Autogenous Healing of Early-Age Cementitious Materials Incorporating Superabsorbent Polymers Exposed to Wet/Dry Cycles

被引:19
|
作者
Shim, Yewon [1 ]
Hong, Geuntae [1 ]
Choi, Seongcheol [1 ]
机构
[1] Chung Ang Univ, Dept Civil & Environm Engn, 84 Heukseok Ro, Seoul 06974, South Korea
关键词
autogenous healing; capillary water absorption testing; cementitious materials; superabsorbent polymer; wet/dry cycling; WATER PERMEABILITY; HYDRATION; CRACKS; TRANSPORT; CONCRETE; STRENGTH; MORTARS;
D O I
10.3390/ma11122476
中图分类号
O64 [物理化学(理论化学)、化学物理学];
学科分类号
070304 ; 081704 ;
摘要
This study experimentally investigated the autogenous healing performances of cementitious materials incorporating superabsorbent polymers (SAPs) after exposure to eight cycles of wet/dry conditions. In each cycle, cracked cement paste specimens with different SAP dosages were exposed to wet conditions for 1 h, during which capillary water absorption tests were conducted, and then exposed to dry conditions for 47 h. The test results reveal that the initial sorptivity values of the reference, 0.5% SAP, 1.0% SAP, and 1.5% SAP specimens after one cycle were decreased by 22.9%, 36.8%, 42.8%, and 46.3%, respectively, after eight cycles. X-ray micro-computed tomography analysis showed that the crack volume percentages filled with healing products were 1.1%, 1.6%, 2.2%, and 2.9% in the reference, 0.5% SAP, 1.0% SAP, and 1.5% SAP specimens, respectively. As the cycling was repeated, the reduction ratio of the initial sorptivity and the quantity of healing products were increased with increases in SAP dosage. Furthermore, more healing products were distributed near SAP voids than in other sections in the specimens. This study demonstrates that the incorporation of SAPs in cementitious materials can enhance the autogenous healing performances of materials exposed to cyclic wet/dry conditions.
引用
收藏
页数:20
相关论文
共 50 条
  • [31] Study of the Healing Effect of Concrete with Supplementary Cementitious Materials after Early-Age Damage by Acoustic Emission Technique
    Chen, Zhonggou
    He, Rui
    Jin, Xianyu
    APPLIED SCIENCES-BASEL, 2022, 12 (12):
  • [32] Effect of Various Supplementary Cementitious Materials on Early-Age Concrete Cracking
    Khan, Inamullah
    Xu, Tengfei
    Khan, Mohammad Shakhaout Hossain
    Castel, Arnaud
    Gilbert, Raymond Ian
    JOURNAL OF MATERIALS IN CIVIL ENGINEERING, 2020, 32 (04)
  • [33] Freezing-and-Thawing Behavior of Cementitious Materials Containing Superabsorbent Polymers at Early Ages
    Jin, Ming
    Ghantous, Rita Maria
    Tao, Jiayin
    Weiss, Jason
    ACI MATERIALS JOURNAL, 2020, 117 (06) : 243 - 252
  • [34] Effects of Curing Conditions and Supplementary Cementitious Materials on Autogenous Self-Healing of Early Age Cracks in Cement Mortar
    Luo, Mian
    Jing, Kang
    Bai, Jingquan
    Ding, Ziqi
    Yang, Dingyi
    Huang, Haoliang
    Gong, Yongfan
    CRYSTALS, 2021, 11 (07)
  • [35] Review of Ultrasonic Wave Reflection Applied to Early-Age Concrete and Cementitious Materials
    Popovics, John S.
    Subramaniam, Kolluru V. L.
    JOURNAL OF NONDESTRUCTIVE EVALUATION, 2015, 34 (01)
  • [36] Review of Ultrasonic Wave Reflection Applied to Early-Age Concrete and Cementitious Materials
    John S. Popovics
    Kolluru V. L. Subramaniam
    Journal of Nondestructive Evaluation, 2015, 34
  • [37] Self-healing at early-age, a way to improve the chloride resistance of blast-furnace slag cementitious materials
    Darquennes, A.
    Olivier, K.
    Benboudjema, F.
    Gagne, R.
    CONSTRUCTION AND BUILDING MATERIALS, 2016, 113 : 1017 - 1028
  • [38] Early-age autogenous cracking of cementitious matrices: physico-chemical analysis and micro/macro investigations
    Mounanga, Pierre
    Bouasker, Marwen
    Pertue, Arnaud
    Perronnet, Annick
    Khelidj, Abdelhafid
    MATERIALS AND STRUCTURES, 2011, 44 (04) : 749 - 772
  • [39] Early-age autogenous cracking of cementitious matrices: physico-chemical analysis and micro/macro investigations
    Pierre Mounanga
    Marwen Bouasker
    Arnaud Pertue
    Annick Perronnet
    Abdelhafid Khelidj
    Materials and Structures, 2011, 44 : 749 - 772
  • [40] The Effect of Superabsorbent Polymers on the Microstructure and Self-Healing Properties of Cementitious-Based Composite Materials
    Kanellopoulou, Irene A.
    Kartsonakis, Ioannis A.
    Charitidis, Costas A.
    APPLIED SCIENCES-BASEL, 2021, 11 (02): : 1 - 19