The low cycle fatigue behaviour of MAR-M247 superalloy under different strain rates and cycle shapes at 750?C

被引：12

作者：

Sulak, I. ^{[1
]}

Obrtlik, K. ^{[1
]}

Babinsky, T. ^{[1
]}

Guth, S. ^{[2
]}

机构：

[1] Inst Phys Mat ASCR, Zizkova 22, Brno 61600, Czech Republic

[2] Karlsruhe Inst Technol, Inst Appl Mat, Engelbert Arnold Str 4, D-76128 Karlsruhe, Germany

来源：

INTERNATIONAL JOURNAL OF FATIGUE | 2022年 / 164卷

关键词：

Strain rate influence; Slow -fast & fast -slow tests; Creep -fatigue interaction; Nickel -based superalloy; High temperature; THERMOMECHANICAL FATIGUE; ELEVATED-TEMPERATURE; ISOTHERMAL FATIGUE; PHASE-SHIFT; DWELL TIME; CREEP; TENSILE; GROWTH; DEFORMATION; INTRUSIONS;

D O I：

10.1016/j.ijfatigue.2022.107133

中图分类号：

TH [机械、仪表工业];

学科分类号：

0802 ;

摘要：

High-temperature low-cycle fatigue experiments were performed at different strain rates on nickel-based su-peralloy MAR-M247. Furthermore, slow-fast, fast-slow and dwell-fatigue tests were conducted. The deformation, damage and lifetime behaviour as a function of strain rate and cycle shape were observed. Results show that the lifetime decreases with decreasing strain rate, indicating the negative influence of time-dependent creep and oxidation mechanisms. The lifetimes of slow-fast and dwell-fatigue tests are lower than those for fast-slow tests, although the mean stress is compressive in slow-fast and dwell-fatigue tests and tensile in fast-slow tests. Slow -fast and dwell-fatigue tests lead to grain boundary cavitation.

引用

页数：13

共 50 条

[41] Low cycle fatigue and fracture behavior of nickel-base superalloy CM247LC at 760°C
Seo, SM
Kim, IS
Jo, CY
DESIGNING, PROCESSING AND PROPERTIES OF ADVANCED ENGINEERING MATERIALS, PTS 1 AND 2, 2004, 449-4 : 561 - 564
[42] Low cycle fatigue of platinum aluminide coated MAR-M002 nickel-base superalloy in a sulphidizing atmosphere at 870°C
Govender, G
Aghion, E
Comins, N
ECF 12: FRACTURE FROM DEFECTS, VOLS. I-III, 1998, : 411 - 416
[43] Deformation behaviour of the single crystal superalloy SC16 under low cycle fatigue loading
Auerswald, J
Mukherji, D
Chen, WY
Wahi, RP
ZEITSCHRIFT FUR METALLKUNDE, 1997, 88 (08): : 652 - 658
[44] High temperature low cycle fatigue behaviour of UDIMET 720 Li superalloy
Marchionni, M
Osinkolu, GA
Onofrio, G
INTERNATIONAL JOURNAL OF FATIGUE, 2002, 24 (12) : 1261 - 1267
[45] Influence of surface recrystallization on the low cycle fatigue behaviour of a single crystal superalloy
Ma, X.
Shi, H. -J.
Gu, J.
Yang, Z.
Chen, G.
Luesebrink, O.
Harders, H.
FATIGUE & FRACTURE OF ENGINEERING MATERIALS & STRUCTURES, 2015, 38 (03) : 340 - 351
[46] Lifetime, Cyclic Deformation and Damage Behaviour of MAR-M247 LC under Thermo-Mechanical Fatigue Loading with 0°, 180°,-90° and+90° Phase Shift between Strain and Temperature
Guth, Stefan
Doll, Simon
Lang, Karl-Heinz
XVII INTERNATIONAL COLLOQUIUM ON MECHANICAL FATIGUE OF METALS (ICMFM17), 2014, 74 : 269 - 272
[47] Short fatigue crack behaviour under low cycle fatigue regime
Hutar, P.
Poduska, J.
Smid, M.
Kubena, Ivo
Chlupova, A.
Nahlik, L.
Polak, J.
Kruml, T.
INTERNATIONAL JOURNAL OF FATIGUE, 2017, 103 : 207 - 215
[48] Influence of Temperature and Strain Amplitude on Low Cycle Fatigue and Creep–Fatigue Interaction Behaviour of Alloy 617 M
G. V. S. Nageswara Rao
P. Anil Kumar
R. Kannan
A. Nagesha
Transactions of the Indian National Academy of Engineering, 2022, 7 (2) : 509 - 517
[49] Influence of phase angle on lifetime, cyclic deformation and damage behavior of Mar-M247 LC under thermo-mechanical fatigue
Guth, Stefan
Doll, Simon
Lang, Karl-Heinz
MATERIALS SCIENCE AND ENGINEERING A-STRUCTURAL MATERIALS PROPERTIES MICROSTRUCTURE AND PROCESSING, 2015, 642 : 42 - 48
[50] A Strain-based continuum damage model for low cycle fatigue under different strain ratios
Pandey, V. B.
Singh, I. V.
Mishra, B. K.
ENGINEERING FRACTURE MECHANICS, 2021, 242 (242)

← 1 2 3 4 5 →