Compression of wood under saturated steam, superheated steam, and transient conditions at 150°C, 160°C, and 170°C

被引:98
|
作者
Kutnar, Andreja [1 ,2 ]
Kamke, Frederick A. [2 ]
机构
[1] Univ Primorska, Primorska Inst Nat Sci & Technol, Koper 6000, Slovenia
[2] Oregon State Univ, Dept Wood Sci & Engn, Corvallis, OR 97331 USA
关键词
VISCOELASTIC PROPERTIES; BEHAVIOR; DEFORMATION; TEMPERATURE; MANUFACTURE; COMPOSITES; RELEVANT; CREEP;
D O I
10.1007/s00226-010-0380-0
中图分类号
S7 [林业];
学科分类号
0829 ; 0907 ;
摘要
In this paper, the compressive deformation of hybrid poplar wood (Populus deltoides x Populus trichocarpa) at high temperature (150, 160, and 170A degrees C) and under various conditions of steam pressure was studied. Temperature and conditions of steam environment affected the relative density change and creep deformation during compression, as well as properties of the resulting densified material. While the temperature significantly affected the compression deformation of specimens compressed under transient and superheated steam conditions, temperature within the range studied had little effect on the compressive deformation in saturated steam. In all tested conditions, compression deformation was achieved without cell wall fractures. Higher temperature of compression, regardless of steam condition, resulted in lower equilibrium moisture content. In specimens compressed under saturated steam, the modulus of rupture (MOR) and modulus of elasticity (MOE) were increased proportionally to the increase in density, while the compression under superheated steam produced lower increase in the MOE and MOR than expected based on the increase in density. Compression in transient steam conditions at 170A degrees C produced densified wood with higher MOE and MOR than expected based on the increase in density.
引用
收藏
页码:73 / 88
页数:16
相关论文
共 50 条
  • [41] Study on the Mechanism of Oxidation-Accelerated Creep Damage of P92 Steel in 650 °C Superheated Steam
    Shang, C. G.
    Wang, M. L.
    Zhou, Z. C.
    Lu, Y. H.
    Yagi, K.
    HIGH TEMPERATURE CORROSION OF MATERIALS, 2025, 102 (02)
  • [42] Steam Oxidation of Aluminide-Coated and Uncoated TP347HFG Stainless Steel under Atmospheric and Ultra-Supercritical Steam Conditions at 700 °C
    Aguero, Alina
    Baraibar, Ignacio
    Gutierrez, Marcos
    Tuurna, Satu
    Toivonen, Aki
    Pennila, Sami
    Auerkari, Pertti
    COATINGS, 2020, 10 (09)
  • [43] Experimental study of pressure and density of saturated and superheated vapor of refrigerant R-236ea from 20 to 150°C
    Gruzdev V.A.
    Komarov S.G.
    Thermophysics and Aeromechanics, 2006, 13 (3) : 411 - 418
  • [44] Effect of spray drying at 150, 160, and 170 °C on the physical and chemical properties of maqui extract (Aristotelia chilensis (Molina) Stuntz)
    Miguel Bastias-Montes, Jose
    Consuelo Choque-Chavez, Monica
    Alarcon-Enos, Julio
    Quevedo-Leon, Roberto
    Munoz-Farina, Ociel
    Vidal-San-Martin, Carla
    CHILEAN JOURNAL OF AGRICULTURAL RESEARCH, 2019, 79 (01): : 144 - 152
  • [45] Behavior of Slurry Aluminized Austenitic Stainless Steels under Steam at 650 and 700 A°C
    Pedraza, Fernando
    Boulesteix, Claire
    Proy, Manuel
    Lasanta, Isabel
    de Miguel, Teresa
    Illana, Andrea
    Javier Perez, Francisco
    OXIDATION OF METALS, 2017, 87 (3-4): : 443 - 454
  • [46] Oceania Under Steam: Sea Transport and the Cultures of Colonialism, c.1870-1914
    Matsuda, Matt K.
    INTERNATIONAL JOURNAL OF MARITIME HISTORY, 2012, 24 (01) : 453 - 454
  • [47] Oceania under Steam: Sea Transport and the Cultures of Colonialism, c.1870-1914
    Watson, James
    NEW ZEALAND JOURNAL OF HISTORY, 2017, 51 (02): : 133 - 134
  • [48] Behavior of Slurry Aluminized Austenitic Stainless Steels under Steam at 650 and 700 °C
    Fernando Pedraza
    Claire Boulesteix
    Manuel Proy
    Isabel Lasanta
    Teresa de Miguel
    Andrea Illana
    Francisco Javier Pérez
    Oxidation of Metals, 2017, 87 : 443 - 454
  • [49] Diffusion stable aluminide coatings: Behaviour under steam and oxy-fuel fire-side conditions at 650 °C and accelerated diffusion tests at 900 °C
    Aguero, A.
    Gonzalez, V
    Muelas, R.
    SURFACE & COATINGS TECHNOLOGY, 2018, 350 : 119 - 127
  • [50] In-situ electrochemical study of chalcopyrite pressure oxidation leaching from 110 °C to 150 °C under saturated vapor pressure
    Bai, Yunlong
    Wang, Wei
    Xie, Feng
    Lu, Diankun
    Jiang, Kaixi
    Dreisinger, David
    ARABIAN JOURNAL OF CHEMISTRY, 2022, 15 (10)