Hot corrosion behavior of Co modified NiAl coating on nickel base superalloys

被引：82
|
作者：
Qiao, Min [1 ]
Zhou, Chungen [1 ]
机构：
[1] Beijing Univ Aeronaut & Astronaut, Sch Mat Sci & Engn, Beijing 100191, Peoples R China
来源：
CORROSION SCIENCE | 2012年 / 63卷
关键词：
Metal coatings; Superalloys; Hot corrosion; HIGH-TEMPERATURE CORROSION; OXIDATION BEHAVIOR; ALUMINIDE COATINGS; DIFFUSION COATINGS; AL; CR; ALLOY; NACL; CODEPOSITION; VAPOR;
D O I：
10.1016/j.corsci.2012.06.027
中图分类号：
T [工业技术];
学科分类号：
08 ;
摘要：
The microstructure and corrosion behavior was studied for a Co modified NiAl coating formed on the superalloy DZ125 by pack cementation process. The hot corrosion kinetics showed that the mass gain of the coated specimen was three orders of magnitude lower than that of the uncoated specimen at 1173 K up to 100 h. The corrosion product formed on the surface of the coating mainly consisted of a protective alpha-Al2O3 film. The presence of Co in the coating could promote the establishment of a protective Al2O3 scale on the coating and restrain the internal diffusion of sulphur in the coating. (C) 2012 Elsevier Ltd. All rights reserved.
引用
收藏
页码：239 / 245
页数：7
相关论文
共 50 条
  • [41] Hot corrosion studies on plasma spray coatings over some nickel- and iron-base superalloys
    Singh, H
    JOURNAL OF THERMAL SPRAY TECHNOLOGY, 2005, 14 (03) : 311 - 312
  • [42] Hot Corrosion Behavior of Ce-Modified NiAl Coating by Cl-Containing Na2SO4 at 1050 °C
    Hongyu Wang
    Han Wang
    Peng Kan
    Qian Zhao
    Xiang Zhang
    Yang Ding
    Oxidation of Metals, 2018, 90 : 571 - 583
  • [43] Hot Corrosion Behavior of Ce-Modified NiAl Coating by Cl-Containing Na2SO4 at 1050°C
    Wang, Hongyu
    Wang, Han
    Kan, Peng
    Zhao, Qian
    Zhang, Xiang
    Ding, Yang
    OXIDATION OF METALS, 2018, 90 (5-6): : 571 - 583
  • [44] Studies on the hot corrosion behavior of HVOF coatings on some Ni- and Fe-base superalloys
    Sidhu, T. S.
    JOURNAL OF THERMAL SPRAY TECHNOLOGY, 2006, 15 (03) : 320 - 322
  • [45] Influence of aging treatment on microstructure, wear and corrosion behavior of a nickel base hardfaced coating
    Kesavan, D.
    Kamaraj, M.
    WEAR, 2011, 272 (01) : 7 - 17
  • [46] OXIDATION AND HOT-CORROSION RESISTANCE OF COBALT-BASE SUPERALLOYS
    BELTRAN, AM
    METALS ENGINEERING QUARTERLY, 1970, 10 (01): : 51 - &
  • [47] Performance Comparison Between Isothermal Hot Corrosion And In Situ Cyclic Hot Corrosion of Nickel-Based Superalloys
    Adnan. U. Syed
    Fabian Duarte Martinez
    Tracey Roberts
    Adriana Encinas-Oropesa
    Nicolau I. Morar
    Marlene Grohne
    Martin Frommherz
    John R. Nicholls
    Simon Gray
    Oxidation of Metals, 2021, 96 : 43 - 55
  • [48] Performance Comparison Between Isothermal Hot Corrosion And In Situ Cyclic Hot Corrosion of Nickel-Based Superalloys
    Syed, Adnan. U.
    Martinez, Fabian Duarte
    Roberts, Tracey
    Encinas-Oropesa, Adriana
    Morar, Nicolau I.
    Grohne, Marlene
    Frommherz, Martin
    Nicholls, John R.
    Gray, Simon
    OXIDATION OF METALS, 2021, 96 (1-2): : 43 - 55
  • [49] Influence of Salt Coating on Hot Corrosion Behavior of Co-Cr Alloy
    Fu, Guangyan
    Zhao, Xin
    Liu, Qun
    Su, Yong
    ADVANCED SCIENCE LETTERS, 2011, 4 (11-12) : 3633 - 3636
  • [50] HOT CORROSION BEHAVIOR OF A LASER-BEAM IRRADIATED NICKEL-BASE SUPERALLOY
    WANG, MC
    JIN, ZJ
    WU, WT
    WERKSTOFFE UND KORROSION-MATERIALS AND CORROSION, 1987, 38 (03): : 124 - 128
12345