, and 1150 degrees C to evaluate its mechanical properties in terms of compressive strength and hardness. The results revealed that the strength and hardness of the samples increased by increasing the sintering temperature up to 1150 degrees C. Finally, the maximum values of hardness and compressive strength of the sintered THA were obtained at 1150 degrees C (37.44 MPa and 3.2 GPa, respectively).