Evaluation of temperature and humidity on PV module degradation- in field degradation analysis of crystalline silicon module

被引：0
|
作者：
Li, Hailing [1 ,2 ,3 ]
Lv, Fang [1 ,2 ]
Diao, Hongwei [1 ,2 ]
Chen, Xu [1 ,2 ]
Wang, Wenjing [1 ,2 ,3 ]
机构：
[1] Chinese Acad Sci, Key Lab Solar Thermal Energy & Photovolta Syst, Beijing 100190, Peoples R China
[2] Chinese Acad Sci, Inst Elect Engn, Beijing, Peoples R China
[3] Univ Chinese Acad Sci UCAS, Beijing 100190, Peoples R China
来源：
2019 IEEE 46TH PHOTOVOLTAIC SPECIALISTS CONFERENCE (PVSC) | 2019年
关键词：
Photovoltaic systems; module; silicon; degradation;
D O I：
10.1109/pvsc40753.2019.8981241
中图分类号：
TE [石油、天然气工业]; TK [能源与动力工程];
学科分类号：
0807 ; 0820 ;
摘要：
PV modules operated in humid and hot climate area in different sites with different operating years were investigated. The average degradation rate is 1.18%/y, higher than guarantee of 20% for 25 years (0.8%/y). By investigating modules from 3 plants operating for 3 years, 6 years and 15 years, the influence of operating year on degradation are studied. As reported before, corrosion of metallic materials is considered to be one of the main degradation models. We find linear relationship between FF and P. degradation, especially at the case with long operating year.
引用
收藏
页码：1986 / 1990
页数：5
相关论文
共 50 条
  • [21] Spatial Investigation and Analysis of PID Shunting in Crystalline Silicon PV Module
    Puranik, Vishal E.
    Gupta, Rajesh
    2021 IEEE 48TH PHOTOVOLTAIC SPECIALISTS CONFERENCE (PVSC), 2021, : 2372 - 2375
  • [22] Corrosion of the Glass and Formation of Lead Compounds in the Metallization by High Temperature and High Humidity Test of Crystalline Silicon PV Module
    Semba, Taeko
    Shimada, Takeo
    Yamada, Kazuyoshi
    Shirasawa, Katsuhiko
    Takato, Hidetaka
    2018 IEEE 7TH WORLD CONFERENCE ON PHOTOVOLTAIC ENERGY CONVERSION (WCPEC) (A JOINT CONFERENCE OF 45TH IEEE PVSC, 28TH PVSEC & 34TH EU PVSEC), 2018, : 1333 - 1335
  • [23] Influence of Front-Side Ag Metallization on High Temperature and High Humidity Test of Crystalline Silicon PV Module
    Semba, Taeko
    Shimada, Takeo
    Fujita, Takayuki
    2019 IEEE 46TH PHOTOVOLTAIC SPECIALISTS CONFERENCE (PVSC), 2019, : 1525 - 1528
  • [24] The effect of moisture on the degradation mechanism of multi-crystalline silicon photovoltaic module
    Kim, T. H.
    Park, N. C.
    Kim, D. H.
    MICROELECTRONICS RELIABILITY, 2013, 53 (9-11) : 1823 - 1827
  • [25] Performance Degradation of Crystalline Silicon Solar Module in Various Ultraviolet Radiation Area
    Wang, He
    Wang, Ao
    Yang, Hong
    Zhang, Junjun
    Huang, Jingsheng
    2016 IEEE 43RD PHOTOVOLTAIC SPECIALISTS CONFERENCE (PVSC), 2016, : 1757 - 1760
  • [26] The mechanism of anti-potential induced degradation for crystalline silicon photovoltaic module
    Lianyungang Shenzhou New Energy Co., Ltd., Lianyungang
    222100, China
    不详
    200235, China
    Taiyangneng Xuebao, 11 (2698-2702):
  • [27] PV module degradation analysis and impact on settings of overcurrent protection devices
    Dhoke, Amit
    Sharma, Rahul
    Saha, Tapan Kumar
    SOLAR ENERGY, 2018, 160 : 360 - 367
  • [28] Evaluation of PV Module Field Performance
    Wohlgemuth, John
    Silverman, Timothy
    Miller, David C.
    McNutt, Peter
    Kempe, Michael
    Deceglie, Michael
    2015 IEEE 42ND PHOTOVOLTAIC SPECIALIST CONFERENCE (PVSC), 2015,
  • [29] Modified STC Correction Procedure for Assessing PV Module Degradation in Field Surveys
    Singh, Hemant K.
    Dubey, R.
    Zachariah, S.
    Narasimhan, K. L.
    Arora, B. M.
    Kottantharayil, A.
    Vasi, J.
    2017 IEEE 44TH PHOTOVOLTAIC SPECIALIST CONFERENCE (PVSC), 2017, : 1995 - 1999
  • [30] Visual and Electrical Degradation of 22 Years Field Age Monocrystalline Silicon PV Module in Composite Climate of India
    Rajput, Pramod
    Tiwari, G. N.
    Bora, Birinchi
    Sastry, O. S.
    2015 IEEE 42ND PHOTOVOLTAIC SPECIALIST CONFERENCE (PVSC), 2015,
12345